C30 tailing sand anti-washout concrete and preparing method thereof

A technology of tailings sand and concrete, which is applied in the field of building materials, can solve the problems of inability to meet the requirements of underwater construction and low concrete strength, and achieve the effects of reducing concrete costs, low production costs, and easy-to-obtain materials

Active Publication Date: 2016-08-17
WUHAN YUANJING READY MIXED CONCRETE CO LTD
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the ordinary concrete material system cannot meet the requirements of underwater construction
At this stage, there are anti-dispersion agents mentio

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • C30 tailing sand anti-washout concrete and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] This embodiment provides a C30 tailings sand anti-dispersion concrete. The amount of materials per cubic concrete is as follows: 300 kg of cement, 100 kg of activated tailings, 350 kg of coarse tailings, 400 kg of machine-made sand, 1100 kg of stone, 150 kg of water, and 60 kg of admixture.

[0035] The preparation method of the above-mentioned C30 tailings sand anti-dispersion concrete comprises the following steps:

[0036] 1) Screening: Take the tailings sand according to the amount of the material, and obtain two kinds of tailings sand with a size of less than 80 μm or more than 80 μm through screening, and the tailings sand with a size of more than 80 μm is coarse tailings sand;

[0037] 2) Calcination: calcining tailings sand below 80 μm at 600-800°C for 3 hours, and cooling to room temperature for 0.5-2 hours;

[0038] 3) Weighing: Take cement, machine-made sand, stone, water, admixture, active tailings sand, and coarse tailings sand according to the amount of ma...

Embodiment 2

[0049] This embodiment provides a kind of C30 tailings sand anti-dispersion concrete. The amount of each material in each cubic concrete is as follows: the amount of each material in each cubic concrete is 240 kg of cement, 160 kg of activated tailings sand, 300 kg of coarse tailings sand, 450 kg of machine-made sand, and 1056 kg of melon seeds. , water 160kg, admixture 60kg.

[0050] The preparation method of the above-mentioned C30 tailings sand anti-dispersion concrete is the same as that of Example 1.

[0051] The composition and preparation method of the above-mentioned admixture are the same as in Example 1.

Embodiment 3

[0053] This embodiment provides a C30 tailings sand anti-dispersion concrete. The amount of materials in each cubic concrete is as follows: 280 kg of cement, 120 kg of activated tailings sand, 450 kg of coarse tailings sand, 300 kg of machine-made sand, 950 kg of melon seeds, 130 kg of water, and 60 kg of admixture .

[0054] The preparation method of the above-mentioned C30 tailings sand anti-dispersion concrete is the same as that of Example 1.

[0055] The composition and preparation method of the above-mentioned admixture are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses C30 tailing sand anti-washout concrete and a preparing method thereof. The concrete is composed of a cementing material, aggregate, an additive and water, the cementing material is composed of cement and activated fine tailing sand, the aggregate is composed of coarse aggregate and fine aggregate, the fine aggregate is composed of coarse tailing sand and manufactured sand, and the coarse aggregate is made of stone. One cubic meter of concrete is prepared from 180-300 kg of cement, 80-160 kg of activated tailing sand, 150-450 kg of coarse tailing sand, 300-600 kg of manufactured sand, 950-1100 kg of stone, 120-170 kg of water and 20-80 kg of additive. The environment-friendly concrete has good promoting effects of protecting the ecological environment and promoting circular economy development, cost of the concrete is reduced, and the concrete has good washout resistance and workability.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a C30 tailing sand anti-dispersion concrete and a preparation method thereof. Background technique [0002] Tailings are the waste after mineral processing and are the main component of industrial solid waste. According to incomplete statistics, more than 10 billion tons of tailings and waste rocks are discharged in the world every year. At present, there are more than 8,000 state-owned mines and more than 110,000 township collective mines in China. The tailings stockpiled is nearly 5 billion tons, and the annual tailings discharge is as high as 500 million tons. Among them, the annual tailings discharge of ferrous metallurgical mines reaches 1.5 billion tons. At present, the comprehensive utilization rate of tailings in my country is only 7%. Therefore, the comprehensive recycling of tailings has been widely concerned by the whole society. [0003] Concrete is one of the mos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B20/04C04B20/02C04B18/12
CPCC04B20/04C04B28/00C04B2201/50C04B18/12C04B14/02C04B24/085C04B24/383C04B24/2652C04B2103/302C04B20/026Y02W30/91
Inventor 周晓阳张凡
Owner WUHAN YUANJING READY MIXED CONCRETE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap