Rubber composition and pneumatic tire
A rubber composition and rubber technology, applied in special tires, tire parts, transportation and packaging, etc., can solve the problems of silica self-agglutination and dispersion difficulties, and achieve excellent performance
Inactive Publication Date: 2014-04-30
SUMITOMO RUBBER IND LTD
View PDF3 Cites 5 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0005] As a method of improving low fuel consumption and wet grip performance in a good balance, there is a method of using silica as a filler, but there is still room for further improvement in terms of silica's strong self-agglomeration and difficulty in dispersing
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0206] The present invention will be specifically described based on examples, but the present invention is not limited to the following examples.
[0207] The various chemicals used for synthesis and polymerization are summarized below. In addition, chemicals can be purified according to conventional methods if necessary.
[0208] n-Hexane: manufactured by Kanto Chemical Co., Ltd.
[0209] Styrene: manufactured by Kanto Chemical Co., Ltd.
[0210] 1,3-Butadiene: manufactured by Tokyo Chemical Industry Co., Ltd.
[0211] p-Methoxystyrene: manufactured by Kanto Chemical Co., Ltd. (compound represented by formula (I))
[0212] p-tert-butoxystyrene: manufactured by Wako Pure Chemical Industries, Ltd. (compound represented by formula (I))
[0213] Tetramethylethylenediamine: manufactured by Kanto Chemical Co., Ltd.
[0214] Modifier A-1: Dimethylamine manufactured by Kanto Chemical Co., Ltd.
[0215] Modifier A-2: Pyrrolidine manufactured by Kanto Chemical Co., Ltd.
[02...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| glass transition temperature | aaaaa | aaaaa |
| particle size | aaaaa | aaaaa |
| specific surface area | aaaaa | aaaaa |
Login to View More
Abstract
Provided are: a rubber composition which is capable of improving low fuel consumption and wet grip performance in a balanced manner; and a pneumatic tire which uses the rubber composition in tire constituent members (especially in a tread). The present invention relates to a rubber composition which contains: a rubber component that contains a copolymer which is obtained by copolymerizing 1,3-butadiene, styrene and a compound represented by formula (I), said copolymer having an amino group at one end, having a functional group containing at least one atom selected from the group consisting of nitrogen, oxygen and silicon at the other end, and having a weight average molecular weight of from 1.0*105 to 2.5*106; silica; and a diene rubber gel having a hydroxyl group and a glass transition temperature from -40 DEG C to -10 DEG C. The rubber composition contains 10-30 parts by mass of the diene rubber gel per 100 parts by mass of the rubber component.
Description
technical field [0001] The present invention relates to a rubber composition and a pneumatic tire prepared using the rubber composition. Background technique [0002] In recent years, from the standpoint of saving resources, saving energy, and protecting the environment, society has become increasingly demanding on reducing carbon dioxide emissions. Even for automobiles, for the purpose of reducing carbon dioxide emissions, various measures such as weight reduction of automobiles and utilization of electric energy have been studied. [0003] As a common problem for automobiles, it is necessary to improve fuel consumption by improving the rolling resistance of tires. In addition, there is an increasing demand for improved safety during driving of automobiles. The low fuel consumption and safety of automobiles largely depend on the performance of tires, and the requirements for the improvement of low fuel consumption, wet grip performance, driving stability, and durability of...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C08L15/00B60C1/00C08C19/25C08K3/36C08L9/00
CPCC08L15/00C08K3/36C08C19/22C08L9/06C08C19/44B60C1/0016C08K5/549C08L7/00C08L9/00
Inventor 冈部升上坂宪市
Owner SUMITOMO RUBBER IND LTD