Fiber cement pile material composition and preparation method of fiber cement pile

A technology of fiber cement and composition, which is applied in the field of preparation of fiber cement pile material composition and fiber cement pile, which can solve the problems of increasing the cost of use, easy loosening of cement piles, and inconvenience for driving vehicles and pedestrians

Inactive Publication Date: 2015-12-23
ANHUI WUHU FLY QI CEMENT PROD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above-mentioned prior art, the purpose of the present invention is to overcome the fact that the cement piles in the prior art are easy to loosen after long-term use and are scattered on the road surface, thereby causing inconvenience to driving vehicles and pedestrians, and at the same time require more manpower to maintain it. The problem of greatly increasing the cost of use, thereby providing a fiber cement pile material composition and a preparation method for fiber cement piles that can effectively improve the coagulation force of cement piles, greatly increase its service life, and reduce use costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0018] The present invention also provides a method for preparing fiber cement piles, wherein the preparation method includes: mixing cement, straw, plant ash, fly ash, water, quartz sand and zinc oxide into a mold to obtain fiber cement pile; among them,

[0019] Relative to 100 parts by weight of the cement, the amount of straw is 30-70 parts by weight, the amount of plant ash is 10-30 parts by weight, and the amount of fly ash is 10-50 parts by weight. The amount of water is 50-100 parts by weight, the amount of the quartz sand is 10-30 parts by weight, and the amount of zinc oxide is 1-10 parts by weight.

[0020] Similarly, in order to make the prepared cement pile have better coagulation force in actual use, to further reduce its loosening probability and improve its service life, in a preferred embodiment of the present invention, relative to 100 parts by weight The cement, the consumption of the straw is 40-60 parts by weight, the consumption of the plant ash is 15-25...

Embodiment 1

[0026] Cut the straw into straw sections with a length of about 3cm; mix 100g of cement, 40g of straw sections, 15g of plant ash, 20g of fly ash, 70g of water, 15g of quartz sand, 3g of zinc oxide and 1g of water reducing agent into the mold. Fiber cement pile A1 was prepared.

Embodiment 2

[0028] Cut the straw into straw sections with a length of about 3cm; mix 100g of cement, 60g of straw sections, 25g of plant ash, 40g of fly ash, 80g of water, 25g of quartz sand, 7g of zinc oxide and 10g of water reducing agent into the mold. A fiber cement pile A2 was prepared.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fiber cement pile material composition and a preparation method of a fiber cement pile. The composition also comprises the following components in parts by weight: 100 parts by weight of cement, 30-70 parts of straws, 10-30 parts of plant ash, 10-50 parts of coal ash, 50-100 parts of water, 10-30 parts of quartz sand and 1-10 parts of zinc oxide. According to the technical scheme, the prepared fiber cement pile has the advantages that the coagulability is greatly improved and the problem that the prepared cement pile easily looses after being used for a long term is greatly avoided on the premise that the favorable service character is ensured.

Description

technical field [0001] The invention relates to the field of production and preparation of cement piles, in particular to a fiber cement pile material composition and a preparation method for fiber cement piles. Background technique [0002] As a common roadblock facility, cement piles are widely used in real life. However, in actual use, many cement piles are prone to loose materials after long-term use, resulting in poor coagulation of cement piles. This will greatly affect the service life of the cement piles, and further affect the safety of the road surface, because the loose cement piles may be scattered on the road surface, which will cause inconvenience to driving vehicles and pedestrians, and also require more manpower to maintain it , greatly increasing the cost of use. [0003] Therefore, it is an urgent problem to be solved in the present invention to provide a fiber cement pile material composition and a fiber cement pile preparation method that can effectively...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00
Inventor 朱琪
Owner ANHUI WUHU FLY QI CEMENT PROD