Steel surface water-based treatment agent carrier

A technology of steel surface and treatment agent, applied in the field of metal surface treatment, can solve problems such as low efficiency and cumbersome steps, and achieve the effect of convenient processing and excellent versatility

Active Publication Date: 2016-08-31
ANHUI KAILIN ADVANCED MATERIAL CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the wide application of steel in various fields, different surface treatments are required for different use environments, so different treatment agents are required, and the existing treatment agents often cannot meet the actual needs and need to be prepared by themselves; However, the steps of self-preparation are cumbersome and inefficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A carrier of water-based treatment agent for steel surface, which is obtained by activating a mixed resin; the components of the mixed resin and the parts by mass of each component are: epoxy resin: 25 parts, polyester resin: 45 parts, auxiliary agent: 12 parts parts and deionized water: 15 parts; powder and white oil are also included; the quality of powder and white oil is respectively 12% and 3% of the total mass of epoxy resin and polyester resin.

[0017] The powder is an inorganic powder, and its composition and the mass percentage of the powder are as follows: TiO 2 : 35%, Al 2 o 3 : 48%, SiO 2 : 17%.

[0018] The components of the additives and the percentages of each component in the total mass of the additives are: compatibilizer: 35%, plasticizer: 52%, dispersant: 13%.

[0019] The specific method for activating the mixed resin is: dissolving polyvinylpyrrolidone in water, and raising the temperature to 220°C to generate polyvinylpyrrolidone vapor; at the...

Embodiment 2

[0021] A carrier of water-based treatment agent for steel surface, which is obtained by activating a mixed resin; the components of the mixed resin and the parts by mass of each component are: epoxy resin: 48 parts, polyester resin: 25 parts, auxiliary agent: 12 parts parts and deionized water: 15 parts; powder and white oil are also included; the quality of powder and white oil is respectively 18% and 7% of the total mass of epoxy resin and polyester resin.

[0022] The powder is an inorganic powder, and its composition and the mass percentage of the powder are as follows: TiO 2 : 58%, Al 2 o 3 : 32%, SiO 2 : 10%.

[0023] The components of the additives and the percentages of each component in the total mass of the additives are: compatibilizer: 55%, plasticizer: 30%, dispersant: 15%.

[0024] The specific method for activating the mixed resin is: dissolving polyvinylpyrrolidone in water, and raising the temperature to 230°C to generate polyvinylpyrrolidone vapor; at the...

Embodiment 3

[0026] A carrier of water-based treatment agent for steel surface, which is obtained by activating a mixed resin; the components of the mixed resin and the parts by mass of each component are: epoxy resin: 40 parts, polyester resin: 40 parts, auxiliary agent: 15 parts parts and deionized water: 17 parts; powder and white oil are also included; the quality of powder and white oil is respectively 15% and 5% of the total mass of epoxy resin and polyester resin.

[0027] The powder is an inorganic powder, and its composition and the mass percentage of the powder are as follows: TiO 2 : 50%, Al 2 o 3 : 35%, SiO 2 : 15%.

[0028] The components of the additives and the percentages of each component in the total mass of the additives are: compatibilizer: 45%, plasticizer: 45%, dispersant: 10%.

[0029] The specific method for activating the mixed resin is: dissolving polyvinylpyrrolidone in water, and raising the temperature to 230°C to generate polyvinylpyrrolidone vapor; at the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a steel surface water-based treatment agent carrier, which is obtained by activation of mixed resin. The mixed resin comprises the following components by mass: 25-48 parts of epoxy resin, 25-45 parts of polyester resin, 12-16 parts of assistants, and 15-20 parts of deionized water. The assistants include a compatibilizer, a plasticizer and a dispersant. The invention provides a modified activated carrier used for a steel surface water-based treatment agent, corresponding components can be added to combine with the carrier according to specific practical use, the carrier is more convenient for processing, and has excellent versatility.

Description

technical field [0001] The invention belongs to the technical field of metal surface treatment, and in particular relates to a water-based treatment agent carrier for steel surface. Background technique [0002] With the wide application of steel in various fields, different surface treatments are required for different use environments, so different treatment agents are required, and the existing treatment agents often cannot meet the actual needs and need to be prepared by themselves; However, the steps of self-preparation are cumbersome and inefficient. [0003] Therefore, it is an urgent problem for those skilled in the art to develop a rapid preparation carrier for the preparation of the steel surface water-based treatment agent for the above problems. Contents of the invention [0004] In order to solve the above problems, the invention discloses a carrier of a steel surface water-based treatment agent. [0005] In order to achieve the above object, the present inv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/00C08L63/00C08L91/06C08K13/02C08K3/22C08K3/36C08J3/00
CPCC08J3/00C08J2363/00C08J2367/00C08J2463/00C08J2467/00C08L63/00C08L67/00C08L2205/035C08L91/06C08K13/02C08K2003/2241C08K2003/2227C08K3/36
Inventor 王和山朱建林王和东
Owner ANHUI KAILIN ADVANCED MATERIAL CO LTD