Highly adhesion-resistant aqueous woodenware paint and preparation method thereof

A technology of water-based wood lacquer and anti-blocking aid, applied in the field of wood lacquer, can solve the problems of water-based wood lacquer stagnation, poor sealing and anti-blocking properties, etc. Effect

Active Publication Date: 2013-09-25
SKSHU PAINT
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, water-based wood coatings are gradually replacing solvent-based coatings as protective coatings for wood products due to their low VOC content. Because water is used as a solvent and easy to use; it has been used more and more in the DIY wood coatings market and industrial wood coatings market. However, its poor sealing and anti-blocking properties have always been the development of sluggish water-based wood lacquers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Highly adhesion-resistant aqueous woodenware paint and preparation method thereof
  • Highly adhesion-resistant aqueous woodenware paint and preparation method thereof
  • Highly adhesion-resistant aqueous woodenware paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A high anti-blocking water-based wood paint, comprising the following components by weight:

[0019]

Embodiment 2

[0021] A high anti-blocking water-based wood paint, comprising the following components by weight:

[0022]

[0023]

Embodiment 3

[0025] A high anti-blocking water-based wood paint, comprising the following components by weight:

[0026]

[0027] Best practice:

[0028] A high anti-blocking water-based wood paint, comprising the following components by weight:

[0029]

[0030]

[0031] The preparation method of the above-mentioned high anti-blocking water-based wood paint: put the water-based pure acrylic resin into the dispersion tank, according to the above-mentioned parts by weight, under the state of 1200r / min rotating speed, add the water-based multifunctional auxiliary agent, defoamer, film-forming aid , antifreeze, anti-corrosion and fungicide, anti-adhesion additive, leveling agent, thickener and water are slowly added into the dispersion tank while stirring, and fully stirred for 30 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
minimum film forming temperatureaaaaaaaaaa
minimum film forming temperatureaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of woodenware paints, and especially relates to a highly adhesion-resistant aqueous woodenware paint and a preparation method thereof. The highly adhesion-resistant aqueous woodenware paint comprises, by weight, 70-80 parts of an aqueous pure acrylic resin, 0.05-0.30 parts of an aqueous multifunctional assistant, 0.05-0.30 parts of an antifoaming agent, 4-7 parts of a film forming assistant, 0.5-1.5 parts of an antifreeze agent, 0.05-0.20 parts of an anticorrosive bactericide, 0.1-1.5 parts of an adhesion resistant assistant, 0.2-1.0 part of a leveling agent, 0.5-1.7 parts of a thickening agent and 6.5-24.5 parts of water. The highly adhesion-resistant aqueous woodenware paint has a good adhesion resistance, can effectively protect a base material from destroying, has a super strong adhesion with the surface of the base material, can resist superposed 1kg adhesion at 60-80DEG C for 48h in a sealed manner, and has a wide market prospect.

Description

technical field [0001] The invention relates to the technical field of wood lacquer, in particular to a high anti-blocking water-based wood varnish and a preparation method thereof. Background technique [0002] At present, water-based wood coatings are gradually replacing solvent-based coatings as protective coatings for wood products due to their low VOC content. Because water is used as a solvent and easy to use; it has been used more and more in the DIY wood coatings market and industrial wood coatings market. However, its poor sealing and anti-blocking properties have always been the development of sluggish water-based wood lacquers. Contents of the invention [0003] The object of the present invention is to provide a kind of high anti-adhesion water-based wood varnish with good sealing anti-adhesion and dry heat resistance and a preparation method thereof. [0004] The present invention is achieved in that a kind of high anti-blocking water-based wood paint is char...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D125/14C09D7/12
Inventor 洪杰何玲玲林伟陈瑞金
Owner SKSHU PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com