400 series stainless steel hot-rolled annealed wire rod mixed acid pickling solution and pickling method

A technology of stainless steel and pickling solution, which is applied in the field of stainless steel surface treatment, and can solve problems such as difficult pickling

Active Publication Date: 2017-11-14
XINGTAI IRON & STEEL
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the above-mentioned technical problems, for annealing materials, especially the problem that it is not easy to be pickled during high-temperature annealing, the present invention proposes a mixed acid pickling solution and a pickling method for 400 series stainless steel hot-rolled annealing wire rods. After washing, the surface is white and beautiful, and there is no phenomenon of over-pickling or under-pickling

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 400 series stainless steel hot-rolled annealed wire rod mixed acid pickling solution and pickling method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Annealing and pickling process of 0Cr13

[0022] The main components of 0Cr13: C content <0.05%, Cr content 13%, Si content 0.5%. The specification of the wire is 5.5mm-42mm, and the annealing temperature is 700-800°C.

[0023] The pickling solution is composed of hydrochloric acid, hydrofluoric acid, corrosion inhibitor, acid mist inhibitor and water; the mass ratio of each substance is as follows: hydrochloric acid 22wt%, hydrofluoric acid 0.1wt%, corrosion inhibitor 1wt%, acid mist inhibitor added The amount is 0.5wt%, and the balance is water; the corrosion inhibitor is an equal mass mixture of urotropine, quaternary ammonium salt, and sodium nitrite; the acid mist inhibitor is sodium dodecylsulfonate.

[0024] Pickling process: inject the pickling solution into the pickling tank, put the entire annealed hot-rolled wire rod directly into the pickling tank for pickling, the pickling temperature is 85°C, the pickling time is 30 minutes, rinse and wash after pickling ...

Embodiment 2

[0027] Annealing and pickling process of 1Cr13

[0028] The main component of 1Cr13, C content <0.15%, Cr content 13%, Si content 0.5%. The specification of the wire is 5.5mm-42mm, and the high temperature annealing temperature is 860-920℃.

[0029] The pickling liquid is composed of hydrochloric acid, hydrofluoric acid, corrosion inhibitor, acid mist inhibitor and water; The additive amount is 0.1wt%, and the balance is water; the corrosion inhibitor is an equal mass mixture of urotropine, thiourea and sodium benzoate; the acid mist inhibitor is sodium dodecylsulfonate, benzenesulfonate, Equal mass mixture of fatty alcohol polyoxyethylene ether.

[0030] Pickling process: inject the pickling liquid into the pickling tank, put the whole annealed hot-rolled wire rod directly into the pickling tank for pickling, the pickling temperature is 70°C, the pickling time is 40min, rinse and wash after pickling Neutralize and store after drying.

[0031] The surface of 1Cr13 pickled ...

Embodiment 3

[0033] Annealing and pickling process of 0Cr17

[0034] The main component of 0Cr17, C content <0.05%, Cr content 17%, Si content 0.5%. The specification of the wire is 5.5mm-42mm, and the annealing temperature is 780-820°C.

[0035] The pickling liquid is composed of hydrochloric acid, hydrofluoric acid, corrosion inhibitor, acid mist inhibitor and water; The addition amount of the inhibitor is 0.25wt%, and the balance is water; the corrosion inhibitor is an equal mass mixture of thiourea, sodium benzoate and citric acid; the acid mist inhibitor is sodium dodecylsulfonate, fatty alcohol polyoxyethylene ether equal mass mixture.

[0036] Pickling process: inject the pickling solution into the pickling tank, put the entire annealed hot-rolled wire rod directly into the pickling tank for pickling, the pickling temperature is 65°C, the pickling time is 30 minutes, rinse and wash after pickling Neutralize and store after drying.

[0037] The surface of 0Cr17 pickled according ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a 400 series stainless steel hot-rolled annealing wire rod mixed acid pickling solution and a pickling method. The pickling solution is composed of hydrochloric acid, hydrofluoric acid, corrosion inhibitor, acid mist inhibitor and water; the mass ratio of each substance is as follows: hydrochloric acid 8-22wt%, hydrofluoric acid 0.1-2wt%, corrosion inhibitor 0.01-1wt %, the amount of acid mist inhibitor added is 0.1‑0.5wt%, and the balance is water. The pickling method is to inject the pickling liquid into the pickling tank, and put the whole annealed hot-rolled wire rod directly into the pickling tank for pickling. The pickling temperature is 45-85°C and the pickling time is 10-40min. The surface of the wire rod treated by the invention is bright and clean, without iron oxide residue, and can be used and stored normally without subsequent passivation.

Description

technical field [0001] The invention belongs to the technical field of stainless steel surface treatment, and in particular relates to a mixed-acid pickling solution and a pickling method for 400 series stainless steel hot-rolled annealed wire rods. Background technique [0002] 400 series wire rod refers to the wire rod with a C content of 0.001-0.4%, a Cr content of 12-18.5%, a manganese content of about 0.5%, a silicon content of 0.5-2%, and the sum of other elements below 1%. It is equivalent to 0Cr13, 0Cr17, 1Cr13, 1Cr17 and other steel types in the national standard. This type of steel does not contain or contain a small amount of nickel. After annealing, the surface oxide scale is very dense, and the conventional pickling method cannot effectively remove the oxide scale. It is very easy to over-pickling when using nitric acid and hydrofluoric acid pickling methods such as 304 steel grades, leaving pitting holes on the surface. Therefore, the pickling of the annealed ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23G1/08C23G1/06
Inventor 王宁涛翟进坡王郢田新中张治广冯忠贤陈继林贾育华王笑丹李军孙增淼赵虎张建周
Owner XINGTAI IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com