A kind of fullerene reinforced ceramic brick

A technology of fullerenes and ceramic bricks is applied in the field of refractory ceramic bricks to achieve the effects of facilitating industrial production, reducing weight and having good mechanical properties

Inactive Publication Date: 2016-05-18
朱玉华
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still many challenges in the application of fullerenes and nanomaterials to the field of fullerene-enhanced ceramic tiles.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A fullerene-enhanced ceramic tile, the green body consists of:

[0025] 10 parts of potassium feldspar; 10 parts of albite; 15 parts of clay; 30 parts of attapulgite; 20 parts of bauxite; 30 parts of water; 1 part of fullerene; 1 part of sodium tripolyphosphate; 1 part of tempered fiber;

[0026] The glaze weight part consists of:

[0027] 15 parts of feldspar, 10 parts of kaolin, 8 parts of quartz, 10 parts of burnt talc, 13 parts of limestone, 0.5 parts of iron oxide, 3 parts of diboron trioxide, 8 parts of alumina, 5 parts of diatomaceous earth, 6 parts of magnesia, 5 parts of zirconium silicate, 1 part of titanium oxide, 1 part of zinc oxide, 1 part of terbium oxide, 1 part of samarium oxide, 1 part of lutetium oxide, and 1 part of gold nanoparticles; the size of the gold nanoparticles is 10 nm;

[0028] The fullerene-enhanced ceramic tiles are prepared by the following preparation method:

[0029] (1) After mixing the green body raw materials in proportion, perfo...

Embodiment 2

[0033] A fullerene-enhanced ceramic tile, the green body consists of:

[0034] 10 parts of potassium feldspar; 10 parts of albite; 15 parts of clay; 30 parts of attapulgite; 20 parts of bauxite; 30 parts of water; 1 part of fullerene; 1 part of sodium tripolyphosphate; 1 part of tempered fiber;

[0035] The glaze weight part consists of:

[0036] 15 parts of feldspar, 10 parts of kaolin, 8 parts of quartz, 10 parts of burnt talc, 13 parts of limestone, 0.5 parts of iron oxide, 3 parts of diboron trioxide, 8 parts of alumina, 5 parts of diatomaceous earth, 6 parts of magnesia, 5 parts of zirconium silicate, 1 part of titanium oxide, 1 part of zinc oxide, 1 part of terbium oxide, 1 part of samarium oxide, 1 part of lutetium oxide, and 1 part of silver nanoparticles; the size of the silver nanoparticles is 10 nm;

[0037] The fullerene-enhanced ceramic tiles are prepared by the following preparation method:

[0038] (1) After mixing the green body raw materials in proportion, p...

Embodiment 3

[0042] A fullerene-enhanced ceramic tile, the green body consists of:

[0043] 10 parts of potassium feldspar; 10 parts of albite; 15 parts of clay; 30 parts of attapulgite; 20 parts of bauxite; 30 parts of water; 1 part of fullerene; 1 part of sodium tripolyphosphate; 1 part of tempered fiber;

[0044] The glaze weight part consists of:

[0045] 15 parts of feldspar, 10 parts of kaolin, 8 parts of quartz, 10 parts of burnt talc, 13 parts of limestone, 0.5 parts of iron oxide, 3 parts of diboron trioxide, 8 parts of alumina, 5 parts of diatomaceous earth, 6 parts of magnesia, 5 parts of zirconium silicate, 1 part of titanium oxide, 1 part of zinc oxide, 1 part of terbium oxide, 1 part of samarium oxide, 1 part of lutetium oxide, and 1 part of copper nanoparticles; the size of the copper nanoparticles is 10 nm;

[0046] The fullerene-enhanced ceramic tiles are prepared by the following preparation method:

[0047] (1) After mixing the green body raw materials in proportion, p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fullerene reinforced ceramic tile. The fullerene reinforced ceramic tile with good mechanical properties is obtained by applying a glaze on the surface of a green body in a glaze spraying or sprinkling manner, wherein potassium feldspar, albite, clay, attapulgite, alumina, water, fullerene, sodium tripolyphosphate and tempered fiber serve as raw materials of the green body, feldspar, kaoline, quartz, burnt talcum, limestone, iron oxide, diboron pentoxide, alumina, kieselguhr, magnesite, zirconium silicate, titanium oxide, zinc oxide, terbium oxide, samarium oxide, lutecia and metal nano particles serve as raw materials of the glaze, and a glazed surface of the ceramic tile is attractive and elegant.

Description

technical field [0001] The invention belongs to the field of refractory ceramic bricks, in particular to a fullerene-reinforced ceramic brick. Background technique [0002] With the rapid development of my country's building ceramics industry, my country's demand for building ceramic materials is also increasing, especially in the field of fullerene-enhanced ceramic tiles. In this field, too, more and more attention is paid to the impact of new materials on fullerene-reinforced ceramic tiles. And by introducing new materials, the external appearance, internal physical and chemical properties, and health and environmental protection of fullerene-enhanced ceramic tiles can be improved. [0003] In the field of materials, fullerenes and nanomaterials have broad application prospects due to their excellent mechanical, electrical and chemical properties. The application of fullerenes to the field of ceramics is now the focus of scientists' research. The introduction of ene into...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B41/86
Inventor 朱玉华
Owner 朱玉华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com