An anti-rust primer, stable technology, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems of use restrictions, etc., to achieve the effect of not easy to decompose, good adhesion, and good use effect
Inactive Publication Date: 2015-02-04
QINGDAO KANGTAIXIN ENVIRONMENTAL PROTECTION TECH
View PDF0 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The traditional anti-rust primer contains a large amount of heavy metals such as lead and hexavalent chromium. Because this anti-rust primer contains a lar
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0010] A stable anti-rust primer made of the following raw materials in parts by weight:
[0011] 20 parts of paint, 5 parts of antimony oxide, 4 parts of zeolite powder, 4 parts of film-forming aids, 8 parts of ethylene glycol butyl ether, 5 parts of aluminum tripolyphosphate, 2 parts of nitrocellulose, 2 parts of coupling agent, fluid 3 parts of leveling agent, 8 parts of acrylic acrylic resin, 2 parts of pigment, 3 parts of butylated amino resin, 1 part of matting powder, 3 parts of drying agent.
Embodiment 2
[0013] A stable anti-rust primer made of the following raw materials in parts by weight:
[0014] 30 parts of paint, 9 parts of antimony oxide, 8 parts of zeolite powder, 6 parts of film-forming aid, 11 parts of ethylene glycol butyl ether, 9 parts of aluminum tripolyphosphate, 6 parts of nitrocellulose, 7 parts of coupling agent, fluid 5 parts of leveling agent, 14 parts of acrylic acrylic resin, 4 parts of pigment, 9 parts of butylated amino resin, 5 parts of matting powder, and 6 parts of drying agent.
Embodiment 3
[0016] A stable anti-rust primer made of the following raw materials in parts by weight:
[0017] 25 parts of paint, 7 parts of antimony oxide, 6 parts of zeolite powder, 5 parts of film-forming aid, 9 parts of ethylene glycol butyl ether, 7 parts of aluminum tripolyphosphate, 4 parts of nitrocellulose, 4 parts of coupling agent, fluid 4 parts of leveling agent, 11 parts of acrylic acrylic resin, 3 parts of pigment, 6 parts of butylated amino resin, 3 parts of matting powder, and 5 parts of drying agent.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
A stable antirust primer is prepared from the following raw materials in parts by weight: 20-30 parts of a paint, 5-9 parts of antimony oxide, 4-8 parts of a zeolite powder, 4-6 parts of a film-forming auxiliary agent, 8-11 parts of ethylene glycol butyl ether, 5-9 parts of aluminum tripolyphosphate, 2-6 parts of nitro cellulose, 2-7 parts of a coupling agent, 3-5 parts of a levelling agent, 8-14 parts of polymethyl methacrylate acrylic resin, 2-4 parts of a pigment, 3-9 parts of butylated amino resin, 1-5 parts of a matting powder, and 3-6 parts of a dryer. The stable antirust primer has the beneficial effects that the stable antirust primer is stable in chemical properties, not easy to decompose, and good in use effect, besides, has quite good adhesiveness, and can be used for a long time.
Description
technical field [0001] The invention relates to a stable antirust primer. Background technique [0002] In order to obtain better decoration and corrosion resistance, various household appliances, motorcycle accessories and other metal parts are coated with multiple layers, such as primer, intermediate paint, varnish, etc. Anti-rust primer is generally used as a primer for base treatment, which mainly plays an anti-rust role. Because the anti-rust paint generally has a poor gloss, it is generally used as a primer. The existing ones mainly include iron red antirust primer, epoxy antirust primer, red lead antirust primer and alkyd antirust primer. Traditional anti-rust primers contain a large amount of heavy metals such as lead and hexavalent chromium. Because this anti-rust primer contains a large amount of harmful substances, it can no longer meet the requirements of new environmental protection regulations, and its use is increasingly restricted. Therefore need a kind of...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more