A special masterbatch for high permeable floor tiles

A masterbatch and ground technology, applied in the field of slab bricks, can solve the problems of easy breakage, rough surface, and single color, and achieve the effects of alleviating the pressure of waterlogging, good emergency characteristics, and efficient water collection and ecological balance.

Active Publication Date: 2018-08-17
山西耀辉生态环保科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The surface of traditional floor tiles is rough, the color is single, the strength is low, and it is easy to break.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 10 parts of resin, 20 parts of styrene-acrylic emulsion, 16 parts of methyl ethyl ketone peroxide, 100 parts of magnesium oxide, 70 parts of cement, and 18 parts of pure acrylic emulsion.

[0020] Wherein, the resin is epoxy resin glue.

[0021] Wherein, the magnesium oxide is nano magnesium oxide with a particle size range of 100nm.

[0022] Wherein, the cement adopts CA-50 aluminate cement.

Embodiment 2

[0024] 25 parts of resin, 35 parts of styrene-acrylic emulsion, 28 parts of methyl ethyl ketone peroxide, 50 parts of magnesium oxide, 98 parts of cement, and 29 parts of pure acrylic emulsion.

[0025] Wherein, the resin adopts anaerobic adhesive.

[0026] Wherein, the magnesium oxide is nano-sized magnesium oxide with a particle size range of 500nm.

[0027] Wherein, the cement adopts sulphoaluminate cement.

Embodiment 3

[0029] 15 parts of resin, 23 parts of styrene-acrylic emulsion, 17 parts of methyl ethyl ketone peroxide, 110 parts of magnesium oxide, 81 parts of cement, 24 parts of pure acrylic emulsion.

[0030] Wherein, the resin is epoxy resin glue.

[0031] Wherein, the magnesium oxide is nano-sized magnesium oxide with a particle size range of 200nm.

[0032] Wherein, the cement adopts iron-aluminate cement.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of slab bricks, and in particular relates to a special master batch of a high-water-permeability floor brick. The special master batch is prepared from the following raw materials in parts: 10-25 parts of resin, 20-35 parts of a benzene acrylic solution, 16-28 parts of methyl ethyl ketone peroxide, 100-150 parts of magnesium oxide, 70-98 parts of cement and 18-29 parts of a pure acrylic emulsion. The special master batch mainly has the effects of preventing sudden heavy rainfall such as heavy rain and rainstorm and has good emergency response properties.

Description

technical field [0001] The invention relates to the technical field of slab tiles, in particular to a special masterbatch for high water-permeable floor slab tiles. Background technique [0002] Floor tiles are an important decorative building material in modern home decoration. In addition to their functional characteristics such as moisture resistance, wear resistance and firmness, they often use different patterns as home decoration. The surface of the traditional floor tiles is rough, the color is single, the strength is low, and it is easy to break. Contents of the invention [0003] The purpose of the present invention is to provide a special masterbatch for highly permeable floor tiles in view of the defects and deficiencies of the prior art. The present invention mainly prevents sudden heavy rainfall such as heavy rain and rainstorm, and has good emergency characteristics. [0004] To achieve the above object, the present invention adopts the following technical s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/06C04B14/30C04B24/00C04B24/26C04B24/28
CPCC04B28/06C04B28/065C04B24/281C04B24/26C04B24/008C04B14/304C04B24/2641
Inventor 李家伟宋刚孙炜宁孙宏亮李毅李韬
Owner 山西耀辉生态环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com