A technology of blended fabrics and fabrics, applied in textiles and papermaking, fiber type, fiber treatment, etc., can solve the problems of poor antibacterial performance and low wear resistance, and achieve the effect of high wear resistance and antibacterial performance.

Active Publication Date: 2014-04-30
吴江市先锋针织有限公司
View PDF4 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Technical problem to be solved: conventional cotton and polyvinyl chloride blended fabrics usually have low abrasion resistance and poor antibacterial properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] (1) To prepare fabric coating liquid, take 5kg of polyvinyl alcohol tert-butyraldehyde, 5kg of dibutyl sebacate, 10kg of dammar resin, 6kg of ethyl acetate, 5kg of magnesium oxide, 4kg of zinc oxide, Ethanol is 15kg; (2) Heat the ingredients in step (1) to dissolve, stir evenly after dissolving, seal and keep warm at 80°C after stirring; (3) Take the blended fabric of cotton and polyvinyl chloride, the cotton content is the total weight 75wt% of the total weight, and the content of polyvinyl chloride is 25wt% of the total weight; (4) scrape the coating solution on the outer layer of the blended fabric with a scraper, and the thickness of the coating solution is 2.5mm; (5) ventilate and dry the blended fabric, A wear-resistant and antibacterial blended fabric is prepared.

Embodiment 2

[0010] (1) To prepare fabric coating solution, take 7kg of polyvinyl alcohol tert-butyraldehyde, 3kg of dibutyl sebacate, 7kg of dammar resin, 5kg of ethyl acetate, 6kg of magnesium oxide, 3kg of zinc oxide, 17kg of ethanol; (2) Dissolve the ingredients in step (1) after heating, stir evenly after dissolving, seal and keep warm at 80°C after stirring; (3) take the blended fabric of cotton and polyvinyl chloride, the cotton content is the total weight 70wt% of the total weight, and the content of polyvinyl chloride is 30wt% of the total weight; (4) scrape the coating solution on the outer layer of the blended fabric with a scraper, and the thickness of the coating solution is 2mm; (5) ventilate and dry the blended fabric to prepare Wear-resistant and antibacterial blended fabric.

Embodiment 3

[0012] (1) To prepare fabric coating solution, take 9kg of polyvinyl alcohol tert-butyraldehyde, 4kg of dibutyl sebacate, 8kg of dammar resin, 7kg of ethyl acetate, 4kg of magnesium oxide, and 4kg of zinc oxide, 19kg of ethanol; (2) Heat the ingredients in step (1) to dissolve, stir evenly after dissolving, seal and keep warm at 80°C after stirring; (3) Take the blended fabric of cotton and polyvinyl chloride, the cotton content is the total weight 65wt% of the total weight, and the content of polyvinyl chloride is 35wt% of the total weight; (4) scrape the coating liquid on the outer layer of the blended fabric with a scraper, and the thickness of the coating liquid is 1.5mm; (5) ventilate and dry the blended fabric, A wear-resistant and antibacterial blended fabric is prepared.

[0013] Get the blended fabric of embodiment 1, embodiment 2, embodiment 3, measure its abrasion resistance with fabric flat grinder, diameter is 120cm, and weight is 300g, measures the weight loss ra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of a wearproof and antibacterial blended fabric. The preparation method comprises the following steps: (1) preparing fabric coating liquid from 5-9 parts of polyvinyl alcohol tert-butyraldehyde, 3-5 parts of dibutyl sebacate, 7-10 parts of dammar, 5-7 parts of ethyl acetate, 4-6 parts of magnesium oxide, 3-4 parts of zinc oxide and 15-19 parts of ethanol; (2) heating and then dissolving the components in the step (1), stirring the components uniformly after dissolving, and sealing and insulating the components at 80 DEG C after uniform stirring; (3) taking a cotton and polyvinyl chloride blended fabric; (4) blade-coating the coating liquid at the outer layer of the blended fabric with a scraper blade; (5) ventilating and drying the blended fabric, thus preparing the wearproof and antibacterial blended fabric.

Description

technical field [0001] The invention relates to a preparation method of a blended fabric, in particular to a preparation method of a cotton and polychloride blended fabric with good wear resistance and antibacterial properties. Background technique [0002] When applying textiles outdoors, the wear resistance and antibacterial effects of textiles need to be considered. Conventional textiles do not have antimicrobial properties. After finishing, some textiles have antibacterial properties. Usually fabrics have antibacterial properties because they are attached with some antibacterial compositions, which are usually inorganic compounds or some antibacterial substances extracted naturally. After these compounds are mixed with some wear-resistant material components, their antibacterial effect will be reduced. Significantly decreased, affecting the antibacterial properties of textiles. Therefore, we need to effectively match wear-resistant ingredients and antibacterial ingred...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/333D06M15/17D06M13/224D06M11/44D06M101/06D06M101/38
Inventor 张德轩
Owner 吴江市先锋针织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap