A kind of brick and its manufacturing method

A technology of hollow bricks and waste slag powder, which is applied in the field of manufacturing, can solve problems such as waste of resources, and achieve the effect of overcoming waste of resources

Active Publication Date: 2016-08-17
王春鸣
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The brick provided by the present invention uses the waste slag powder formed after burning the woody slag produced in the fiberboard production process as one of the components together with cement and water to form a component of the brick, and then realizes the effect of reusing the waste slag powder. It overcomes the defect of waste of resources caused by direct discarding of waste residue powder in related technologies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of brick and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] An embodiment of the present invention provides a brick, whose raw material components include 7.5-8.0 parts of waste slag powder, 1.6-1.8 parts of cement and 0.4-0.5 parts of water in parts by weight.

[0014] The brick provided by the invention uses the waste slag powder formed after burning the woody slag produced in the fiberboard production process as one of the components to form brick components together with cement and water, and then realizes the effect of reusing the waste slag powder The invention overcomes the defect of waste of resources caused by direct discarding of waste slag powder in the related art.

[0015] Preferably, in this embodiment, in parts by weight, the raw material components include 7.7-7.9 parts of waste residue powder, 1.6-1.7 parts of cement and 0.45-0.5 parts of water. The bricks made according to the above-mentioned preferred ratio have a dense surface and are not easy to be damaged.

[0016] In addition, in order to mix the waste sl...

Embodiment 2

[0020] In this embodiment, the manufacturing method of the brick provided in the first embodiment specifically includes the following steps:

[0021] Step 101: Stir and mix waste residue powder and cement in predetermined parts by weight to obtain a mixture;

[0022] In step 101, specifically, in order to ensure the compressive strength of the bricks produced, it is necessary to mix the waste slag powder and cement as much as possible. Therefore, in this embodiment, preferably, the stirring and mixing time is 10-20 minutes.

[0023] Step 102: Adding predetermined weight parts of water into the mixture, stirring evenly to obtain a slurry.

[0024] Specifically, step 102 can be implemented according to the following method: the mixture is added to the blender, and then water of a predetermined weight part is added to the mixture, and the slurry is obtained after being uniformly stirred by the blender; the blender can mix well Material and mixing to obtain a slurry.

[0025] S...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of manufacturing industry and specifically relates to a brick and a manufacturing method thereof. The brick comprises the material components in parts by weight: 7.5-8.0 parts of waste residue powder, 1.6-1.8 parts of cement and 0.4-0.5 part of water. The manufacturing method of the brick comprises the following steps of stirring and mixing the waste residue powder and the cement with the set weight parts to obtain mixed materials; adding the water with the set weight parts into the mixed materials, and uniformly stirring to obtain slurry; and forming the slurry to form the brick. According to the brick and the manufacturing method thereof, effect of reutilizing the waste residue powder is realized, and the defect that resources are wasted as the waste residue powder in correlative techniques is directly wasted is overcome.

Description

technical field [0001] The invention relates to the field of manufacturing, in particular to a brick and a manufacturing method thereof. Background technique [0002] During the production and processing of fiberboard, a large amount of waste wood slag will be produced. At present, most of these wood residues will be burned as fuel, and a large amount of waste residue powder will be formed after combustion. [0003] However, in the related art, most of the waste residue powder produced after burning the wood residue is not reused but directly discarded, thus causing a waste of resources. Contents of the invention [0004] The object of the present invention is to provide a brick and its manufacturing method to solve the above problems. [0005] In an embodiment of the present invention, a brick is provided. According to parts by weight, its raw material components include: 7.5-8.0 parts of waste residue powder, 1.6-1.8 parts of cement and 0.4-0.5 parts of water. [0006...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B18/06
CPCY02W30/91
Inventor 王春鸣
Owner 王春鸣
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com