Indium oxide film material modified with aluminum oxide-coated palladium nanoparticles and its preparation method and application
A technology of palladium nanoparticles and thin-film materials, applied in the direction of material resistance, etc., can solve the problems of inability to realize selective identification of ethanol gas and inability to obtain products, and achieve the effects of improved gas sensing performance, reasonable structure, and scientific preparation methods
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0040] The concrete steps of preparation are:
[0041] Step 1, first pick up the single-layer colloidal ball template floating in the indium nitrate solution and then heat it to obtain a single-layer colloidal ball template solidified with indium nitrate; wherein, the colloidal balls forming the single-layer colloidal ball template have a ball diameter of 1000nm polystyrene colloidal balls. Then place the single-layer colloidal ball template solidified with indium nitrate at 300° C. for annealing to obtain a single-layer porous indium oxide film.
[0042]Step 2, first place the palladium target in a stirred 0.01mol / L aluminum nitrate solution; wherein, the aluminum nitrate solution is an aqueous aluminum nitrate solution. Then use a laser with a wavelength of 532nm (or 1064nm), a repetition rate of 1Hz, a pulse width of 15ns, and a power of 40mJ / pulse to irradiate the palladium target for 18 minutes; wherein, the diameter of the laser spot is 0.5mm, and the emission wavelengt...
Embodiment 2
[0045] The concrete steps of preparation are:
[0046] Step 1, first pick up the single-layer colloidal ball template floating in the indium nitrate solution and then heat it to obtain a single-layer colloidal ball template solidified with indium nitrate; wherein, the colloidal balls forming the single-layer colloidal ball template have a ball diameter of 1000nm polystyrene colloidal balls. Then place the single-layer colloidal ball template solidified with indium nitrate at 325° C. for annealing to obtain a single-layer porous indium oxide film.
[0047] Step 2, first place the palladium target in a stirred 0.05 mol / L aluminum nitrate solution; wherein, the aluminum nitrate solution is an aqueous aluminum nitrate solution. Then use a laser with a wavelength of 532nm (or 1064nm), a repetition rate of 5Hz, a pulse width of 12.5ns, and a power of 60mJ / pulse to irradiate the palladium target for 14min; wherein, the laser spot diameter is 1mm, and the emission wavelength is 532nm...
Embodiment 3
[0050] The concrete steps of preparation are:
[0051] Step 1, first pick up the single-layer colloidal ball template floating in the indium nitrate solution and then heat it to obtain a single-layer colloidal ball template solidified with indium nitrate; wherein, the colloidal balls forming the single-layer colloidal ball template have a ball diameter of 1000nm polystyrene colloidal balls. Then place the single-layer colloidal ball template solidified with indium nitrate at 350° C. for annealing to obtain a single-layer porous indium oxide film.
[0052] Step 2, first place the palladium target in a 0.2 mol / L aluminum nitrate solution under stirring; wherein, the aluminum nitrate solution is an aqueous aluminum nitrate solution. Then use a laser with a wavelength of 532nm (or 1064nm), a repetition rate of 10Hz, a pulse width of 10ns, and a power of 80mJ / pulse to irradiate the palladium target for 9 minutes; wherein, the laser spot diameter is 1.5mm, and the emission waveleng...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com