Anti-static ceramic tile and production method thereof

A ceramic tile, anti-static technology, applied in the field of ceramic materials, can solve the problems of unable to meet market demand, poor anti-static performance, limited use range, etc., to achieve high anti-static function, good corrosion resistance, good wear resistance Effect

Inactive Publication Date: 2015-08-26
安徽省亚欧陶瓷有限责任公司
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The ceramic tiles currently on the market have the disadvantage of poor antistatic performance, which limits their scope of use and cannot meet market demand.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] An antistatic ceramic tile made of the following raw materials in weight (kg): river sand 36, lithium china stone 27, dickite 23, pebble chips 20, steel slag 18, composite clay 18, colloidal graphite powder 12, disilicide Molybdenum 10, tin oxide antimony 4.5, liquid phenolic resin 6, sodium lauryl sulfate 2.5, chitosan 3.5;

[0021] The preparation method of described composite clay is as follows:

[0022] a. Take Suzhou soil, attapulgite soil and mountain mud according to the mass ratio of 4:3:1, mix them evenly, pulverize them, pass through a 150 mesh sieve, add water and stir to make a slurry with a concentration of 55%, and then add 4 % sodium methylene dinaphthalene sulfonate, 3% Turkish red oil, 1.5% sodium hyaluronate, heated in a water bath to 55°C, 2500r / min high-speed grinding for 25min, suction filtration, drying, and stand-by;

[0023] b. Weigh aramid pulp, corn stalks and bagasse according to the mass ratio of 2:1:1, mix evenly, pulverize, pass through a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-static ceramic tile and a production method thereof. The anti-static ceramic tile is formed by the following raw materials of, by weight, 27 to 41 parts of river sand, 19 to 33 parts of lithium China stone, 16 to 28 parts of dickite, 15 to 25 parts of pebble chips, 12 to 24 parts of steel slags, 14 to 22 parts of composite clay, 10 to 15 parts of colloidal graphite powder, 8 to 14 parts of molybdenum disilicide, 3 to 6 parts of tin antimony oxide, 5 to 7 parts of liquid phenolic resin, 2 to 3 parts of sodium lauryl sulfate and 3 to 4 parts of chitosan. According to the anti-static ceramic tile and the production method thereof, the colloidal graphite powder, the molybdenum disilicide, the tin antimony oxide and the other components are added and accordingly the high anti-static function is achieved through the produced ceramic tile, the national anti-static ceramic tile standard GB26539-2011 requirements for the anti-static property are met, the strength is high, the heat stability is good, the abrasion resistance is good, the corrosion resistance is good, the service life of the anti-static ceramic tile is extended, and the use range of the anti-static ceramic tile is expanded.

Description

technical field [0001] The invention relates to an antistatic ceramic tile and a preparation method thereof, belonging to the field of ceramic materials. Background technique [0002] Ceramic brick is a kind of acid and alkali resistant porcelain or stone building or decorative material formed by grinding, mixing, pressing, glazing, sintering and other processes with refractory metal oxides and semi-metal oxides. , and its raw materials are mostly mixed with clay, quartz sand and other inorganic non-metallic materials. In recent years, with the rapid development of my country's building ceramics industry, people have higher and higher performance requirements for ceramic tiles. The ceramic tiles currently on the market have the disadvantage of poor antistatic performance, which limits their scope of use and cannot meet market demand. Contents of the invention [0003] The object of the present invention is to provide an antistatic ceramic tile with good antistatic perfor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/14C04B35/622
Inventor 徐安辉孔德泽郑辉
Owner 安徽省亚欧陶瓷有限责任公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com