A solar photovoltaic glass with high light transmittance

A technology of photovoltaic glass and high light transmittance, applied in the field of solar photovoltaic preparation, can solve the problems of unsatisfactory effect of single-layer film, inconvenient processing, etc., to promote absorption of solar energy, avoid thermal decay, and improve the relative conversion rate of photoelectricity Effect

Active Publication Date: 2017-01-25
泰州恒润玻璃有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the unsatisfactory effect of a single-layer film, in order to achieve the desired effect, 2-3 layers of coating or mixed coating must be used, which is extremely inconvenient to process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A solar photovoltaic glass with high light transmittance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A solar photovoltaic glass with high light transmittance, comprising a glass body 1, a coating film 2 is provided on the surface of the glass body 1, the coating film is formed by a coating solution, and 60 parts of silicon dioxide, tetraethyl orthosilicate 15 parts and 10 parts of ethanol, stirred at a speed of 1200r / min for 30min, mixed them uniformly to form a mixed solution, dripped 6 parts of ammonia water into the mixed solution, stirred at a speed of 1200r / min for 2 hours, and made a silica solution Sealed for use; take 30 parts of titanium dioxide, 2.5 parts of tetrabutyl titanate and 10 parts of ethanol and mix uniformly to form a mixed solution, add 8 parts of hydrochloric acid to the mixed solution, stir well, and make a titanium dioxide solution sealed for use; take silicon dioxide Mix 80 parts of solution and 12 parts of titanium dioxide solution evenly to form a mixed solution, add 0.1 part of triethanolamine, 0.1 part of polyethylene glycol and 0.1 part of...

Embodiment 2

[0038] A solar photovoltaic glass with high light transmittance, comprising a glass body 1, a coating film 2 is provided on the surface of the glass body 1, the coating film is formed by a coating solution, and 63 parts of silicon dioxide, tetraethyl orthosilicate 16 parts and 12.5 parts of ethanol, stirred at a speed of 1200r / min for 30min, mixed them uniformly to form a mixed solution, dripped 7 parts of ammonia water into the mixed solution, stirred at a speed of 1200r / min for 2 hours, and made a silicon dioxide solution Seal it for use; take 35 parts of titanium dioxide, 3 parts of tetrabutyl titanate and 11.5 parts of ethanol and mix evenly to form a mixed solution, add 9 parts of hydrochloric acid to the mixed solution, stir evenly, and make a titanium dioxide solution and seal it for use; take silicon dioxide 82 parts of the solution and 13 parts of the titanium dioxide solution were mixed uniformly to form a mixed solution, and 0.8 parts of triethanolamine, 0.8 parts of...

Embodiment 3

[0041] A solar photovoltaic glass with high light transmittance, comprising a glass body 1, a coating film 2 is provided on the surface of the glass body 1, the coating film is formed by a coating solution, and 65 parts of silicon dioxide, tetraethyl orthosilicate 18 parts and 15 parts of ethanol, stirred at a speed of 1200r / min for 30min, mixed them evenly to form a mixed solution, dripped 8 parts of ammonia water into the mixed solution, stirred at a speed of 1200r / min for 2 hours, and made a silica solution Seal it for use; take 39 parts of titanium dioxide, 5.5 parts of tetrabutyl titanate and 13.5 parts of ethanol and mix evenly to form a mixed solution, add 11 parts of hydrochloric acid to the mixed solution, stir evenly, and make a titanium dioxide solution and seal it for use; 88 parts of the solution and 14 parts of the titanium dioxide solution were mixed evenly to form a mixed solution, and 1.6 parts of triethanolamine, 1.8 parts of polyethylene glycol and 1.8 parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-transparency solar photovoltaic glass which comprises a glass body, wherein a coating film is arranged on the surface of the glass body, and is formed by a film coating solution; the film coating solution comprises the following components in parts by volume: a silicon dioxide solution, a titanium dioxide solution, triethanolamine, polyethylene glycol, ethylene glycol and aluminum oxide. The film coating solution is used for preparing an inorganic hybrid membrane layer with a porous structure by using nanometer silicon dioxide as a basic system, main components of the nanometer silicon dioxide material is consistent with main components of the photovoltaic glass, and the binding performance of nanometer silicon dioxide material and the glass body is good; silicon dioxide is very stable at normal temperature, and has better acid and alkaline resistance and high-temperature resistance.

Description

technical field [0001] The invention relates to a solar photovoltaic glass, in particular to a solar photovoltaic glass with high light transmittance, and belongs to the technical field of solar photovoltaic preparation. Background technique [0002] At present, the well-known photoelectric conversion of solar energy depends on the silicon wafer in the solar cell module, which has a good light absorption effect. With the continuous improvement of solar cell modules, the photoelectric conversion rate of the silicon wafer in the solar cell module is The current manufacturing level has reached the limit, and it has become a difficult problem to improve the photoelectric conversion rate of solar cells. At the same time, since the workplaces of solar cells are mostly installed outdoors or in deserts with harsh environments, the surface of solar cell modules is easy to get dirty, and it is difficult to clean after being dirty. One of the existing methods to solve the photoelectri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C17/23
Inventor 于静
Owner 泰州恒润玻璃有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products