Weather-proof resin master batch for agricultural plastic mulching film synthesis and preparation method

An agricultural mulch film and weather-resistant technology, which is applied in the field of weather-resistant resin masterbatch for agricultural mulch film synthesis and its preparation, can solve the problems of high cost of mulch film, inability to recycle for secondary use, etc., achieve excellent heat resistance, improve water and fertilizer utilization, and reduce deep seepage effect

Active Publication Date: 2016-02-17
MINQIN COUNTY BANGDE TRADE
View PDF9 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, on the one hand, the cost of the above-mentioned mulch film is relatively high, and it cannot be recycled for secondary use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A weather-resistant resin masterbatch for agricultural mulch film synthesis, the formula is the following materials in parts by weight: 55 parts of linear low-density polyethylene powder, 20 parts of low-density polyethylene powder, 6 parts of high-density polyethylene powder, 1 part 2,6-tertiary butyl-4-methylphenol, 0.5 parts of dodecyl alcohol ester, 0.5 parts of 4-benzoyloxy-2,2,6,6-tetramethylpiperidine, 0.5 parts Hexamethylphosphoric triamide, 0.5 parts of phenyl o-hydroxybenzoate, 0.5 parts of 2,4-dihydroxybenzophenone, 5 parts of acrylic acid, 6 parts of 7.5 wt% aqueous sodium hydroxide solution, 1 part of seawater Foam powder, 1 part konjac glucomannan, 0.03 part potassium persulfate, 0.05 part aluminum chloride, 0.02 part N,N' methylenebisacrylamide, 0.2 part sodium bicarbonate, 1 part sodium carboxymethylcellulose , 1.5 parts polyethylene wax.

[0028] A method for preparing a weather-resistant resin masterbatch for agricultural mulch film synthesis, carried...

Embodiment 2

[0055] A weather-resistant resin masterbatch for agricultural mulch film synthesis, the formula is the following weight parts: 65 parts of linear low-density polyethylene powder, 15 parts of low-density polyethylene powder, 4 parts of high-density polyethylene powder, 1 part of Bis(3,5-tertiary butyl-4-hydroxyphenyl) sulfide, 0.5 parts dioctadecyl ester, 0.5 parts 2,4,6-tris(2'-butoxyphenyl)-1 , 3,5-triazine, 0.5 part of phenyl o-hydroxybenzoate, 4 parts of acrylic acid, 4 parts of 10wt% sodium hydroxide aqueous solution, 0.5 part of sepiolite powder, 0.5 part of konjac glucomannan, 0.02 part of over Potassium sulfate, 0.04 parts of aluminum chloride, 0.01 parts of N,N' methylenebisacrylamide, 0.1 parts of sodium bicarbonate, 0.5 parts of sodium carboxymethylcellulose, 1 part of polyethylene wax, 0.5 parts of attapulgite and 0.5 part oleic acid.

[0056] A method for preparing a weather-resistant resin masterbatch for agricultural mulch film synthesis, carried out according t...

Embodiment 3

[0084] A weather-resistant resin masterbatch for agricultural mulch film synthesis, the formula is the following weight parts: 45 parts of linear low-density polyethylene powder, 25 parts of low-density polyethylene powder, 8 parts of high-density polyethylene powder, 1 part of Bis(3,5-tertiary butyl-4-hydroxyphenyl) sulfide, 0.5 part of didodecyl alcohol ester, 0.5 part of dioctadecyl alcohol ester, 0.5 part of hexamethylphosphoric triamide, 0.5 part 2,4,6-tris(2'-butoxyphenyl)-1,3,5-triazine, 0.5 part 2,4-dihydroxybenzophenone, 0.5 part 2-hydroxy-4-methoxy Base benzophenone, 6 parts of acrylic acid, 8 parts of 5 wt% sodium hydroxide aqueous solution, 1.5 parts of sepiolite powder, 1.5 parts of konjac glucomannan, 0.04 parts of potassium persulfate, 0.06 parts of aluminum chloride, 0.03 parts N,N' Methylenebisacrylamide, 0.3 parts sodium bicarbonate, 1.5 parts sodium carboxymethylcellulose, 2 parts polyethylene wax, 1.5 parts attapulgite and 1.5 parts oleic acid.

[0085] A ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tear loadaaaaaaaaaa
tear loadaaaaaaaaaa
tear loadaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of mulching film materials, and discloses a weather-proof resin master batch for agricultural plastic mulching film synthesis and a preparation method thereof. The weather-proof resin master batch is prepared from 45-65 parts of linear low density polyethylene powder, 15-25 parts of low density polyethylene powder, 4-8 parts of high density polyethylene powder, 1-2 parts of an antioxidant, 0.5-1 part of a light stabilizer, 0.5-1 part of an ultraviolet light absorber, 4-6 parts of acrylic acid, 4-8 parts of a sodium hydroxide water solution, 0.5-1.5 parts of sea-foam stone powder, 0.5-1.5 parts of konjac glucomannan, 0.02-0.04 part of potassium persulfate, 0.04-0.06 part of aluminum chloride, 0.01-0.03 part of N,N' methylene-bisacrylamide, 0.1-0.3 part of sodium bicarbonate, 0.5-1.5 parts of sodium carboxymethyl cellulose and 1-2 parts of polyethylene wax. The weather-proof resin master batch has the good light resistance and heat resistance and excellent tensile property, and is capable of being repeatedly recycled and long in service life.

Description

technical field [0001] The invention relates to the field of mulch materials, in particular to a weather-resistant resin masterbatch for synthesizing agricultural mulch and a preparation method thereof. Background technique [0002] my country is a traditional large agricultural country, and there is a huge demand for agricultural mulch every year. However, most of the current mulch films have poor weather resistance, and are prone to aging and cracking after being exposed to wind, sun, and rain for a long time. [0003] The Chinese invention patent with application number 201510186686.2 discloses a plastic mulch film with good weather resistance, which is made of the following raw materials in parts by weight: EPDM 2-8 parts, white oil 5-9 parts, polyvinyl chloride 7-10 parts, 1-5 parts of carboxymethyl fatty amine, 4-11 parts of vinyl acetate, 9-14 parts of stearic acid, 1-4 parts of nano-Cr-W alloy powder, 4-9 parts of aluminum-based nanomaterials, 1 part of chromium oxi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/06C08L33/02C08L5/02C08L1/28C08K13/06C08K9/12C08K9/06C08K3/34C08K5/09A01G13/02
CPCA01G13/0275C08J5/18C08J2323/08C08J2423/06C08L23/0815C08L2201/08C08L2203/16C08L2205/025C08L2205/035C08L2207/062C08L2207/066C08L23/06C08L33/02C08L5/02C08L1/286C08K13/06C08K9/12C08K9/06C08K3/346C08K5/09
Inventor 李玉德王晓玲周自政
Owner MINQIN COUNTY BANGDE TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka