Preparation method for finishing agent of thermal-storage fabric
A fabric finishing agent, heat storage technology, applied in fiber processing, textiles and papermaking, etc., can solve the problems of bloated, not easy to wash, not durable, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0011] A preparation method of heat storage and warming fabric finishing agent, comprising the steps of:
[0012] 70 parts by mass of molybdenum oxide and medical stone mixed nanopowder, 30 parts by mass of water-based acrylic resin, 60 parts by mass of water, 3 parts by mass of sodium polyacrylate, 9 Parts by mass of hydroxypropyl methylcellulose was dispersed for 8 hours at a speed of 15,000 rpm to obtain a heat-storing and warming fabric finishing agent;
[0013] In the molybdenum oxide and medical stone mixed nano-powder, the mass percentages of the molybdenum oxide nano-powder and the medical stone nano-powder are 80% and 20% respectively, and the molybdenum oxide and medical stone mixed nano-powder The average particle size of ≤ 10nm.
Embodiment 2
[0015] A preparation method of heat storage and warming fabric finishing agent, comprising the steps of:
[0016] 65 parts by mass of molybdenum oxide and medical stone mixed nano-powder, 25 parts by mass of water-based acrylic resin, 55 parts by mass of water, 2 parts by mass of sodium polyacrylate, 7 mass parts 1 part of hydroxypropyl methylcellulose was dispersed for 6 hours at a rotating speed of 14500 rev / min to obtain a heat-storing and warming fabric finishing agent;
[0017] In the molybdenum oxide and medical stone mixed nano-powder, the mass percentages of molybdenum oxide nano-powder and medical stone nano-powder are respectively 75% and 25%, and the molybdenum oxide and medical stone mixed nano-powder The average particle size of ≤ 10nm.
Embodiment 3
[0019] A preparation method of heat storage and warming fabric finishing agent, comprising the steps of:
[0020] 66 parts by mass of molybdenum oxide and medical stone mixed nano-powder, 28 parts by mass of water-based acrylic resin, 57 parts by mass of water, 2.3 parts by mass of sodium polyacrylate, 7.9 Parts by mass of hydroxypropyl methylcellulose was dispersed for 7 hours at a speed of 14,800 rpm to obtain a heat-storing and warming fabric finishing agent;
[0021] In the molybdenum oxide and medical stone mixed nano-powder, the mass percentages of molybdenum oxide nano-powder and medical stone nano-powder are 78% and 22% respectively, and the molybdenum oxide and medical stone mixed nano-powder The average particle size is ≤10nm.
PUM
Property | Measurement | Unit |
---|---|---|
The average particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com