Self-cleaning type real stone lacquer and preparation method thereof

A real stone paint and self-cleaning technology, which is applied in the field of self-cleaning real stone paint and its preparation, can solve the problems of lack of preparation methods for self-cleaning real stone paint, troubles in the social environment of buildings, and rare building surfaces, etc., to achieve prolonged cleaning time, good freeze-thaw resistance, and reduced contact area

Inactive Publication Date: 2015-03-25
NANJING FORTUNE RECYCLING TECH
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The surface of the dusty building is washed by rainwater that also contains acid and alkali corrosion, forming water stains and stains. If the waterproof system of the building itself is damaged, the pollution surface of these water stains and stains will be greater, which will affect the building itself and the environment. The social environment brings more trouble
[0004] As we all know, the environmental sanitation of the urban ground can be improved with the help of sanitation workers, but the cleaning of the surface of buildings lined with forests is rare, and the cost is high and it is not easy to operate
[0005] Based on the above-mentioned present situation, there is currently a lack of a self-cleaning real stone paint with strong hydrophobicity and oil resistance and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-cleaning type real stone lacquer and preparation method thereof
  • Self-cleaning type real stone lacquer and preparation method thereof
  • Self-cleaning type real stone lacquer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The invention provides a self-cleaning real stone paint, which consists of the following components according to mass percentage:

[0025]

[0026] The binder is inorganic gelling synthetic resin and synthetic resin emulsion. The tailings powder contains silicon, and the silicon content accounts for more than 65% of the total tailings powder.

[0027] The binder is made of the following components in parts by weight:

[0028]

[0029] A kind of method for preparing described self-cleaning type genuine stone paint of the present invention, comprises the steps:

[0030] (1) Crush the natural gravel to a diameter of 0.2cm; in order to maintain the effect of marble, do not add any pigment or dye;

[0031] (2) Weigh the natural gravel, stone powder, binder, water-repellent, tailings powder and dispersant of the above ratio for standby; mix the stone powder and tailings powder into the natural gravel particles, stir evenly, and then add Stir the water-repellent agent...

Embodiment 2

[0039] The difference between embodiment 2 and embodiment 1 is: the present invention provides a kind of self-cleaning real stone paint, is made up of following components by mass percentage:

[0040]

[0041] The binder is an inorganic gelling synthetic resin.

[0042] The tailings powder contains silicon, and the silicon content accounts for more than 65% of the total tailings powder.

[0043] The binder is made of the following components in parts by weight:

[0044]

[0045] A kind of method for preparing described self-cleaning type genuine stone paint of the present invention, comprises the steps:

[0046] In step (1), crushing the natural gravel to a diameter of 0.6 cm;

[0047] In step (2), the natural crushed stone, stone powder, binder, water-repellent, tailings powder and dispersant of the above ratio are weighed for standby; the stone powder and tailings powder are mixed into the natural crushed stone particles, Stir, then add water-repellent agent for sti...

Embodiment 3

[0050] The difference between embodiment 3 and embodiment 1 is: the present invention provides a kind of self-cleaning genuine stone paint, is made up of following components by mass percentage:

[0051]

[0052] The binder is a synthetic resin emulsion.

[0053] The tailings powder contains silicon, and the silicon content accounts for more than 65% of the total tailings powder.

[0054] The binder is made of the following components in parts by weight:

[0055]

[0056] A kind of method for preparing described self-cleaning type genuine stone paint of the present invention, comprises the steps:

[0057]In step (1), the natural gravel is crushed to a diameter of 0.8cm; in step (2), the natural gravel, stone powder, binder, water repellent, tailings powder and dispersion Mix the stone powder and tailings powder into the natural gravel particles, stir evenly, then add water-repellent agent to stir, stir for 5 minutes, add binder and stir to obtain a uniformly stirred mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a self-cleaning type real stone lacquer and a preparation method thereof. The self-cleaning type real stone lacquer comprises the following components in percentage by weight: 55%-60% of natural gravels, 15%-20% of stone powder, 15%-20% of adhesion agents, 2%-4% of water repellents, 3%-5% of tailing powder and 3%-5% of dispersing agents. The self-cleaning type real stone lacquer disclosed by the invention has the characteristics of strong hydrophobic capacity and oil pollutant-resistant capacity, fire prevention, water prevention, acid-base resistance, pollution resistance, no toxicity, no odor, high adhesion power, color permanence, easiness and convenience for construction, easiness for drying, time saving, energy conservation, environmental friendliness and the like, can be used for effectively preventing the erosion of an external harsh environment on a building and prolonging the life of the building and has good adhesive power and freeze thawing resistant property, thereby being suitable for being used for various regions.

Description

technical field [0001] The invention relates to the field of architectural coatings, in particular to a self-cleaning genuine stone paint and a preparation method thereof. Background technique [0002] In recent years, with the development of industry, the density of urban population, and the rapid growth of coal and petroleum fuels, the urban air quality is deteriorating day by day, seriously affecting the air environment and endangering the health of residents. The dust particles in the air are increasing rapidly, polluting the surface of buildings and seriously affecting the city environment. [0003] Dust particles in the air are mostly metal particles, organic chemical components, inorganic salts and other substances. The surface of urban buildings absorbs a large amount of dust every day, which increases the acid-base corrosion of dust over time. Once the urban air drops, it will It means that these substances will be doubled in the air, which will intensify the damag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B26/10
Inventor 祁守岗李平高学清王晶晶朱曼莉
Owner NANJING FORTUNE RECYCLING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com