Flame retardant composite textile fabric

A flame retardant composite and fabric technology, which is applied to synthetic resin layered products, layered products, metal layered products, etc. Simple production process, different styles of effects

CN105644046AInactive Publication Date: 2016-06-08吴建平
0 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
Publication Date
2016-06-08
Estimated Expiration
Not applicable · inactive patent

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
Patent Text Reader

Abstract

The present invention relates to a flame retardant composite textile fabric including an upper cotton cloth layer (1) and a lower cotton cloth layer (2), a base layer (5) is compounded under the lower cotton cloth layer, an anti-static layer(3) is arranged between the upper cotton cloth layer (1) and the lower cotton cloth layer (2), the anti-static layer(3) is made from core-spun yarn fiber, the core-spun yarn fiber includes a yarn (3.1) and a metal wire (3.2), the metal wire winds the yarn, the surface of the upper cotton cloth layer (1) is covered with a layer of fire-retardant coating (4), and the fire-retardant coating (4) comprises a bottom fire-retardant polyurethane layer (4.1) and a top silicone oil layer (4.2). The base layer is made of a fabric, the fabric comprises a machine-woven fabric and a knitted fabric, the machine-woven fabric and the knitted fabric are bonded together by an adhesive. The flame retardant composite textile fabric is low in cost and bending-variable. One side of the flame retardant composite textile fabric is the machine-woven fabric, and the other side of the flame retardant composite textile fabric is the knitted fabric, so that garments prepared from the flame retardant composite textile fabric can be used in both sides, and are different in styles, novel and unique.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a flame-retardant composite fabric fabric. Background technique

[0002] As one of the most familiar textiles in people's lives, flame-retardant composite fabrics are widely used in modern life. The flame-retardant composite fabrics in the prior art are mostly woven with flame-retardant yarns, but they are woven with flame-retardant yarns. The production cost of the flame-retardant composite fabric fabric is relatively high, and the process is relatively complicated; meanwhile, the flame-retardant composite fabric fabric in the prior art adopts low price and good cotton-type fabric of its comfort, but the wrinkle resistance of this cotton-type fabric product is Sexuality and coolness are poor. At the same time, pure cotton cloth also has the defects of being easy to shrink, wrinkle, and not crisp, and the rigidity and flexibility of the fabric are poor. Features.

[0003] In addition, the traditional fabrics used to make clo...

Examples

Embodiment Construction

[0013] see figure 1 and figure 2 , the present invention relates to a flame-retardant composite fabric fabric, which includes an upper cotton layer 1 and a lower cotton layer 2, a base layer 5 is compounded under the lower cotton layer 2, and there is a gap between the upper cotton layer 1 and the lower cotton layer 2. An antistatic layer 3 is provided, and the antistatic layer 3 is made of core-spun silk fibers, and the fibers include yarns 3.1 and metal wires 3.2, and the metal wires 3.2 are wound on the yarns 3.1, and the upper cotton layer 1 The surface is covered with a layer of flame-retardant coating 4, which includes a flame-retardant polyurethane layer 4.1 at the bottom and an organic silicone oil layer 4.2 at the top. The flame-retardant polyurethane layer 4.1 has good flame-retardant performance and is suitable for applications with high flame-retardant requirements. In the use of occasions, the silicone oil layer 4.2 makes the surface of the fabric smooth and non...