One-component low-temperature polyurethane foam and preparation method thereof
A polyurethane foam, one-component technology, used in polyurea/polyurethane adhesives, adhesives, adhesive types, etc., can solve the problems of long dry time, high curing temperature, short surface dry time, etc. The effect of short dry time, low curing temperature and long surface dry time
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0028] The one-component low-temperature polyurethane foam of the present invention comprises 150 to 200 parts of polyhexamethylene adipate or polybutylene adipate; 5 to 10 parts of trimethylolpropane; 10 to 200 parts of polybutylene adipate; 30 parts of polyether 330N; 0.1 to 0.3 parts of catalyst; 80 to 150 parts of black material and 200 to 340 parts of solvent, all the parts mentioned in the present invention are parts by mass. In the present invention, the molecular weight of polyhexamethylene adipate or polybutylene adipate is 2000-4000, and the single-component low-temperature polyurethane foam in this embodiment includes polyhexamethylene adipate 150 parts of ester; 5 parts of polytrimethylolpropane; 10 parts of ether 330N; 0.1 part of catalyst; 80 parts of black material; 200 parts of solvent.
[0029] The black material of the present invention is any one in toluene diisocyanate, diphenylmethane diisocyanate, polymethyl polyphenylisocyanate, what the black material i...
Embodiment 2
[0033] The implementation of this example is the same as that of Example 1, except that the single-component low-temperature polyurethane foam in this example is composed of the following components by mass: 155 parts of polyhexamethylene adipate; 12 parts of polyether 330N; 90 parts of black material, what black material adopts is diphenylmethane diisocyanate; 6 parts of trimethylolpropane; 210 parts of solvent, what solvent adopts is trichloroethane; 0.14 part of catalyst, what catalyst uses is dilauric acid di Butyl tin. The surface-drying time of the one-component low-temperature polyurethane foam prepared in this example is 16 minutes, the curing temperature is 55° C., and the hard-drying time is 18 minutes.
Embodiment 3
[0035] The implementation of this example is the same as Example 1, except that the single-component low-temperature polyurethane foam in this example is composed of the following components by mass: 160 parts of polyhexamethylene adipate; 15 parts of polyether 330N; 95 parts of black material, the black material used is polymethyl polyphenyl isocyanate; 6.5 parts of trimethylolpropane; 240 parts of solvent, the solvent used is a compound of ethyl acetate and butyl acetate; 0.18 parts of catalyst , the catalyst used is bismorpholine. The surface-drying time of the one-component low-temperature polyurethane foam adhesive prepared in this example is 18 minutes, the curing temperature is 50° C., and the hard-drying time is 16 minutes.
PUM
Property | Measurement | Unit |
---|---|---|
tack-free time | aaaaa | aaaaa |
tack-free time | aaaaa | aaaaa |
tack-free time | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com