A kind of puncture-resistant vacuum insulation panel and preparation method thereof

A vacuum insulation panel and puncture-resistant technology, which is applied to heat exchange equipment, mechanical equipment, and pipelines through heat insulation protection, and can solve problems such as the rate of defective products that are easy to leak, and are not resistant to punctures.

Active Publication Date: 2017-01-25
铁科创恒新材料科技有限公司 +2
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It mainly solves the problem that the existing VIP board is not resistant to puncture and easy to leak air during actual transportation and use, resulting in a high defective rate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of puncture-resistant vacuum insulation panel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1: Prefabricate the core material 1 of the vacuum insulation panel first, and the core material is glass fiber, fumed silica, chemically deposited nano-silica, open-cell polyurethane foam or open-cell phenolic foam. Then put the prepared vacuum insulation board core material into the vacuum packaging bag 2 after drying. membrane. Next, the core material is heat-sealed in a vacuum packaging bag 2 at a vacuum degree of less than 100 Pa, preferably at a vacuum degree of less than 0.2 Pa. Then fold the excess edge of the vacuum packaging bag according to the shape of the core material, and use rubber-type pressure-sensitive adhesive, polyurethane adhesive, polyacrylate adhesive, hot-melt adhesive or epoxy resin glue to fold the excess edge of the vacuum packaging bag Adhesive fixation. Mix 100 parts of polyether or polyester polyol, 10 parts of pentane, 3 parts of hard foam silicone oil, 1 part of triethylenediamine, and 1 part of dibutyltin dilaurate; then add...

Embodiment 2

[0027] Embodiment 2: Prefabricate the core material 1 of the vacuum insulation panel first, and the core material is glass fiber, fumed silica, chemically deposited nano-silica, open-cell polyurethane foam or open-cell phenolic foam. Then put the prepared vacuum insulation board core material into the vacuum packaging bag 2 after drying. membrane. Next, the core material is heat-sealed in a vacuum packaging bag 2 at a vacuum degree of less than 100 Pa, preferably at a vacuum degree of less than 0.2 Pa. Then fold the excess edge of the vacuum packaging bag according to the shape of the core material, and use rubber-type pressure-sensitive adhesive, polyurethane adhesive, polyacrylate adhesive, hot-melt adhesive or epoxy resin glue to fold the excess edge of the vacuum packaging bag Adhesive fixation. Mix 100 parts of polyether or polyester polyol, 30 parts of chlorofluoroalkane, 0.1 part of hard foam silicone oil, and 0.1 part of dibutyltin dilaurate; then add 150 parts of po...

Embodiment 3

[0028] Embodiment 3: Prefabricate the core material 1 of the vacuum insulation panel first, and the core material is glass fiber, fumed silica, chemically deposited nano-silica, open-cell polyurethane foam or open-cell phenolic foam. Then put the prepared vacuum insulation board core material into the vacuum packaging bag 2 after drying. membrane. Next, the core material is heat-sealed in a vacuum packaging bag 2 at a vacuum degree of less than 100 Pa, preferably at a vacuum degree of less than 0.2 Pa. Then fold the excess edge of the vacuum packaging bag according to the shape of the core material, and use rubber-type pressure-sensitive adhesive, polyurethane adhesive, polyacrylate adhesive, hot-melt adhesive or epoxy resin glue to fold the excess edge of the vacuum packaging bag Adhesive fixation. Mix 100 parts of polyether or polyester polyol, 20 parts of chlorofluoroalkane, 2 parts of hard foam silicone oil, and 1 part of triethylenediamine; After the material is fully ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a puncture-resistant vacuum insulation board. The puncture-resistant vacuum insulation board comprises a puncture-resistant layer, a vacuum encapsulation layer and a core material inside the vacuum encapsulation layer. The puncture-resistant layer is made of polyurethane foam materials, bonds to the surface of the vacuum encapsulation layer, and is obtained through a foaming reaction of polyether polyol or polyester polyol and polyisocyanates. Meanwhile, the invention further discloses a manufacturing method of the vacuum insulation board. The obtained vacuum insulation board has good puncture resistance, largely reduces the high defective rate caused by puncture, scrapping and rubbing when the vacuum insulation board is conveyed and used, lowers the construction difficulty, has excellent insulation property, and is suitable for being applied to and popularized in various heat-preservation places.

Description

technical field [0001] The invention relates to a vacuum insulation panel (VIP panel) insulation material, in particular to a puncture-resistant vacuum insulation panel and a preparation method thereof. Background technique [0002] Vacuum insulation panel (VIP panel) is a high-efficiency and energy-saving high-tech vacuum insulation material obtained by packaging the insulation core material in a vacuum packaging bag. Since the heat transfer caused by air convection is effectively avoided, the thermal conductivity is greatly reduced compared with traditional thermal insulation materials (vitrified beads, polystyrene board, polyurethane foam, etc.), generally at 0.008 W / (m K ) below, has very excellent thermal insulation performance. Compared with other insulation materials, vacuum insulation panels have the advantages of small size, thin thickness, light weight and low thermal conductivity, so they have attracted extensive attention in the fields of building exterior wall ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F16L59/065
CPCF16L59/065
Inventor 孙俊陈林王化田兴友王建张强李治俊吕万青
Owner 铁科创恒新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com