A kind of aminosilane modified ecological nano gel material and preparation method thereof

An aminosilane and nanomaterial technology, applied in the field of building materials, can solve problems such as inability to disperse silica fume, and achieve the effect of improving dispersibility and improving microstructure

Active Publication Date: 2017-12-19
SOUTHEAST UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the field of rubber industry, silane coupling agent plays an important role in the dispersant of nanomaterials. However, in the field of rubber materials, most of the matrix is ​​weakly acidic, while the matrix of cement materials is strongly alkaline. The polymerization state in the state is also completely different, therefore, it is impossible to disperse silica fume by deriving the method described in the patent CN102964881B

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of aminosilane modified ecological nano gel material and preparation method thereof
  • A kind of aminosilane modified ecological nano gel material and preparation method thereof
  • A kind of aminosilane modified ecological nano gel material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An aminosilane modified ecological nano cementitious material, by weight, the water-cement ratio is 0.15, the other components except water and the mass percentage are as follows: cement is 35%, ecological nanomaterial is 3%, limestone powder 19.987%, 40% of high-quality I grade low calcium fly ash, 0.013% of aminosilane modifier, and 2% of polycarboxylic acid superplasticizer.

[0027] The surface potential diagram of silica fume particles before and after modification is as follows figure 1 As shown, the picture shows that the potential of the modified silica fume particles is converted to a positive potential; the comparison of the microscopic morphology of the silica fume particles before and after the modification combined with the water reducing agent is shown in the figure figure 2 As shown, the picture shows that the dispersibility of silica fume is significantly improved after modification.

Embodiment 2

[0029] An aminosilane modified ecological nano cementitious material, by weight, the water-cement ratio is 0.20, the other components except water and the mass percentage are as follows: cement 38.5%, ecological nanomaterials 5%, limestone powder 17%, high-quality I-grade low-calcium fly ash is 38%, aminosilane modifier is 0.017%, and superplasticizer is 1.483%.

Embodiment 3

[0031] An aminosilane modified ecological nano cementitious material, by weight, the water-cement ratio is 0.25, the other components except water and the mass percentage are as follows: cement is 42%, ecological nano-material is 11%, limestone powder 14%, high-quality I-grade low-calcium fly ash is 32%, aminosilane modifier is 0.024%, and superplasticizer is 0.976%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aminosilane-modified ecological nano cementing material and a preparation method thereof. According to the aminosilane-modified ecological nano cementing material, the ratio of water to ash is 0.15-0.35; except the water, the cementing material is prepared from the following raw materials in percentage by mass: 35%-55% of cement, 3%-11% of an ecological nano material, 10%-20% of limestone powder, 30%-40% of flyash, 0.013%-0.024% of an aminosilane modification agent and 0.2%-2% of a water reducer. The ecological nano material silicon powder is pre-dispersed, so that the dispersibility of the ecological nano material in a cement-based material is greatly improved; the micro-aggregate effect, the filling effect and the volcanic ash effect of the ecological nano material are more fully exerted; the properties such as microstructure, the physical and mechanical properties and the durability and the like of the cementing material are more effectively improved.

Description

Technical field [0001] The invention relates to the technical field of building materials, in particular to an aminosilane modified ecological nano-gelling material and a preparation method thereof. Background technique [0002] Silica fume is a kind of ecological nano-material with micro-nano particles, which has been widely used in the configuration and use of cement concrete and other building materials. Silica fume has a good pozzolanic effect and particle filling effect, which can significantly improve the microstructure of cement-based materials and improve their mechanical and durability properties. It is precisely because of the extremely high surface area and surface energy of silica fume that silica fume particles are easily agglomerated in their natural state, which leads to the complete loss of many excellent properties of micro-nano silica fume, and the actual use effect is not good. Therefore, how to eliminate The agglomeration effect between silica fume particles ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B20/02
CPCC04B20/02C04B28/04C04B2111/00008C04B18/146C04B14/28C04B18/08C04B24/42C04B24/24C04B20/0016C04B20/0004
Inventor 郭丽萍雷东移
Owner SOUTHEAST UNIV