Water-soluble metal short-term antirust liquid and preparation method thereof

A kind of anti-rust liquid and water-soluble technology, which is applied in the field of water-soluble metal short-term anti-rust liquid and its preparation, which can solve the problems of easy oxidation and discoloration, inability to prevent long-term rust, refractory degradation, etc., and achieve good corrosion inhibition effect and anti-rust effect Long-lasting, easy-to-remove effect

Active Publication Date: 2014-04-02
MINGGUANG CITY LIUXIANG PUMP IND
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary anti-rust water contains a large amount of sodium nitrite, which is carcinogenic and is not conducive to environmental protection and human health. However, the use of humectants to prolong the life of anti-rust water brings the disadvantages of sticking hands and dust, and cannot prevent rust for a long time; Although the general dura-film anti-rust oil is suitable for long-term anti-rust, and the film is transparent and beautiful, there are few types of colorless and transparent resins, which are unstable and easy to oxidize and change color. They also need organic solvents to dissolve, which brings the danger of flammability and explosion. It is not conducive to environmental protection and health; the general anti-rust oil uses mineral oil, which is difficult to degrade, and it will also cause the problem of difficult degreasing when used for short-term anti-rust

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] A water-soluble metal short-term anti-rust solution, made of the following raw materials in parts by weight (kg): alkyl polyglycoside 2.5, emulsifier OP-10 1.5, sodium metaborate 2.5, ascorbic acid 1.5, butyl hydroxyanisole 2.5, Hexatropine 1, tallow diamine trioleate 1.2, silicon nitride 0.8, acrylonitrile 11, water glass 6, disodium EDTA 1.5, additive 4.5, water 300. The auxiliary agent is made of the following raw materials in parts by weight (kg): polyoxyethylene sorbitan monooleate 2, nano-titanium dioxide 0.1, sodium bicarbonate 2, diethanolamine 2, carboxymethyl cellulose 3, Polyvinyl alcohol 2, peach gum 1, sodium silicate 2, urea 3, ammonium persulfate 1, water 20; the preparation method is to dissolve ammonium persulfate in water, then add other remaining materials, stir for 10-15 minutes, heat To 70-80 ℃, stirring reaction for 1-2 hours, that is.

[0010] The preparation method of the water-soluble metal short-term anti-rust liquid comprises the following st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-soluble metal short-term antirust liquid which is prepared from the following raw materials in parts by weight: 2-3 parts of alkyl polyglucoside, 1-2 parts of an emulsifier OP-10, 2-3 parts of sodium metaborate, 1-2 parts of ascorbic acid, 2-3 parts of butyl hydroxyanisole, 0.5-1.5 parts of urotropine, 1.1-1.7 parts of trioleic acid tallow diamine, 0.5-1 part of silicon nitride, 10-12 parts of acrylonitrile, 5-7 parts of water glass, 1-2 parts of EDTA disodium, 4-5 parts of an auxiliary agent, and 300 parts of water. The antirust liquid can form a thin film on a metal surface, so as to isolate air and prevent oxidation; the thin film is easy to clean up, and can be immediately removed by water washing; the antirust liquid has good oxidation resistance and corrosion inhibition effects, can form the oxidation protective film on the metal surface, and has lasting antirust effect; and the antirust liquid is suitable for short-term rust prevention of hardware, automobile parts and other metal products, and does not affect welding and other performance.

Description

technical field [0001] The invention relates to the technical field of antirust, in particular to a water-soluble metal short-term antirust liquid and a preparation method thereof. Background technique [0002] Rust prevention on metal surfaces is an important subject in industrial production. Traditional antirust liquids and antirust oils have both advantages and disadvantages. Ordinary anti-rust water contains a large amount of sodium nitrite, which is carcinogenic and is not conducive to environmental protection and human health. However, the use of humectants to prolong the life of anti-rust water brings the disadvantages of sticking hands and dust, and cannot prevent rust for a long time; Although the general dura-film anti-rust oil is suitable for long-term anti-rust, and the film is transparent and beautiful, there are few types of colorless and transparent resins, which are unstable and easy to oxidize and change color. They also need organic solvents to dissolve, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23F11/173
Inventor 刘和明刘和兵陈乡
Owner MINGGUANG CITY LIUXIANG PUMP IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products