Liquid butyl rubber asphalt waterproof coating and preparation method

A liquid butyl rubber, asphalt waterproof coating technology, applied in the direction of asphalt coating, coating, application, etc., can solve the problems of limited service life, easy curing, easy crystallization, etc., to achieve the effect of improving the service life and maintaining the original performance

Inactive Publication Date: 2015-10-14
北京世纪洪雨科技有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The waterproof materials in the prior art include modified asphalt waterproof coatings. The use of various polymer modified asphalt can greatly improve the performance of asphalt substrates, but its disadvantages are also obvious: it is easy to crystallize at low temperatures, and if it is placed for a long time after construction It is easy to cure, so the original performance of the waterproof material cannot be maintained, which greatly limits the service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A kind of liquid butyl rubber asphalt waterproof coating, the number of formula parts comprises:

[0013] 42 parts of asphalt, 13 parts of liquid butyl rubber, 9.4 parts of SBS, 8.6 parts of reclaimed rubber powder,

[0014] 9.4 parts of polybutene, 20.9 parts of naphthenic oil, 11.7 parts of petroleum resin.

[0015] The preparation method of the liquid butyl rubber asphalt waterproof coating comprises: first, heating the bitumen of formula weight to 130-180 DEG C; then, adding modifier, polybutene and tackifier of formula weight, and heating Stir at ℃ for 1-2 hours; finally, cool down to 160℃, and add reclaimed rubber powder according to the formula weight, stir for 1-1.5 hours until it is uniform and free of particles, and then discharged until it is in a molten state.

Embodiment 2

[0017] A kind of liquid butyl rubber asphalt waterproof coating, the number of formula parts comprises:

[0018] 32 parts of asphalt, 14 parts of liquid butyl rubber, 9 parts of SBS, 10 parts of reclaimed rubber powder,

[0019] 9 parts of polybutene, 22 parts of naphthenic oil, 12 parts of petroleum resin.

[0020] The preparation method of the liquid butyl rubber asphalt waterproof coating comprises: first, heating the bitumen of formula weight to 130-180 DEG C; then, adding modifier, polybutene and tackifier of formula weight, and heating Stir at ℃ for 1-2 hours; finally, cool down to 160℃, and add reclaimed rubber powder according to the formula weight, stir for 1-1.5 hours until it is uniform and free of particles, and then discharged until it is in a molten state.

Embodiment 3

[0022] A kind of liquid butyl rubber asphalt waterproof coating, the number of formula parts comprises:

[0023] 48 parts of asphalt, 11 parts of liquid butyl rubber, 8.1 parts of SBS, 9 parts of reclaimed rubber powder,

[0024] 9.8 parts of polybutene, 25 parts of naphthenic oil, 10.9 parts of petroleum resin.

[0025] The preparation method of the liquid butyl rubber asphalt waterproof coating comprises: first, heating the bitumen of formula weight to 130-180 DEG C; then, adding modifier, polybutene and tackifier of formula weight, and heating Stir at ℃ for 1-2 hours; finally, cool down to 160℃, and add reclaimed rubber powder according to the formula weight, stir for 1-1.5 hours until it is uniform and free of particles, and then discharged until it is in a molten state.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses liquid butyl rubber asphalt waterproof coating and a preparation method. According to the invention, a used additive has long chain and low molecular weight, can ensure that the asphalt can be mutually mixed and dissolved with various high polymer materials in the production process, so that steady combination is formed, respective characteristics take effect under the most steady state in the application process, and thus the asphalt never can be cured. The preparation method of the waterproof coating disclosed by the invention comprises the following steps of heating the asphalt in formula weight to 130-180 DEG C, then, adding liquid butyl rubber, SBS, naphthenic oil and petroleum resin into the asphalt in formula weight, stirring at 175-180 DEG C for 1-2h, finally, decreasing the temperature to 160 DEG C, adding reclaimed rubber in formula weight, stirring for 1-1.5h till the mixture is uniform and does not contain particles, and discharging after the mixture is molten. The waterproof coating disclosed by the invention has the advantages that the waterproof coating is difficult to crystallize at low temperature; the waterproof coating cannot be cured even though placed for a long time after construction; the original property of the waterproof material is kept; and furthermore, the service life of the waterproof coating is greatly increased.

Description

technical field [0001] The invention relates to a liquid butyl rubber asphalt waterproof coating and a preparation method thereof. Background technique [0002] The waterproof materials in the prior art include modified asphalt waterproof coatings. The use of various polymer modified asphalt can greatly improve the performance of asphalt substrates, but its disadvantages are also obvious: it is easy to crystallize at low temperatures, and if it is placed for a long time after construction It is easy to cure, so the original performance of the waterproof material cannot be maintained, which greatly limits the service life. Contents of the invention [0003] In view of this, the main purpose of the present invention is to provide a kind of liquid butyl rubber asphalt waterproof coating and its preparation method, the additive used in it is long chain, low molecular weight, can make asphalt and various macromolecular materials intermix in the production process , miscible, f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D123/22C09D11/08
Inventor 潘冰
Owner 北京世纪洪雨科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap