Sealing system of vacuum high-pressure casting mold of aluminum alloy structural member

A technology for high-pressure casting and structural parts, applied in the field of vacuum high-pressure casting molds for aluminum alloy structural parts, can solve the problems of reducing product strength, affecting the mechanical properties of castings, and low mold air tightness, and improving product quality.

Inactive Publication Date: 2015-02-04
KOLBENSCHMIDT PIERBURG SHANGHAI NONFERROUS COMPONENTS
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The bubbles not only affect the mechanical properties of the casting, but also reduce the strength of the product; in addition, if there are bubbles on the assembly surface of the casting, the bubbles will also affect the assembly of the parts. Therefore, when casting aluminum alloy structural parts, the quality of the casting should be improved , the mold must be fully sealed
However, when casting aluminum alloy structural parts, the mold cannot be fully sealed, in other words, the airtightness of the mold is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sealing system of vacuum high-pressure casting mold of aluminum alloy structural member
  • Sealing system of vacuum high-pressure casting mold of aluminum alloy structural member
  • Sealing system of vacuum high-pressure casting mold of aluminum alloy structural member

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] The implementation of the present invention will be illustrated by specific specific examples below, and those skilled in the art can easily understand other advantages and effects of the present invention from the contents disclosed in this specification.

[0035] see Figure 1 to Figure 6 . It should be noted that the structures, proportions, sizes, etc. shown in the drawings attached to this specification are only used to match the content disclosed in the specification, for those who are familiar with this technology to understand and read, and are not used to limit the implementation of the present invention. Limiting conditions, so there is no technical substantive meaning, any modification of structure, change of proportional relationship or adjustment of size, without affecting the effect and purpose of the present invention, should still fall within the scope of the present invention. within the scope covered by the disclosed technical content. At the same ti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a sealing system of a vacuum high-pressure casting mold of an aluminum alloy structural member. The casting mold comprises a movable mold frame and a fixed mold frame, wherein a movable mold insert with a cavity is mounted in the movable mold frame; a fixed mold insert with a cavity is mounted in the fixed mold frame; the sealing system of the vacuum high-pressure casting mold at least comprises a sealing structure between the mold frames, a sealing structure between the inserts, a sealing structure between the inserts and the mold frames, a sealing structure of an ejection mechanism, and a sealing structure between a cylinder and a mold; and the sealing structures can prevent air from entering the cavities, so that the mold is totally sealed, and the product quality can be improved.

Description

technical field [0001] The invention relates to a vacuum high-pressure casting mold of an aluminum alloy structural part, in particular to a sealing system of a vacuum high-pressure casting mold of an aluminum alloy structural part. Background technique [0002] There are many types of casting. According to the molding material, casting can be divided into special casting with natural mineral sand and stone as the main molding material (such as investment casting, mud casting, shell casting in foundry, negative pressure casting, solid casting, ceramic casting) etc.) and special casting with metal as the main casting material (such as metal casting, pressure casting, continuous casting, low pressure casting, vacuum high pressure casting, gravity casting, etc.). Vacuum high pressure casting is different from gravity casting and low pressure casting. The filling speed of gravity pouring and low pressure casting is relatively slow, so there is enough time for the filled aluminu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22D17/22
CPCB22D17/2227
Inventor 曹云喻晓奇杨春雷
Owner KOLBENSCHMIDT PIERBURG SHANGHAI NONFERROUS COMPONENTS