Water-based wear-resistant and scratch-resistant surface treatment agent for artificial leather and synthetic leather and its preparation method

A water-based surface treatment agent and synthetic leather technology, which is applied in fiber treatment, textiles and papermaking, etc., can solve the problems that cannot meet the requirements of ecological synthetic leather, achieve good antibacterial and mildew resistance, high transparency, and improve wear resistance and scratch resistance sexual effect

Active Publication Date: 2017-06-06
SICHUAN UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the traditional solvent resin-based synthetic leather manufacturing technology is unable to meet the requirements of ecological synthetic leather

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) Pretreatment of graphene wear-resistant agent:

[0031] Wetting the graphene with propylene glycol methyl ether acetate, adding 1% isopropanol by weight of the graphene, ultrasonically dispersing for 1-2 h, and set aside;

[0032] (2) Preparation of water-based surface treatment agent:

[0033] Take 50 parts of aliphatic matting water-based polyurethane with a modulus of 50 Mpa and a solid content of 30% by weight, 40 parts of water, 0.03 parts of graphene wear-resistant agent pretreated according to (1) (solid parts), and 2.0 parts of matting powder , 0.5 parts of silicone leveling agent, 1.0 parts of aziridine crosslinking agent, 2.0 parts of silicone handle improver, 0.5 parts of water-based polyurethane thickener, mix well, react at 20-30 ℃ for 2 h, adjust the viscosity to 1000 mPa.s or so, after grinding and filtering, a water-based surface treatment agent is obtained.

[0034] The surface treatment agent uses aliphatic water-based polyurethane with a low mod...

Embodiment 2

[0036] (1) Pretreatment of graphene oxide wear-resistant agent:

[0037] Wet the graphene oxide with dimethylformamide, add KH560 with 5% by weight of graphene oxide, ultrasonically disperse for 1-2 h, and set aside;

[0038] (2) Preparation of water-based surface treatment agent:

[0039] Take 60 parts by weight of matting aromatic water-based polyurethane with a modulus of 80 Mpa and a solid content of 35%, 40 parts of water, 0.06 parts of graphene oxide wear-resistant agent pretreated by (1) (solid parts), matting powder 6 Parts, 1.0 part of silicone leveling agent, 1.5 parts of blocked water-based isocyanate crosslinking agent, 5.0 parts of hand feel improver, mixed evenly, 0.6 part of water-based polyurethane thickener, 0.4 part of water-based acrylic polymer thickener, mixed evenly, in React at 20-30 °C for 3 h, adjust the viscosity to 2000 mPa.s slurry, grind and filter to obtain a water-based surface treatment agent.

[0040] The surface treatment agent is made of ar...

Embodiment 3

[0042](1) Pretreatment of graphene and graphene oxide wear agents:

[0043] Wet the graphene with propylene glycol methyl ether acetate, add OP-10 with 1% by weight of graphene, ultrasonically disperse for 1-2 h, and set aside; wet the graphene oxide with dimethylformamide, add graphene oxide 5% by weight of KH550, ultrasonically disperse for 1-2 h, set aside;

[0044] (2) Preparation of water-based surface treatment agent:

[0045] Take 55 parts of aliphatic medium-gloss water-based polyurethane with a modulus of 60 Mpa and a solid content of 35% by weight fraction, 35 parts of water, 0.02 part of graphene oxide wear-resistant agent pretreated by (1), and 0.3 part of graphene (solid part ), 0.7 parts of silicone leveling agent, 1.2 parts of carbodiimide crosslinking agent, 3 parts of oily wax handle improver, 0.6 parts of water-based polyurethane thickener, mix well, and react at 20-30 ℃ for 2-3 h , adjust the viscosity to 1500 mPa.s slurry, grind and filter to obtain a wat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
modulusaaaaaaaaaa
Login to View More

Abstract

The invention discloses a waterborne wear-resistant and scraping-resistant surface treating agent for artificial leather and synthetic leather. The waterborne wear-resistant and scraping-resistant surface treating agent is prepared from, by weight, 50-60 parts of waterborne polyurethane, 30-40 parts of water, 0.03-0.06 part of graphene or oxidized graphene modifier, 2-6 parts of extinction powder, 0.5-1 part of organosilicone flatting agent, 1-1.5 parts of organosilicone coupling agents, 2.0-5.0 parts of hand feeling modifier and 0.5-1.0 part of waterborne thickening agent. The wear resistance, scraping resistance static electricity resistance, ageing resistance, self-cleaning performance and other performance of artificial leather and synthetic leather coatings are greatly improved through the lubricating property, high transparency, electrical conductivity, bacterium resistance, mildew resistance, UV resistance and other characteristics of graphene, and therefore the grade and international market competitiveness of artificial leather and synthetic leather are improved. In addition, traditional solvent type polyurethane is replaced by waterborne polyurethane, and therefore organic solvent resources are saved, organic pollution is eliminated from sources, potential safety hazards are eliminated, and the employment environment of workers is improved. The VOC content in finished leather is lower than 5 mg / kg (leather), and the waterborne wear-resistant and scraping-resistant surface treating agent is ecological and environmentally friendly and conforms to the requirements for ecological synthetic leather of European Union.

Description

technical field [0001] The invention relates to a method for preparing an environment-friendly surface treatment agent for artificial leather and synthetic leather, belonging to the field of fine chemical manufacturing. Background technique [0002] my country is the largest producer and consumer of synthetic leather in the world. In 2014, my country's artificial leather and synthetic leather production accounted for 76% of the world's total, and the production of artificial leather and synthetic leather by enterprises above designated size reached 3.1426 million tons, totaling 6.28 billion square meters. [0003] In the manufacturing process of artificial leather and synthetic leather, there is a very important process called surface treatment, and the materials used are called surface treatment agents (ie surface treatment agents). The surface treatment agent is generally made of polyurethane and special additives, which mainly endow artificial leather and synthetic leath...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/564D06M11/74D06N3/14
Inventor 范浩军盖静陈意颜俊郭学方汪峰
Owner SICHUAN UNIV