High-wear resistance rubber material for tyre

A rubber material, high wear-resistant technology, used in special tires, tire parts, transportation and packaging, etc.

Inactive Publication Date: 2015-01-28
QINGDAO TORIX ELECTRONICS TECH
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The problem brought about is the safety of the vehicle. The requirement for the tire is to have a good grip on the road surface under the premise of ensuring high mileage (tread wear resistance), especially on wet roads in rainy days and winter ice and snow roads. good performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] A high wear-resistant rubber material for tires, which is made of the following raw materials in parts by weight:

[0009] 8-15 parts of calcium carbonate, 6-10 parts of cinder powder, 10-20 parts of carbon black, 20-30 parts of EPDM glue, 4-6 parts of defoamer, 6-8 parts of trichloropropyl phosphate, oxidation 3-6 parts of iron, 2-5 parts of smoked sheet glue, 1-5 parts of paraffin, 4-7 parts of magnesium oxide, 2-5 parts of active agent, 4-6 parts of film-forming aid.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-wear resistance rubber material for a tyre. The high-wear resistance rubber material is prepared from 8-15 parts by weight of calcium carbonate, 6-10 parts by weight of coal slag powder, 10-20 parts by weight of carbon black, 20-30 parts by weight of ethylene-propylene-diene terpolymer, 4-6 parts by weight of an antifoaming agent, 6-8 parts by weight of trichloropropylphosphate, 3-6 parts by weight of iron oxide, 2-5 parts by weight of rubber smoked sheet, 1-5 parts by weight of paraffin, 4-7 parts by weight of magnesium oxide, 2-5 parts by weight of an activator and 4-6 parts by weight of a film-forming assistant. The high-wear resistance rubber material for a tyre has high temperature resistance, wear resistance and a certain skid resistance.

Description

technical field [0001] The invention relates to a high wear-resistant rubber material for tires. Background technique [0002] With the rapid development of highways and the acceleration of vehicle speeds, the driving speed rating of tires has also increased accordingly. The problem brought about is the safety of the vehicle. The requirement for the tire is to have a good grip on the road surface under the premise of ensuring high mileage (tread wear resistance), especially on wet roads in rainy days and winter ice and snow roads. Good performance. Tires with wear resistance, low rolling resistance and good wet skid resistance are called high-performance tires. Contents of the invention [0003] Aiming at the deficiencies of the prior art, the problem to be solved by the present invention is to provide a high wear-resistant rubber material for tires, which has wear-resistant and high-temperature-resistant properties, and at the same time has certain skid resistance. [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/16C08L7/00C08K13/02C08K3/26C08K3/04C08K5/521C08K3/22B60C1/00
CPCC08L23/16C08L2201/08C08L2205/03
Inventor 刘宏法
Owner QINGDAO TORIX ELECTRONICS TECH