Top-grade shirt fabric formed by interweaving long stapled cotton and mulberry silk

A technology of mulberry silk and long-staple cotton is applied in the field of high-grade shirt fabrics, which can solve the problems of low manufacturing cost, rough fabric texture, poor air permeability, etc., and achieve the effects of reducing production cost, good moisture dissipation performance, and increasing resilience.

Active Publication Date: 2014-10-08
苏州新超针纺织有限公司
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, in the direct sales of shirts in China, medium and high-end shirts are more similar to fine denim Oxford fabrics. The manufacturing cost is low, and the fabric texture is thick. It is a low-end shirt fabric, which is not in line with the life style of the upper class and mainstream business concepts.
At the same time, according to European and American practices, high-grade pure cotton fabrics do not use iron-free finishing, which belongs to chemical treatment, which often changes the skin-friendly characteristics of pure cotton fabrics, and leaves harmful chemicals at the same time. The fabric with non-ironing effect has lost the elasticity and skin-friendly feeling of pure cotton, and the touch feels close to chemical fiber fabrics
[0003] With the provision of people's living standards, more and more attention is paid to the quality of shirt fabrics. However, the existing shirt fabrics still have the disadvantages of poor air permeability, bad hand feeling, and not comfortable enough to wear next to the body.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A high-grade shirt fabric interwoven with long-staple cotton and mulberry silk, which is blended with 50wt% Egyptian long-staple cotton and 50wt% mulberry silk, the Egyptian long-staple cotton is a warp yarn, and the mulberry silk is a weft yarn. The warp yarn density is 100 / cm, the weft yarn density is 60 / cm, the yarn of the long-staple cotton is 180N / 3, the mulberry silk is double-strand 20 / 22d, and the width of the shirting fabric is 44 inches, the sizing rate reaches 96% during the sizing.

[0028] The weaving process of described shirt fabric comprises:

[0029] Ⅰ. Sectional warping: the warp and weft yarns are made into warp beams through the GAI62E warping machine, and the speed is 720m / min;

[0030] Ⅱ. Two-for-one twisting: the twist of the yarn is increased through the CY98 two-for-one twisting machine;

[0031] Ⅲ. Sizing: Put the finished warp beam on the sizing machine, suck the warp surface through the trough, and dry it in an oven;

[0032] Ⅳ. Steaming a...

Embodiment 2

[0044] A high-grade shirt fabric interwoven with long-staple cotton and mulberry silk, which is blended with 42wt% Egyptian long-staple cotton and 58wt% mulberry silk, the Egyptian long-staple cotton is warp yarn, and the mulberry silk is weft yarn. The warp yarn density is 80 / cm, the weft yarn density is 58 / cm, and the yarn of the long-staple cotton is 180N / 3; the mulberry silk is double-strand 20 / 22d, and the width of the shirt fabric is 40 inches, the sizing rate reaches 95% during the sizing.

[0045] The weaving process of described shirt fabric comprises:

[0046] Ⅰ. Sectional warping: the warp and weft yarns are made into warp beams through the GAI62E warping machine, and the speed is 650m / min;

[0047] Ⅱ. Two-for-one twisting: the twist of the yarn is increased through the CY98 two-for-one twisting machine;

[0048] Ⅲ. Sizing: Put the finished warp beam on the sizing machine, suck the warp surface through the trough, and dry it in an oven;

[0049] Ⅳ. Steaming and ...

Embodiment 3

[0061] A high-grade shirt fabric interwoven with long-staple cotton and mulberry silk, which is blended with 65wt% Egyptian long-staple cotton and 35wt% mulberry silk, the Egyptian long-staple cotton is a warp yarn, and the mulberry silk is a weft yarn. The warp density is 120 / cm, the weft density is 65 / cm, and the yarn of the long-staple cotton is 180N / 3; the mulberry silk is a single strand 20 / 22d, and the width of the shirt fabric is 45 inches, the sizing rate reaches 96% during the sizing.

[0062] The weaving process of described shirt fabric comprises:

[0063] Ⅰ. Sectional warping: the warp and weft yarns are made into warp beams through the GAI62E warping machine, and the speed is 800m / min;

[0064] Ⅱ. Two-for-one twisting: the twist of the yarn is increased through the CY98 two-for-one twisting machine;

[0065] Ⅲ. Sizing: Put the finished warp beam on the sizing machine, suck the warp surface through the trough, and dry it in an oven;

[0066] Ⅳ. Steaming and sett...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a top-grade shirt fabric formed by interweaving long stapled cotton and mulberry silk. The top-grade shirt fabric is formed by blending 42-65wt% of Egyptian long stapled cotton and 35-58wt% of the mulberry silk, the Egyptian long stapled cotton is warp, the mulberry silk is weft, the density of the warp is 80-120 pieces per centimeter, the density of the weft is 58-65 pieces per centimeter, and the specification of yarn made of the long stapled cotton is 180 N / 3. The top-grade shirt fabric has the advantages that the Egyptian long stapled cotton is added to the mulberry silk, characteristics of cotton are integrated with real silk, the smooth and skin-care characteristics of a common real silk fabric are achieved, real silk raw materials are saved, and accordingly production cost is reduced, and the product can be popular with more consumers; meanwhile, due to the adoption of cotton yarn, the fabric is easy to clean, the defects that the real silk is not suitable for being washed in water and is prone to wrinkling are overcome, water shrinkage is reduced, and elastic resilience, wear resistance, breaking strength and moisture absorption are improved; when the fabric is worn next to the skin, and the fabric does good to the human body, enables the skin to be smooth and has good moisture absorption performance and breathability.

Description

technical field [0001] The invention relates to a high-grade shirt fabric interwoven with long-staple cotton and mulberry silk, belonging to the technical field of textiles. Background technique [0002] At present, in the direct sales of shirts in China, medium and high-end shirts are more similar to fine denim Oxford fabrics. The manufacturing cost is low, and the fabric texture is thick. It is a low-end shirt fabric, which is not in line with the life style of the upper class and mainstream business concepts. . At the same time, according to European and American practices, high-grade pure cotton fabrics do not use iron-free finishing, which belongs to chemical treatment, which often changes the skin-friendly characteristics of pure cotton fabrics, and leaves harmful chemicals at the same time. The fabric with non-ironing effect has lost the elasticity and skin-friendly feeling of pure cotton, and the touch feels close to chemical fiber fabrics. [0003] With the provis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A41D31/00D03D15/00D03D13/00D06C27/00D06B21/00D06M16/00D06M15/53D06M11/38D06M101/06D06M101/10D03D15/217D03D15/233
Inventor 潘锦超
Owner 苏州新超针纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com