A kind of inner and outer glaze applied to Linglong porcelain

An internal and external, feldspar technology, applied in the field of ceramic products, can solve the problems of not being high-grade enough, low whiteness, inability to adapt to free and unrestrained beauty, etc., and achieve the effect of high-grade grade and high whiteness of appearance

Inactive Publication Date: 2017-05-24
JINGDEZHEN YAXING SPECIAL CERAMICS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The traditional artistic features of exquisite and exquisite, quiet and elegant, exquisite and delicate, simple and generous give people a fresh and lively feeling, but their exquisite eyes are small, so they can only be arranged and combined into various patterns with the exquisite eyes. The free and unrestrained beauty pursued by modern people
[0005] Traditionally used on the inner and outer glazes of Linglong porcelain, the appearance is white and blue, the whiteness is not high, and the grade displayed is not high enough to meet the aesthetic requirements of modern people.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Embodiment 1: a kind of inner and outer glaze applied to Linglong porcelain, including feldspar, quartz, talcum powder, calcite, talc, zinc oxide, is characterized in that: the weight percent of described flaky Linglong glaze is composed of:

[0019] Feldspar 54%, quartz 28%, talc powder 10%, calcite 2%, talc 3%, zinc oxide 3%; the sum of the weight percentages of each component is 100%.

[0020] After mixing the above raw materials evenly, melt them at 1520°C, put them into cold water and quench them into a frit, put the frit into a ball mill, add water, high alumina ball stone and 5% kaolin to grind it into a glaze slurry, and the fineness is controlled at 10,000 The remaining 2% of the hole sieve is then dried at 80-100°C and made into granules and passed through a 250-mesh sieve. The granules are mixed according to the glaze moisture content of 10-15% and can be used.

Embodiment 2

[0021] Embodiment 2: a kind of inner and outer glaze applied to Linglong porcelain, including feldspar, quartz, talcum powder, calcite, talcum, zinc oxide, and the weight percentage of described flaky Linglong glaze is composed of:

[0022] Feldspar 51%, quartz 24%, talc powder 12%, calcite 5%, talc 5%, zinc oxide 3%; the sum of the weight percentages of each component is 100%.

[0023] After mixing the above raw materials evenly, melt them at 1520°C, put them into cold water and quench them into a frit, put the frit into a ball mill, add water, high alumina ball stone and 5% kaolin to grind it into a glaze slurry, and the fineness is controlled at 10,000 The remaining 2% of the hole sieve is then dried at 80-100°C and made into granules and passed through a 250-mesh sieve. The granules are mixed according to the glaze moisture content of 10-15% and can be used.

Embodiment 3

[0024] Embodiment 3: a kind of inner and outer glaze applied to Linglong porcelain, including feldspar, quartz, talcum powder, calcite, talcum, zinc oxide, and the weight percentage of described flaky Linglong glaze is composed of:

[0025] Feldspar 52%, quartz 24%, talc powder 14%, calcite 4%, talc 4%, zinc oxide 2%; the sum of the weight percentages of each component is 100%.

[0026] After mixing the above raw materials evenly, melt them at 1520°C, put them into cold water and quench them into a frit, put the frit into a ball mill, add water, high alumina ball stone and 5% kaolin to grind it into a glaze slurry, and the fineness is controlled at 10,000 The remaining 2% of the hole sieve is then dried at 80-100°C and made into powder and passed through a 250-mesh sieve. The prepared powder is mixed according to the moisture content of the glaze of 10-15% and can be used evenly.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an internal and external surface glaze applied to rice-pattern decorated porcelain. The internal and external surface glaze comprises the following components in percentage by weight: 50-54% of feldspar,20-30% of quartz, 10-20% of talcum powder,2-6% of calcite,3-5% of kaolinite and 1-3% of zinc oxide, totaling 100%. Due to use of the internal and external surface glaze, the rice-pattern decorated porcelain is relatively high in appearance whiteness, looksveryhigh-grade and well caters to the aesthetical standard of modern people.

Description

technical field [0001] The invention relates to the technical field of ceramic products, in particular to an inner and outer glaze applied to Linglong porcelain. Background technique [0002] Jingdezhen Linglong Porcelain is a treasure in the Han porcelain making process. It was created and developed on the basis of the hollowing process during the Yongle period of the Ming Dynasty. It has a history of more than 500 years. Using the engraving technique, a number of exquisite eyes of a certain shape are first carved out on the porcelain body, and the eyes are filled with a special exquisite glaze, and then painted with blue and white, glazed and fired at high temperature. It is the product of skillful blending of blue and white and Linglong in terms of craftsmanship and artistic treatment. The green and transparent Linglong and the elegant green blue and white set off each other. There are glazes, there are flowers in the flowers, and the combination is seamless, showing the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/86
Inventor 程鹏
Owner JINGDEZHEN YAXING SPECIAL CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com