High-strength low-hardness low-chromium medium-manganese alloy for motor rotor

A motor rotor, high-strength technology, applied in the field of alloys, can solve the problems of medium manganese content, low chromium content, low cost, etc., and achieve the effects of increasing hardenability, improving hardness and prolonging service life

Inactive Publication Date: 2016-10-26
宁国井田机电有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the technical problems existing in the background technology, the present invention proposes a high-strength hard low-chromium manganese alloy for motor rotors, which has excellent hardness and hardness, low chromium content, medium manganese content, low cost, and uniform strength and hardness. Can meet the needs of actual production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The present invention proposes a high-strength hard low-chromium manganese alloy for a motor rotor. The high-strength hard low-chromium manganese alloy for a motor rotor is composed of 3.55 mass percent of C, 3.8 mass percent of Si, 6.35 mass percent of Mn, 0.08% by mass of P, 0.015% by mass of S, 0.0375% by mass of Re, and the remainder is composed of Fe and unavoidable impurities.

Embodiment 2

[0023] The present invention proposes a high-strength hard low-chromium manganese alloy for a motor rotor. The high-strength hard low-chromium manganese alloy for a motor rotor consists of 3.3 mass percent of C, 4.3 mass percent of Si, 5.7 mass percent of Mn, 0.15% by mass of P, 0.01% by mass of S, 0.05% by mass of Re, and the remainder is composed of Fe and unavoidable impurities.

Embodiment 3

[0025] The present invention proposes a high-strength hard low-chromium manganese alloy for a motor rotor. The high-strength hard low-chromium manganese alloy for a motor rotor consists of 3.8 mass percent of C, 3.3 mass percent of Si, 7.0 mass percent of Mn, 0.01 mass percent of P, 0.02 mass percent of S, 0.025 mass percent of R, and the remainder is composed of Fe and unavoidable impurities.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength low-hardness low-chromium medium-manganese alloy for a motor rotor. The high-strength low-hardness low-chromium medium-manganese alloy for the motor rotor comprises, by mass, no less than 3.3% and no more than 3.8% of C, no less than 3.3% and no more than 4.3% of Si, no less than 5.7% and no more than 7.0% of Mn, no less than 0.01% and no more than 0.15% of P, no less than 0.01% and no more than 0.02% of S, and no less than 0.025% and no more than 0.05% of Re, with the balance being Fe and unavoidable impurities. The alloy provided by the invention has excellent hardness and rigidity, low chromium content, medium manganese content and low cost, and the strength of rigidity of the alloy can meet demands of actual production.

Description

technical field [0001] The invention relates to the field of alloys, in particular to a high-strength hard low-chromium medium-manganese alloy for motor rotors. Background technique [0002] At present, during the use of the motor rotor, the hardness of the alloy determines the amount of wear of the alloy. The hardness of the existing high-chromium alloy is generally HRC55-60, which has smaller wear and loss than medium-chromium alloys and low-chromium alloys. Alloy hardness is too high and it is easy to cause adverse consequences of fracture. Therefore, in the process of producing the alloy, it is necessary to ensure that the alloy has high hardness and good toughness. Contents of the invention [0003] In order to solve the technical problems existing in the background technology, the present invention proposes a high-strength hard low-chromium manganese alloy for motor rotors, which has excellent hardness and hardness, low chromium content, medium manganese content, low...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/04C22C38/02
CPCC22C38/04C22C38/005C22C38/02
Inventor 倪盛
Owner 宁国井田机电有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More