Method for preparing silver micro-powder for electronic paste of pressure sensitive element
A technology for electronic paste and pressure sensitive components, which is applied in the field of preparing silver micropowder for electronic paste of pressure sensitive components, which can solve the problems of low specific surface area, high bulk density of silver micropowder, unsuitability for electronic paste of pressure sensitive components, etc. , to achieve the effect of high surface activity and concentrated particle size distribution
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0017] Example 1: (1) Liquid preparation: Put solid silver nitrate crystals in the reactor and add sufficient water to stir to form a uniform aqueous solution. The mass ratio of silver nitrate solid crystals to water is 1:10, and the temperature is maintained at 35°C. , PH value is 4, make A solution; put the soda ash solid powder in the batching kettle and add enough water to stir to form a uniform aqueous solution. The quality of the soda ash solid powder is 50% of the quality of the silver nitrate solid crystal. The mass ratio of water is 1:6, the temperature is maintained at 40℃, the PH value is 12, and the solution B is prepared; gelatin is used as a surface coating agent and sufficient alcohol is added to stir to dissolve evenly. The amount of gelatin is the quality of silver nitrate solid crystals Make up 0.5% of silver nitrate and make solution C; make up an aqueous solution containing 37% of ascorbic acid and keep it at room temperature. The amount of ascorbic acid is 4...
Example Embodiment
[0021] Example 2: (1) Liquid preparation: Put solid silver nitrate crystals in the reactor and add enough water to stir to form a uniform aqueous solution. The mass ratio of silver nitrate solid crystals to water is 1:10, and the temperature is maintained at 45°C. , PH value is 5, make A solution; put the soda ash solid powder in the batching kettle and add enough water to stir to form a uniform aqueous solution. The quality of the soda ash solid powder is 50% of the quality of the silver nitrate solid crystal. The mass ratio of water is 1:6, the temperature is maintained at 50℃, the PH value is 13, and the solution B is prepared; gelatin is used as a surface coating agent and sufficient alcohol is added to stir to dissolve evenly. The amount of gelatin is the quality of silver nitrate solid crystals Make up 0.5% of silver nitrate and make solution C; make up an aqueous solution containing 37% of ascorbic acid and keep it at room temperature. The amount of ascorbic acid is 40% o...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap