A kind of golden double-silver low-e glass with high light transmittance and preparation method thereof

A high light transmittance, golden technology, applied in chemical instruments and methods, glass/slag layered products, metal layered products, etc., can solve the problems of dull color tone and high production cost, and achieve high light transmittance and bright color Effect

Active Publication Date: 2016-04-13
JIEYANG HONGGUANG COATED GLASS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the existing golden coated glass products on the market, the color tone is dull and the production cost is high, and most of them are solar control coated glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of golden double-silver low-e glass with high light transmittance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] A golden double-silver LOW-E glass with high light transmittance, including a glass substrate 1, on the composite surface of the glass substrate, thirteen film layers are sequentially and adjacently compounded from the inside to the outside, of which the first The film layer, the innermost layer, is SSTZrO X layer 21, the second layer is AZO layer 22, the third layer is Si layer 23, the fourth layer is AZO layer 24, the fifth layer is Cu layer 25, and the sixth layer is CrN x o y Layer 26, the seventh layer is SnO 2 layer 27, the eighth layer is AZO layer 28, the ninth layer is Si layer 29, the tenth layer is AZO layer 210, the eleventh layer is Ag layer 211, and the twelfth layer is CrN x o y Layer 212, the outermost layer is Si 3 N 4 Layer 213.

[0034] The first film layer, that is, the innermost layer, is SSTZrO X Layer 21 is the zirconium-doped stainless steel layer. By doping zirconium into the stainless steel, the refractive index of the film layer is incr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a golden-class double-silver LOW-E glass with high light transmittance. The glass comprises a glass substrate, and is characterized in that thirteen film layers are sequentially compounded on the compound surface of the glass substrate in an adjacent way from inside to outside, wherein the first film layer is an SSTZrOX layer arranged at the innermost layer, the second film layer is an AZO layer, the third film layer is an Si layer, the fourth film layer is an AZO layer, the fifth film layer is a Cu layer, the sixth film layer is a CrN(x)O(y) layer, the seventh film layer is an SnO2 layer, the eighth film layer is an AZO layer, the ninth film layer is an Si layer, the tenth film layer is an AZO layer, the eleventh film layer is an Ag layer, the twelfth film layer is a CrN(x)O(y) layer, and the outermost layer is an Si3N4 layer. Aiming at overcoming the defects of the prior art, the golden-class double-silver LOW-E glass which is high in transmittance, bright in color, low in radiance, remarkable in energy-saving effect and low in production cost and has high light transmittance is provided. The invention also provides a method for preparing the golden-class double-silver LOW-E glass with high light transmittance by a magnetron sputtering method.

Description

【Technical field】 [0001] The invention relates to a gold-like double-silver LOW-E glass with high light transmittance, and also relates to a method for preparing the gold-like double-silver LOW-E glass with high light transmittance by a magnetron sputtering method. 【Background technique】 [0002] Coated glass has dual effects of energy saving and emission reduction and decorative curtain wall. As an unconventional variety of coated glass, golden glass is very popular. However, due to the existing golden coated glass products on the market, the color tone is dull and the production cost is high, and most of them are solar control coated glass. 【Content of invention】 [0003] The object of the present invention is to overcome the deficiencies of the prior art, and provide a gold-like double-silver LOW-E glass with high light transmittance, high transmittance, bright color, low emissivity, remarkable energy-saving effect, and low production cost. The invention also provides...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B9/04B32B15/00B32B15/20B32B17/00C03C17/36
Inventor 魏佳坤林改郑梅鹏宋晓群郑凯永
Owner JIEYANG HONGGUANG COATED GLASS