Preparation method of antibacterial nanofiber membrane

A nanofiber membrane and nanoparticle technology is applied in the processing of textile materials, continuous processing of textile materials, textiles and papermaking, etc. Good uniformity, overcoming poor mechanical properties and simple operation

Active Publication Date: 2018-01-23
上海展恒环保科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to enhance the antibacterial properties of existing nanofiber membranes, overcome the shortcomings of poor mechanical properties of nanofibers, poor resistance to rubbing and poor anti-pollution performance, and disclose a preparation method of antibacterial nanofiber membranes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] The preparation method of a kind of antibacterial nanofiber membrane of the present invention comprises the preparation of nanofiber membrane, the preparation of bactericide solution and the modification nanofiber membrane of bactericide solution, and described antibacterial nanofiber membrane is to soak nanofiber membrane in the bactericide of different concentration The nanofibrous membrane is formed in an organic monomer or organic monomer and inorganic fungicide solution through polymerization reaction, or is directly soaked in a polymer solution or a polymer and inorganic mixed solution of a fungicide solution Film-forming, described preparation method comprises the following steps:

[0016] A. Step (1) Prepare fungicide solution:

[0017] (a) Dissolving or dispersing 0.1-20 parts by weight of fungicide powder or fungicide solution in water, controlling the temperature at 20-50°C, and stirring for 1-3 hours;

[0018] (b) Add antibacterial nanoparticles or saline s...

Embodiment 1

[0031] A preparation method of dopamine@polyacrylonitrile nanofiber membrane, comprising the following steps:

[0032] A. Step (1) Preparation of dopamine solution:

[0033] (a) Dissolve 0.394g of Tris in 250g of water, then add 5g of silver nanoparticles, and then disperse with ultrasonic vibration for 30 minutes;

[0034] (b) Add 0.5g of dopamine to the solution, adjust the pH to 8.5, and stir evenly;

[0035] B. Step (2) Preparation of polyacrylonitrile electrospinning solution and preparation of polyacrylonitrile nanofiber membrane:

[0036] (a) Dissolving polyacrylonitrile in N,N-dimethylformamide solvent under the action of a magnetic stirrer, stirring for 10 to 24 hours until a uniform and clear polyacrylonitrile spinning solution appears;

[0037] (b) The configured polyacrylonitrile spinning solution is loaded into the spinneret, and spun on the non-woven fabric substrate at a humidity of 20-50% and a temperature of 20-50°C. The spinning process parameters are: spin...

Embodiment 2

[0044] A preparation method of zinc oxide-organosilicon quaternary ammonium salt@polyacrylonitrile nanofiber membrane, comprising the following steps:

[0045] A. Step (1) Preparation of organosilicon quaternary ammonium salt solution: disperse 5 g of zinc oxide nano-ions in 100 g of alcohol aqueous solution, then disperse by ultrasonic vibration for 30 minutes, and then add 5 g of organosilicon quaternary ammonium salt;

[0046] B. Step (2) Preparation of polyacrylonitrile electrospinning solution and preparation of polyacrylonitrile nanofiber membrane:

[0047] (a) Dissolving polyacrylonitrile in N,N-dimethylformamide solvent under the action of a magnetic stirrer, stirring for 10 to 24 hours until a uniform and clear polyacrylonitrile spinning solution appears;

[0048] (b) The configured polyacrylonitrile spinning solution is loaded into the spinneret, and spun on the non-woven fabric substrate at a humidity of 20-50% and a temperature of 20-50°C. The spinning process para...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention is a preparation method of an antibacterial nanofiber membrane, which comprises the preparation of a nanofiber membrane, the preparation of a bactericide solution, and the modification of the nanofiber membrane by a bactericide solution, and is characterized in that: the antibacterial nanofiber membrane is soaked in the nanofiber membrane Prepared in different concentrations of bactericide solutions, the nanofiber membranes are formed by polymerization in organic monomers or organic monomers and inorganic bactericide solutions, or in polymer solutions or polymer and inorganic mixed solutions Directly soaking in a fungicide solution to form a film, the preparation method includes the following steps: step (1) preparing a fungicide solution; step (2) preparing a polymer electrospinning solution and preparing a nanofiber film; step (3) preparing a fungicide solution The solution modifies the nanofiber membrane, and the obtained multi-level hole nanofiber cross-linked film with core-shell structure is the finished product of the antibacterial nanofiber membrane.

Description

technical field [0001] The invention relates to a preparation method of a fiber membrane, in particular discloses a preparation method of an antibacterial nanofiber membrane, which is applied in fields requiring antibacterial functions such as medicine, air filtration, and water treatment. Background technique [0002] Today in the 21st century, the development of science and technology has made outstanding contributions to the survival and development of human beings, but human beings have ignored the synergy between technological development and environmental issues. The natural ecological environment has been seriously damaged, and human health has been greatly threatened. The SARS in 2003, various bird flus and bacterial viruses in the later period caused human beings to face unprecedented disasters. Therefore, people began to have extremely high requirements for antibacterial in terms of food, drink, housing, transportation, antibacterial textiles, etc. [0003] Due t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04H1/4382D04H1/728D06B21/00D06B9/00
Inventor 张秀芳赵炯心朱志高柴明飞
Owner 上海展恒环保科技有限公司