A kind of high-strength supramolecular hydrogel and its preparation method and application

A supramolecular hydrogel, high-strength technology, applied in the field of biomedical materials, can solve the problems of difficult to meet the long-term sustained release of gene drugs, rapid degradation, etc., to increase degradability, maintain biological activity, and the preparation method is simple and fast. Effect

Inactive Publication Date: 2017-04-12
广州新犇富科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the gene transfection efficiency of this material has been improved, its degradation is too fast to meet the purpose of long-term sustained release of gene medicine

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-strength supramolecular hydrogel and its preparation method and application
  • A kind of high-strength supramolecular hydrogel and its preparation method and application
  • A kind of high-strength supramolecular hydrogel and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A method for preparing high-strength supramolecular hydrogel includes the following steps:

[0045] 1. Drying of polyethylene glycol: The polyethylene glycol is vacuum dried at 60°C for 24 hours.

[0046] 2. Drying of caprolactone monomer: distill the caprolactone monomer under reduced pressure at 90°C.

[0047] 3. Drying of dichloromethane and pyridine: add calcium hydride powder to dichloromethane or pyridine solution (add 1-2 grams of calcium hydride per 500ml solution), stir at room temperature for 24 hours and then distill.

[0048] 4. Synthesis of polyethylene glycol-polycaprolactone-polycationic copolymer (corresponding to "Step 1)" in the claims);

[0049] a. Synthesis of polyethylene glycol-polycaprolactone block polymer:

[0050] 15 grams of dry polyethylene glycol (weight average molecular weight 1900), 10 grams of caprolactone monomer, and 0.05 grams of stannous octoate were added to the reaction device at the same time, and the oil pump was used to vacuum for 40 minut...

Embodiment 2

[0060] A method for preparing high-strength supramolecular hydrogel includes the following steps:

[0061] 1. Drying of polyethylene glycol: The polyethylene glycol is vacuum dried at 60°C for 24 hours.

[0062] 2. Drying of caprolactone monomer: distill the caprolactone monomer under reduced pressure at 90°C.

[0063] 3. Drying of dichloromethane and pyridine: add calcium hydride powder to dichloromethane or pyridine solution (add 1-2 grams of calcium hydride per 500ml solution), stir at room temperature for 24 hours and then distill.

[0064] 4. Synthesis of polyethylene glycol-polycaprolactone-polycationic copolymer (corresponding to "Step 1)" in the claims);

[0065] a. Synthesis of polyethylene glycol-polycaprolactone block polymer:

[0066] 15 grams of dry polyethylene glycol (weight average molecular weight 1900), 5 grams of caprolactone monomer, and 0.05 grams of stannous octoate were added to the reaction device at the same time, and the oil pump was used to vacuum for 40 minute...

Embodiment 3

[0076] A method for preparing high-strength supramolecular hydrogel includes the following steps:

[0077] 1. Drying of polyethylene glycol: The polyethylene glycol is vacuum dried at 60°C for 24 hours.

[0078] 2. Drying of caprolactone monomer: distill the caprolactone monomer under reduced pressure at 90°C.

[0079] 3. Drying of dichloromethane and pyridine: add calcium hydride powder to dichloromethane or pyridine solution (add 1-2 grams of calcium hydride per 500ml solution), stir at room temperature for 24 hours and then distill.

[0080] 4. Synthesis of polyethylene glycol-polycaprolactone-polycationic copolymer (corresponding to "Step 1)" in the claims);

[0081] a. Synthesis of polyethylene glycol-polycaprolactone block polymer:

[0082] 15 grams of dry polyethylene glycol (weight average molecular weight 5000), 10 grams of caprolactone monomer, and 0.05 grams of stannous octoate were added to the reaction device at the same time, and the oil pump was used to vacuum for 40 minut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing high-strength supramolecular hydrogel. The method comprises the following steps: (1) synthesizing polyethylene glycol-polycaprolactone-polycationic copolymer; (2) preparing a copolymer / nucleic acid composite liquid; and (3) mixing the copolymer / nucleic acid composite liquid obtained in the step (2) and an alpha-cyclodextrin liquid to prepare the high-strength supramolecular hydrogel. The invention also relates to the high-strength supramolecular hydrogel prepared by the method and an application of the hydrogel. The hydrogel forming process does not have chemical crosslinking reactions, the influence of chemical crosslinking reaction by-products on the activity of nucleic acid can be effectively avoided, the hydrogel has an effective gene transfer effect, the preparation method is convenient and quick, the hydrogel can be formed at room temperature, and the bioactivity of an embedded gene and the biocompatibility of a material can be kept. According to the hydrogel, the defect of quick degradation of current similar gel materials can be overcome, the nucleic acid can be released for more than 2 weeks, and the aim of long-time durable transfection can be achieved.

Description

Technical field [0001] The invention relates to the field of biomedical materials, in particular to a high-strength supramolecular hydrogel that can be used as a gene carrier, and a preparation method and application thereof. Background technique [0002] Gene therapy refers to the introduction of foreign genes into cells to correct or compensate diseases caused by gene defects and abnormalities to achieve the purpose of treatment. It is currently an effective method for the treatment of cancer and congenital immune system diseases. The key to the implementation of this technology is to select a suitable gene vector and gene introduction method, so that the gene can be safely, efficiently, controlled and stable expression in the cell. As a type of biomedical material that can be used as a drug or gene carrier, hydrogel has the characteristics of high loading rate, protection of macromolecular drugs from biological degradation or removal, and sustainable release of drug molecules....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K48/00A61K47/34C08J3/075C08G81/00C08G63/91C08G63/664A61P35/00A61P37/02
Inventor 张宏斌武婕隆湘蕾
Owner 广州新犇富科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com