An environment-friendly aluminum alloy rapid electroless nickel-phosphorus additive

A technology for electroless nickel plating and phosphorus additive, which is applied in the field of environmental-friendly aluminum alloy rapid electroless nickel-phosphorus plating and its preparation, and can solve the problem that the stability of nickel-phosphorus deposition rate has not reached an efficient balance, the plating period is long, and it is easy to fall off. and other problems, to achieve the effect of stabilizing the deposition rate of electroless nickel-phosphorus plating, protecting the environment and promoting human health, and achieving a dense and uniform coating.

Active Publication Date: 2015-08-05
哈尔滨三泳金属表面技术有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the problem of domestic electroless nickel-phosphorus plating is that the efficiency is not high, and the nickel-phosphorus deposition rate and the stability of the plating solution have not reached a high-efficiency balance. After 10 minutes, the plating speed drops sharply, the average plating speed is slow, the coating is not well bonded, it is easy to fall off, the plating solution is unstable, and it is prone to self-catalyzed decomposition during high-temperature chemical nickel-phosphorus plating. Some of the plating solutions are stable, but nickel -Phosphorus deposition rate is too slow, a plating cycle is too long, the efficiency is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An environment-friendly aluminum alloy rapid electroless nickel-phosphorus additive
  • An environment-friendly aluminum alloy rapid electroless nickel-phosphorus additive
  • An environment-friendly aluminum alloy rapid electroless nickel-phosphorus additive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Additive ingredients: A component is 30mg / L yttrium oxide, 30mg / L ytterbium oxide, 300mg / L sodium tetraborate, 40ml / L 1:1 dilute sulfuric acid; B component is 4g / L DL-malic acid, 4g / L aminopropionic acid, 4g / L methylene succinic acid, 2g / L ethylenediamine, 40g / L lactic acid; C component is 2mg / L copper sulfate, 2mg / L antimony potassium tartrate, 2mg / L molybdic acid Ammonium, 6mg / L allyl iodide; D component is 2mg / L bis-benzenesulfonimide (BBI), 2mg / L N, N-diethylpropynylamine (DEP), 2mg / L vinyl Sodium sulfonate (VS), 2mg / L sodium allyl sulfonate (SAS).

[0020] When configuring the above-mentioned additives, the four groups A, B, C, and D are firstly prepared into a 0.5-300g / L concentrated solution, and then the amount of each component is calculated according to the volume of the concentrated solution. In the first group, place weighed yttrium oxide, ytterbium oxide, and 1:1 dilute sulfuric acid in the container in sequence, heat and stir until dissolved, then add so...

Embodiment 2

[0027]Additive ingredients: A component is 40mg / L yttrium oxide, 20mg / L ytterbium oxide, 400mg / L sodium tetraborate, 35ml / L 1:1 dilute sulfuric acid; B component is 3g / L DL-malic acid, 2g / L aminopropionic acid, 3g / L methylene succinic acid, 1.5g / L ethylenediamine, 30g / L lactic acid; C component is 1mg / L copper sulfate, 1mg / L antimony potassium tartrate, 3mg / L molybdenum Ammonium acid, 5mg / L allyl iodide; D component is 3mg / L bis-benzenesulfonimide (BBI), 1mg / L N, N-diethylpropynylamine (DEP), 2mg / L ethylene Sodium sulfonate (VS), 3mg / L sodium allyl sulfonate (SAS).

[0028] When configuring the above-mentioned additives, the four groups A, B, C, and D are firstly prepared into a 0.5-300g / L concentrated solution, and then the amount of each component is calculated according to the volume of the concentrated solution. In the first group, place weighed yttrium oxide, ytterbium oxide, and 1:1 dilute sulfuric acid in the container in sequence, heat and stir until dissolved, then ...

Embodiment 3

[0035] Additive ingredients: A component is 20mg / L yttrium oxide, 40mg / L ytterbium oxide, 500mg / L sodium tetraborate, 30ml / L 1:1 dilute sulfuric acid; B component is 5g / L DL-malic acid, 3g / L aminopropionic acid, 5g / L methylene succinic acid, 0.5g / L ethylenediamine, 50g / L lactic acid; C component is 3mg / L copper sulfate, 0.5mg / L antimony potassium tartrate, 4mg / L Ammonium molybdate, 5.5mg / L allyl iodide; D component is 1mg / L bis-benzenesulfonimide (BBI), 3mg / L N, N-diethylpropynylamine (DEP), 3mg / L L sodium vinyl sulfonate (VS), 1mg / L sodium allyl sulfonate (SAS).

[0036] When configuring the above-mentioned additives, the four groups A, B, C, and D are firstly prepared into a 0.5-300g / L concentrated solution, and then the amount of each component is calculated according to the volume of the concentrated solution. The first group will place the weighed yttrium oxide, ytterbium oxide, and 1:1 dilute sulfuric acid in the container in sequence, heat and stir until dissolved, th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
hardnessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an environment-friendly aluminum alloy fast electroless nickel-phosphorus additive, which is composed of four components A, B, C and D, component A: 20-60mg / L yttrium oxide, 20-60mg / L ytterbium oxide, 100-500mg / L sodium tetraborate, 20-40ml / L 1:1 dilute sulfuric acid and the remaining water; B component: complexing agent and the remaining water; C component: 1-4mg / L copper sulfate, 0.5-2mg / L antimony potassium tartrate, 1-5mg / L ammonium molybdate, 4-10mg / L allyl iodide and the water of the remainder; D component: intermediate and the water of the remainder, the additive of the present invention makes Nickel-phosphorus rapid and stable deposition, the coating thickness reaches 5.6-6.0μm within 10 minutes of plating, the thickness can reach 24.3-25.0μm after continuous plating for 1 hour, the average plating speed exceeds 24.3μm / h, the coating is amorphous, uniform and dense , high hardness, excellent corrosion resistance.

Description

technical field [0001] The invention relates to an environment-friendly aluminum alloy rapid chemical plating nickel-phosphorus additive and a preparation method thereof. Background technique [0002] In recent years, with the rapid rise of my country's electronics industry, automobile manufacturing industry, and aerospace industry, aluminum alloys have been widely used due to their advantages such as high specific strength, good processing performance, and low manufacturing cost, such as internal and external support plates for computers, mobile phone plug-ins, Aircraft wings, spars, skins, etc. In these service environments, aluminum alloys are required to have good corrosion resistance, wear resistance, and welding performance, and surface treatment is required to obtain a certain thickness of nickel-phosphorus alloy coating on the surface of the workpiece. As an emerging surface treatment technology, electroless nickel-phosphorus plating is widely used in the above-menti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C18/32
Inventor 董欢欢米艳丽崔永利王丽雪
Owner 哈尔滨三泳金属表面技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com