Polypropylene film and application thereof

A polypropylene film, polypropylene technology, applied in the field of polypropylene film, can solve the problems of small high elastic state range, limited use range of polypropylene, unevenness, etc., and achieve the effect of meeting the requirements

Active Publication Date: 2014-04-16
GUANGDONG TIANAN NEW MATERIAL
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the secondary thermal processing that is common in the decoration industry limits the scope of use of polypropylene.
Due to its crystallinity, polypropylene has a rapid transition from glass state to molten state, narrow melting range, small high elastic state range, and low melt strength. During secondary processing, it is prone to tensile fracture and uneven stretching. Case

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene film and application thereof
  • Polypropylene film and application thereof
  • Polypropylene film and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] The preparation method of the polypropylene film of Examples 1-5 is as follows: add random copolymer polypropylene and TPO materials into a high-speed mixer and stir, then put in antioxidants and fillers, and after stirring, the materials enter the internal mixer , The material is initially melted in the internal mixer and then enters the double-roll mill for refining, filtered and then enters the calendering roller, calendering and forming a film of the required size. The processing temperature of the main calender is selected at 170~200℃.

[0035] Table 1

[0036]

[0037] The polypropylene films obtained in Examples 1 to 5 and Comparative Example 1 were tested for performance, and the experimental results are shown in Table 2.

[0038] Table 2

[0039]

Embodiment 6～11

[0041] The compositions of Examples 6 to 11 are shown in Table 3, and the preparation methods thereof are as shown in Examples 1 to 5. The polypropylene films obtained in Examples 6-11 were tested for performance, and the experimental results are shown in Table 4.

[0042] table 3

[0043]

[0044]

[0045] Table 4

[0046]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polypropylene film which is mainly prepared from the following raw materials in parts by weight: 100 parts of polypropylene random copolymer, 10-40 parts of TPO, 0.2-3 parts of an antioxidant and 0.5-40 parts of filler, wherein the melt flow rate of the polypropylene random copolymer is 1-15g / 10min. According to the polypropylene film, the melting range is widened, secondary processing can be performed, and the conditions of tensile break and tensile non-uniformity are avoided. Moreover, the requirements of double-vacuum plastic molding can be met, and the polypropylene film can be used for secondary processing and molding for preparing decorative materials.

Description

Technical field [0001] The invention relates to a polypropylene film and its use, which can be used for secondary vacuum suction molding to prepare decorative materials. Background technique [0002] Among the five general engineering plastics, polypropylene has a short development history, but it is the one with the fastest development speed, the largest output, the most brands, and the most versatile. Because polypropylene is not only low in price, excellent in performance, but also an environmentally friendly material, polypropylene has become one of the fastest growing polymers at present. [0003] In today's society, the scope of decoration materials is becoming wider and wider, and the demand is also increasing. Polypropylene is gradually entering the sight of the decoration industry. Among them, the secondary thermal processing that is common in the decoration industry limits the use of polypropylene. Because of its crystallinity, polypropylene has a rapid transition from ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/14C08L23/06C08L23/12C08L23/16C08L9/02C08L23/22
CPCC08J5/18C08J2323/14C08J2423/12C08J2423/16C08L23/14C08L2203/16C08L2205/03C08L2207/14C08L23/12C08L23/16
Inventor 吴启超丰俊湘林梅绪陈慧雪黎华强王东勇宋岱瀛
Owner GUANGDONG TIANAN NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com