A method for continuous production of high-clean silicon dioxide

A silica and cleaning technology, which is applied in the direction of silica, pharmaceutical formulations, cosmetic preparations, etc., can solve the problems of toothpaste agglomeration, poor stability, uniformity, and inability to effectively clean the tooth surface, achieving easy separation and stable performance Consistent, low wear value results

Active Publication Date: 2015-08-12
ZHAOQING SANJIANG SILICON MATERIALS CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the silica produced by this method has poor stability and uniformity, and it is easy to make the toothpaste agglomerate and cannot effectively clean the deposits on the tooth surface.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for continuous production of high-clean silicon dioxide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 1) In a 30m 3 Add the sodium sulfate solution whose concentration n0 is 0.5mol / L in the continuous reactor, and the volume of the added sodium sulfate solution is 10m 3 ;

[0026] 2) Adding a sodium silicate solution whose concentration n1 is 1mol / L in the continuous reactor, and adjusting the pH value of the reaction solution to 8;

[0027] 3) keep reaction temperature at 60 ℃, add the sodium silicate solution that the amount concentration n1 of substance is 1mol / L and the sulfuric acid solution that the amount concentration n2 of substance is 1mol / L simultaneously, the volume of the sodium silicate solution that adds is 8000L, The volume of the added sulfuric acid solution is 8000L;

[0028] The sodium silicate solution was added at a rate of 3m 3 / h, the adding speed of sulfuric acid solution is 3m 3 / h;

[0029] 4) A precipitate and solution with a volume of 16000L is discharged from the outlet below the continuous reactor, and the obtained precipitate is filte...

Embodiment 2

[0032] 1) In a 30m 3 The amount of substance added in the continuous reactor is a sodium sulfate solution whose concentration n0 is 1mol / L, and the volume of the added sodium sulfate solution is 10m 3 ;

[0033] 2) Adding a sodium silicate solution with a substance concentration n1 of 1.5 mol / L in the continuous reactor, and adjusting the pH value of the reaction solution to 8;

[0034] 3) Keeping the reaction temperature at 60°C, add a sodium silicate solution with a substance concentration n1 of 1.5mol / L and a sulfuric acid solution with a substance concentration n2 of 3mol / L at the same time, and the volume of the added sodium silicate solution is 8000L , the volume of the added sulfuric acid solution is 4000L;

[0035] The sodium silicate solution was added at a rate of 3m 3 / h, the adding speed of sulfuric acid solution is 1.5m 3 / h;

[0036] 4) While step 3) was carried out, precipitation was generated in the reactor, and the outlet below the continuous reactor rele...

Embodiment 3

[0039] 1) In a 30m 3 Add the sodium sulfate solution whose concentration n0 is 0.8mol / L in the continuous reactor, and the volume of the added sodium sulfate solution is 10m 3 ;

[0040] 2) Adding a sodium silicate solution with a substance concentration n1 of 1.2 mol / L in the continuous reactor, and adjusting the pH value of the reaction solution to 8;

[0041] 3) keep the reaction temperature at 60°C, add the sodium silicate solution of 1.2mol / L and the sulfuric acid solution of 2.4mol / L with the concentration n1 of the substance added simultaneously, and the volume of the sodium silicate solution added is 8000L, the volume of sulfuric acid solution added is 4000L;

[0042] The sodium silicate solution was added at a rate of 6 m 3 / h, the adding speed of sulfuric acid solution is 3m 3 / h;

[0043] 4) While step 3) was carried out, precipitation was generated in the reactor, and the outlet below the continuous reactor released the mixture of precipitation and reaction so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for continuously producing high-cleanness silicon dioxide. The method comprises the following steps: (1) a sodium sulfate solution V0 of which the amount-of-substance concentration n0 is 0.5 to 1 mol / L is added into a continuous reactor; (2) a sodium silicate solution of which the amount-of-substance concentration n1 is 1 to 1.5 mol / L is added into the continuous reactor, and the pH value of a reaction liquid is regulated to 8 to 10; (3) a reaction system is kept at 59 to 61 DEG C, at the same time, the sodium silicate solution of which the amount-of-substance concentration n1 is 1 to 1.5 mol / L and the sulfuric acid solution with the amount-of-substance concentration n2 are added, the volume of the added sodium silicate solution is V1, the volume of the added sulfuric acid solution is V2, the V1, V2, n1, n2 and V0 satisfy the following three relational expressions: V1*n1=V2*n2; (V1*n1) / (V1+V2)=no; n0<n1; (4) precipitation and solutions of which the volume is V1+V2 are discharged from an outlet below the continuous reactor, and the obtained precipitation is filtered, washed and dried to obtain silicon dioxide. By using the method, the silicon dioxide with stable properties can be produced continuously, the obtained silicon dioxide can be used in toothpastes, and teeth can be effectively cleaned.

Description

technical field [0001] The invention relates to the field of silicon dioxide, in particular to a method for continuously producing high-clean silicon dioxide. Background technique [0002] When people eat, various deposits, including bacterial film, are easily produced on the tooth surface. Bacteria often contain brown or yellow pigments, which not only make the teeth unsightly, but may also cause some oral diseases. Therefore, it is of great practical significance to remove deposits on the tooth surface. In order to effectively clean the deposits on the tooth surface, abrasives are added to the toothpaste, and silicon dioxide is one of the abrasives. [0003] In the prior art, by adding a certain proportion of sodium silicate and concentrated sulfuric acid into the reactor for direct reaction, the reacted material is cooled and pumped into a filter press for filtration, washing and drying. Make the solid-liquid two-phase reach a certain ratio, and the filter cake is subj...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B33/113A61K8/25A61Q11/00
Inventor 王宪伟庹文喜崔昀
Owner ZHAOQING SANJIANG SILICON MATERIALS CO LTD