Hyacinth-like coated glass and preparation method thereof

A technology for coating glass and hyacinth stone, which is applied in chemical instruments and methods, glass/slag layered products, layered products, etc. High hardness, the effect of delaying the oxidation rate

Active Publication Date: 2014-05-14
天津南玻节能玻璃有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The method of coating the diamond-like film on the outermost layer can play a great role in protecting the glass when the glass is not tempered, but it will react with oxygen and gasify during the glass tempering process, which will be lost in the subsequent processing and transportation. Protection for functional layers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hyacinth-like coated glass and preparation method thereof
  • Hyacinth-like coated glass and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A kind of low-radiation coated glass is plated by magnetron sputtering deposition method, the glass substrate, the functional film system layer coated on the surface of the glass substrate and the hyacinoid stone plated on the surface of the functional film system layer are mixed and mixed. Miscellaneous film layer, the above-mentioned film layers include in order from the glass substrate outward:

[0037] The base dielectric layer plated on the glass substrate, the material of the film layer is: titanium oxide film layer, and the thick plating is about 12nm.

[0038] The film material of the first barrier layer plated on the base dielectric layer is: a nickel-chromium alloy film layer with a thickness of about 4nm.

[0039] The material of the functional layer plated on the first barrier layer is: silver simple film layer with a thickness of about 12nm.

[0040] The film material of the second barrier layer plated on the functional layer is: a nickel-chromium alloy fi...

Embodiment 2

[0045] A low-radiation coated glass, a glass substrate, a functional film system layer coated on the surface of the glass substrate, and a hyacinoid mixed-doped film layer coated on the surface of the functional film system layer. The glass substrate outwardly includes:

[0046] The base dielectric layer plated on the glass substrate, the material of the film layer is: titanium oxide film layer, and the thick plating is about 12nm.

[0047] The film material of the first barrier layer plated on the base dielectric layer is: a nickel-chromium alloy film layer with a thickness of about 4nm.

[0048] The material of the functional layer plated on the first barrier layer is: silver simple film layer with a thickness of about 12nm.

[0049] The film material of the second barrier layer plated on the functional layer is: a nickel-chromium alloy film with a thickness of about 1 nm.

[0050] The top dielectric layer plated on the second barrier layer is made of silicon oxide film wi...

Embodiment 3

[0054] A low-radiation coated glass, a glass substrate, a functional film system layer coated on the surface of the glass substrate, and a hyacinoid mixed-doped film layer coated on the surface of the functional film system layer. The glass substrate outwardly includes:

[0055] The material of the first dielectric layer plated on the glass substrate is: zinc tin oxide film layer, and the thickness of the film layer is about 39.4nm.

[0056] The film material of the first barrier layer plated on the first dielectric layer is: nickel-chromium alloy film layer 3nm.

[0057] The material of the functional layer plated on the first barrier layer is silver-copper alloy with a thickness of about 6.7nm.

[0058] The film material of the second barrier layer plated on the functional layer is: nickel-chromium alloy film layer 1nm.

[0059] The material of the second dielectric layer plated on the second barrier layer is zinc oxide 20nm.

[0060] The top dielectric layer plated on th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses hyacinth-like coated glass and a preparation method thereof. The hyacinth-like coated glass comprises a glass substrate, one layer or multi-layers of functional film layers with which the surface of the glass substrate is coated, and a hyacinth-like-mixed and doped film layer with which the surface of the functional film layer is coated, wherein each functional film layer is a tempered low-radiation film layer, or a non-tempered low-radiation film layer or a solar control film layer. The coated hyacinth-like doped film has the high stability, the high temperature resistance, the wear resistance and the high chemical resistance. After glass of the hyacinth-like film layer is tempered, the transmission can be improved, the glass is not burnt like diamond-like carbon, the tempered glass can be well protected in the glass transport and storage processes, the scratch is avoided, and the oxidization is delayed.

Description

technical field [0001] The invention relates to the technical field of coated glass, in particular to coated glass doped with a hyacinoid. technical background [0002] At present, coated glass has been widely used in various fields due to its excellent performance. However, in the process of transportation and storage, the substrate film layer is easily scratched and worn, and its silver layer is easily damaged. In addition, the physical and chemical properties of coated glass are easy to change after various cold processing and heat treatment, such as slicing, edging, interlayer and other treatments. In response to this problem, most domestic glass deep-processing enterprises currently use PE organic film to protect the substrate film layer, which can play a certain protective effect. However, when using the substrate, it is necessary to manually remove the film, and the protective film cannot be reused. A unit square meter of glass requires a unit square meter of PE film...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B9/04B32B15/04B32B17/00
Inventor 王勇曾小绵彭立群王烁宋宇秦伟哲
Owner 天津南玻节能玻璃有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap