Binary metal organic framework material applied to super capacitor and preparation method for binary metal organic framework material

A technology of supercapacitors and binary metals, applied in the manufacture of hybrid/electric double layer capacitors, hybrid capacitor electrodes, hybrid capacitor collectors, etc., can solve the problems of poor specific capacity cycle stability and low specific capacity cycle stability, etc. Achieve the effect of large specific surface area

Inactive Publication Date: 2015-10-21
CHINA UNIV OF GEOSCIENCES (WUHAN)
View PDF3 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, MOFs are widely used as adsorption materials, catalytic materials, magnetic materials, optical materials and energy storage materials, especially the application of MOFs in the field of energy storage has attracted the attention of many scholars, and in recent years more and more MOFs materials are applied to lithium-ion batteries and supercapacitor electrode materials (Journal of Solid State Chemistry 223 (2015) 109–121), we found that the MOFs direc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Binary metal organic framework material applied to super capacitor and preparation method for binary metal organic framework material
  • Binary metal organic framework material applied to super capacitor and preparation method for binary metal organic framework material
  • Binary metal organic framework material applied to super capacitor and preparation method for binary metal organic framework material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A stable binary metal-organic framework electrode material, which is composed of binary metal ions and organic ligands through self-assembly, the binary metal is Co-Ni, and the organic ligand is trimesic acid, The molar ratio of Co: Ni: trimesic acid is 2:8:5.

[0026] The preparation method of the above-mentioned binary metal-organic framework electrode material, the specific steps are as follows: Weigh 0.006mol Co(NO 3 ) 2 ·6H 2 O, 0.004mol Ni(NO 3 ) 2 ·6H 2 O and 0.005mol trimesic acid, with 65mL mixed solvent (N, N-dimethylformamide (DMF): ethanol (C 2 h 5 OH): distilled water (H 2 (0)=1:1:1) dissolved, stirred at room temperature with a magnetic stirrer until evenly mixed; poured the mixed solution into a polytetrafluoroethylene-lined hydrothermal reaction kettle, and kept it at a constant temperature of 100°C for 30h , the reaction system was slowly cooled to room temperature, and the resulting mixed solution was poured out from the reactor for suction fil...

Embodiment 2

[0029] A binary metal-organic framework material applied to supercapacitors, which is composed of two metal ions and organic ligands through self-assembly, the two metal ions are Co-Ni, and the organic ligand is trimesene Formic acid, the molar ratio of Co:Ni:trimesic acid is 6:4:5.

[0030] The preparation method of the above-mentioned binary metal-organic framework material, the specific steps are as follows: Weigh 0.006mol Co(NO 3 ) 2 ·6H 2 O, 0.004mol Ni(NO 3 ) 2 ·6H 2 O and 0.005mol trimesic acid, with 65mL mixed solvent (N, N-dimethylformamide (DMF): ethanol (C 2 h 5 OH): distilled water (H 2 (2)=1:1:1) dissolves, stirs to mix with magnetic stirrer at room temperature; The solution that mixes is poured in the hydrothermal reactor of polytetrafluoroethylene liner, after putting into baking oven, with 5 ℃min -1 The heating rate was increased to 85°C and kept at a constant temperature for 20h, the reaction system was slowly cooled to room temperature, the resulting...

Embodiment 3

[0033] A stable binary metal-organic framework electrode material, which is composed of binary metal ions and organic ligands through self-assembly, the binary metal is Co-Ni, and the organic ligand is trimesic acid, The molar ratio of Co: Ni: trimesic acid is 8:2:5.

[0034] The preparation method of the above-mentioned binary metal-organic framework electrode material, the specific steps are as follows: Weigh 0.006mol Co(NO 3 ) 2 ·6H 2 O, 0.004mol Ni(NO 3 ) 2 ·6H 2 O and 0.005mol trimesic acid, with 65mL mixed solvent (N, N-dimethylformamide (DMF): ethanol (C 2 h 5 OH): distilled water (H 2 (0)=1:1:1) dissolved, stirred at room temperature with a magnetic stirrer until uniformly mixed; poured the mixed solution into a polytetrafluoroethylene-lined hydrothermal reaction kettle, and kept it at a constant temperature of 120°C for 40h , the reaction system was slowly cooled to room temperature, and the resulting mixed solution was poured out from the reactor for suction ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Maximum discharge specific capacityaaaaaaaaaa
Specific capacityaaaaaaaaaa
Maximum discharge specific capacityaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of super capacitors and particularly relates to a binary metal organic framework material applied to a super capacitor and a preparation method for the binary metal organic framework material. The binary metal organic framework material is formed of two types of metal ions and an organic ligand using a solvothermal method in a self assembly coordination manner. The two types of metal ions are Co-Ni, Co-Fe, Co-Mn, Ni-Mn or Ni-Cu. The organic ligand is trimesic acid, terephthalic acid, 2,6-naphthalene acid, 4,4'-biphenyl diacid or 2-methylimidazole. The binary metal organic framework material is advantaged by having multiple holes, large specific surface area and an adjustable structure, and being varied in structure. The cooperative effect between the two types of metal ions in the binary metal organic framework material (MOFs) is utilized, so that when the binary metal organic framework material is applied to the electrode material of a super capacitor, excellent cycling stability and high specific discharge capacity are achieved.

Description

technical field [0001] The invention belongs to the field of supercapacitors, and in particular relates to a binary metal-organic framework material applied to supercapacitors and a preparation method thereof. Background technique [0002] A supercapacitor is a new type of energy storage element whose performance is between that of a traditional capacitor and a battery. It has both the high energy density of a battery and the high power density of a traditional capacitor. Supercapacitor has the advantages of simple principle and structure, safety and reliability, wide application range, high power density, short charging time, long service life, energy saving and environmental protection, etc. Its excellent pulse discharge performance and large-capacity energy storage performance make it promising It plays an extremely important role in many fields such as mobile communications, electric vehicles and aerospace, and has broad application prospects. At present, the specific c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01G11/70H01G11/84
CPCY02E60/13H01G11/24H01G11/26H01G11/30H01G11/48H01G11/86
Inventor 周成冈闫允璠周吟韩波冀转吴金平
Owner CHINA UNIV OF GEOSCIENCES (WUHAN)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap