Synthesis process for special engineering plastic polyetheretherketone
A technology of special engineering plastics and polyether ether ketone, which is applied in the field of organic polymer synthesis, can solve problems such as negative effects, and achieve the effect of avoiding side reactions and improving reaction yield
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0009] A 1-liter three-neck glass flask is equipped with a mechanical stirrer, an oil-water separator, a glass condenser and a thermometer. Add 33.1 grams of hydroquinone, 62 grams of 40% aqueous sodium hydroxide solution, and 150 grams of toluene in the bottle. Heating to the reflux of the solvent and maintaining the reflux state, the water is continuously separated from the oil-water separator. After reacting for three hours, no moisture was produced in the oil-water separator. A white solid appeared in the reaction vial. The reaction was stopped, and the white solid sodium hydroquinone was filtered to remove toluene, and the solid was dried to obtain 47 grams of solid powder.
[0010] Add 300 grams of sulfolane, 67.1 grams of 4,4-difluorobenzophenone, and 47 grams of the above-mentioned solid powder in a four-neck flask equipped with a condenser, a thermometer, and an N2 port. Heating to raise the temperature, the temperature rises to 280°C and maintains it. The reactio...
Embodiment 2
[0012] A 1-liter three-neck glass flask is equipped with a mechanical stirrer, an oil-water separator, a glass condenser and a thermometer. Add 33.1 grams of hydroquinone, 84 grams of 40% potassium hydroxide aqueous solution, and 150 grams of toluene in the bottle. Heating to the reflux of the solvent and maintaining the reflux state, the water is continuously separated from the oil-water separator. After reacting for three hours, no moisture was produced in the oil-water separator. A white solid appeared in the reaction vial. The reaction was stopped, and the white solid potassium hydroquinone was filtered to remove toluene, and the solid was dried to obtain 67 grams of solid powder.
[0013] Add 300 grams of sulfolane, 67.1 grams of 4,4-difluorobenzophenone, and 67 grams of the above-mentioned solid powder in a four-necked flask equipped with a condenser, a thermometer, and an N2 port. Heating to raise the temperature, the temperature rises to 280°C and maintains it. The...
Embodiment 3
[0015] A 1-liter three-neck glass flask is equipped with a mechanical stirrer, an oil-water separator, a glass condenser and a thermometer. Add 33.1 grams of hydroquinone, 44 grams of lithium hydroxide monohydrate, and 150 grams of toluene into the bottle. Heating to the reflux of the solvent and maintaining the reflux state, the water is continuously separated from the oil-water separator. After reacting for three hours, no moisture was produced in the oil-water separator. A white solid appeared in the reaction vial. The reaction was stopped, and the white solid potassium hydroquinone was filtered to remove toluene, and the solid was dried to obtain 38 grams of solid powder.
[0016] Add 300 grams of sulfolane, 67.1 grams of 4,4-difluorobenzophenone, and 47 grams of the above-mentioned solid powder in a four-neck flask equipped with a condenser, a thermometer, and an N2 port. Heating to raise the temperature, the temperature rises to 280°C and maintains it. The reaction s...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap