PTC (Positive Temperature Coefficient) thermistor base material and preparation method thereof
A thermistor and base material technology, applied in the direction of resistors with positive temperature coefficients, etc., can solve the problems of wide resistance distribution at room temperature, low PTC strength, and low stability, and achieve stable PTC characteristics, increased service life, and high Effect of PTC stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment Construction
[0009] A PTC thermistor substrate, made of the following raw materials in parts by weight (kg): polyvinylidene fluoride 50, linear low-density polyethylene 30, carbon black 25, aluminum powder 24, aluminum nitride 16, medical stone powder 20. Aluminum hydroxide powder 16. Magnesium oxide 6. meerschaum 14 , Crosslinker TAC 5, Crosslinker TAIC 2, N-2-(aminoethyl)-3-aminopropyltrimethoxysilane 5, isooctyltin dimethyl dimercaptoacetate 3, epoxidized triglyceride 8-.
[0010] The preparation method of the PTC thermistor base material comprises the following steps: adding aluminum hydroxide powder to water and stirring to form a suspension, then adding aluminum powder and medical stone powder, dispersing at high speed for 10-20 minutes, and heating to 80- 95℃, plus Cross-linking agent TAC, N-2-(Aminoethyl)-3-Aminopropyltrimethoxysilane, after stirring evenly, then add magnesium oxide powder, grind for 2-3 hours, to the slurry, spray dry to obtain powder; linear low density Mix...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap