A kind of lubricating grease specially used for plastic gears and its preparation method

A lubricating grease and gear technology, which is applied in the field of lubricating grease for plastic gears and its preparation, can solve the problems of poor compatibility of plastic materials, large starting resistance at low temperature, poor oxidation resistance, etc., and achieve good adhesion, small low temperature resistance, The effect of small friction coefficient

Active Publication Date: 2017-08-25
安徽中天石化股份有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, lubricants made of polymer materials on the market can meet high-temperature performance and adhesion performance, but low-temperature start-up resistance is large and noise is large. Greases made of metal soaps have poor oxidation resistance, are easy to lose at high temperatures, and are compatible with plastic materials. Poor performance, short service life and no insulation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of lubricating grease specially used for plastic gears and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The embodiment of the present invention provides a kind of lubricating grease specially used for plastic gears, which comprises: 4-8 parts of aniline, 3-5 parts of cyclohexylamine, MDI (diphenylmethane-4,4'-diisocyanate) 3 -6 parts, 60-80 parts of base oil, 1-2 parts of antioxidant A, 2-3 parts of antioxidant B, 1-2 parts of extreme pressure and anti-wear agent, 5-10 parts of tackifier, 1.5- parts of solid lubricant 3 copies.

[0023] Wherein said base oil adopts PAO-8 synthetic oil; said antioxidant A is diphenylamine; said antioxidant B is butyl octyl zinc salt; said extreme pressure antiwear agent is trimethyl phosphate Phenol ester; the tackifier is low molecular weight polyisobutylene PB2400; the solid lubricant is boron nitride.

Embodiment 2

[0025] A preparation method of lubricating grease specially used for plastic gears,

[0026] First provide according to the weight ratio: 4-8 parts of aniline, 3-5 parts of cyclohexylamine, 3-6 parts of MDI (diphenylmethane-4,4'-diisocyanate), 60-80 parts of base oil, antioxidant A1 -2 parts, 2-3 parts of antioxidant B, 1-2 parts of extreme pressure anti-wear agent, 5-10 parts of tackifier, 1.5-3 parts of solid lubricant, and then carry out the following steps:

[0027] (1) 80% base oil is put into saponification kettle by weight proportion, and is heated up to 40-60 ℃;

[0028] (2) drop aniline and cyclohexylamine into the saponification kettle by weight and stir evenly with the mixture of step (1), and the stirring time is 5-10 minutes;

[0029] (3) Warm up to 60-80°C, put MDI into the mixture of step (2) according to specific gravity and mix, fully stir until fully dissolved;

[0030] (4) Slowly heat up for 2-3 hours, stop heating when the temperature is raised to 180-200...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A grease specially used for plastic gears, which includes: 4-8 parts of aniline, 3-5 parts of cyclohexylamine, 3-6 parts of MDI (diphenylmethane-4,4'-diisocyanate), base 60-80 parts of oil, 1-2 parts of antioxidant A, 2-3 parts of antioxidant B, 1-2 parts of extreme pressure and anti-wear agent, 5-10 parts of tackifier, 1.5-3 parts of solid lubricant; The invention also provides a preparation method of lubricating grease specially used for plastic gears. The lubricating grease described in the present invention has superior noise reduction and anti-wear properties, good water resistance, small low-temperature torque, high-temperature non-diffusion, good adhesion, long-lasting noise reduction, excellent lubricity, reduced friction coefficient, and anti-oxidation Good performance, long-lasting lubricity and long service life. Moreover, the preparation method is simple and easy to operate, and the product has good effect in use.

Description

technical field [0001] The invention relates to the field of lubricating grease, in particular to lubricating grease specially used for plastic gears and a preparation method thereof. Background technique [0002] With the development of science and the lightweight requirements for gear products, gears have changed from metal gears to plastic gears. Compared with metal gears, plastic gears have the advantages of light weight, low working noise, wear resistance, more complex shapes can be formed, and low mass production costs. They can be used in environments where metal gears are prone to corrosion and degradation. However, due to the shrinkage and water absorption of the plastic itself, the relative strength is relatively weak, the requirements for the working environment are high, and the temperature is sensitive. Therefore, plastic gears also have disadvantages such as low precision, short life, and high requirements for the use environment. With the application of new ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M169/00C10M177/00C10N40/04C10N50/10
Inventor 高晓谋高荣权
Owner 安徽中天石化股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com