Water-based anti-static bonding agent for shoes and preparation method thereof

A water-based, anti-static technology, applied in the field of rubber processing, can solve the problems of low production environment safety, harm to human health, flammability of rubber slurry, etc., and achieve the effects of good adhesion performance, low cost and high safety.

Active Publication Date: 2013-08-28
JIHUA 3537 SHOE MAKING
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of adhesive is toxic and can endanger human health, and at the same time, due to the flammability of rubber pulp, the safety of the production environment is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based anti-static bonding agent for shoes and preparation method thereof
  • Water-based anti-static bonding agent for shoes and preparation method thereof
  • Water-based anti-static bonding agent for shoes and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1 of the present invention: water-based antistatic adhesive for shoes, including 50kg natural latex, 1kg ball-milled water-based vulcanization system, 0.5kg ammonia water, 0.5kg flat plus O, 0.3kg antistatic agent SN and 0.05kg carboxymethyl Base cellulose sodium and 1kg soft water; every 1kg ball milled water-based vulcanization system consists of 0.05kg sulfur, 0.03kg accelerator M, 0.04kg accelerator TMTD, 0.07kg nano-zinc oxide, 0.05kg anti-aging agent KY-405L, 0.05kg hydrogen Potassium oxide, 0.02kg diffusing agent NNO (powder), 0.02kg casein anhydride (powder) and 0.67kg soft water; the ammonia water used is industrial ammonia water, and the mass percentage of ammonia is 27%.

[0027] The preparation method of water-based antistatic adhesive for shoes, each component is taken according to the above weight, the preparation method is as follows:

[0028] Step A, preparation of sodium carboxymethyl cellulose water-swellable body: sodium carboxymethyl cellu...

Embodiment 2

[0033] Embodiment 2 of the present invention: Water-based antistatic adhesive for shoes, including 45kg natural latex, 1.2kg ball-milled water-based vulcanization system, 0.4kg ammonia water, 0.6kg flat plus O, 0.25kg antistatic agent SN and 0.06kg carboxylate Sodium methylcellulose and 0.8kg soft water; every 1kg ball milled water-based vulcanization system consists of 0.05kg sulfur, 0.03kg accelerator M, 0.04kg accelerator TMTD, 0.07kg nano zinc oxide, 0.05kg anti-aging agent KY-405L, 0.05 kg potassium hydroxide, 0.02kg diffusing agent NNO (powder), 0.02kg casein anhydride (powder) and 0.67kg soft water; the ammonia water used is industrial ammonia water, and the mass percentage of ammonia is 27%.

[0034] The preparation method is the same as in Example 1.

Embodiment 3

[0035] Embodiment 3 of the present invention: Water-based antistatic adhesive for shoes, including 55kg natural latex, 0.8kg ball-milled water-based vulcanization system, 0.6kg ammonia water, 0.4kg flat plus O, 0.35kg antistatic agent SN and 0.04kg carboxylate Sodium methylcellulose and 1.2kg soft water; every 1kg ball milled water-based vulcanization system consists of 0.05kg sulfur, 0.03kg accelerator M, 0.04kg accelerator TMTD, 0.07kg nano zinc oxide, 0.05kg anti-aging agent KY-405L, 0.05 kg potassium hydroxide, 0.02kg diffusing agent NNO (powder), 0.02kg casein anhydride (powder) and 0.67kg soft water; the ammonia water used is industrial ammonia water, and the mass percentage of ammonia is 27%.

[0036] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a water-based anti-static bonding agent for shoes and a preparation method thereof. The water-based anti-static bonding agent for shoes comprises the following components in parts by weight: 45-55 parts of natural emulsion, 0.8-1.2 parts of grinding water-based vulcanization system, 0.4-0.6 part of ammonia water, 0.4-0.6 part of peregal O, 0.25-0.35 part of antistatic agent, 0.04-0.06 part of sodium carboxymethylcellulose and 0.8-1.2 parts of soft water. Research is carried out on the formula and the preparation method of the water-based anti-static bonding agent for shoes, a safe and environment-friendly anti-static bonding agent with good bonding performance is obtained, raw materials are available, cost is low, safety is high, and the preparation technology is simple, so that the water-based anti-static bonding agent is applicable to industrial production; and the preparation method is simple and practicable, cost is low, and the water-based anti-static bonding agent for shoes has a good using effect.

Description

technical field [0001] The invention relates to the field of rubber processing, in particular to a water-based antistatic adhesive for shoes and a preparation method thereof. Background technique [0002] In the manufacturing process of rubber shoes, the adhesives that need to be used are usually solvent-based adhesives. The conventionally used shoe adhesives include natural rubber compound rubber glue made of toluene, benzene or gasoline and esters as solvents. . Such adhesives are toxic and can endanger human health, and at the same time, due to the flammability of the rubber pulp, the production environment has a low degree of safety. With the development of the shoemaking industry, non-toxic, safe and environmentally friendly antistatic adhesives with simple manufacturing methods have become a new inevitable demand. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a water-based antistatic adhesive for shoes ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J107/02C09J11/04C09J11/06C09J11/08
Inventor 晋齐怀彭德彪陈松雄王春桥石银平安廷飞
Owner JIHUA 3537 SHOE MAKING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products