Mud of firewood-fired Nixing pottery and process of making firewood-fired Nixing pottery by using the mud

A technology of Nixing pottery and firewood burning, applied in the field of preparing Nixing pottery, can solve the problems of burning and cracking of the body of Nixing pottery, high cost of firewood burning Nixing pottery, poor ash falling effect, etc., and can reach the firing temperature range. The effect of widening and saving fuelwood cost

Inactive Publication Date: 2018-11-13
钦州市壮冠坭兴陶材料开发有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Firewood-fired Nixing pottery requires more than two days of firing time, and the firing temperature must be above 1260°C, otherwise the effect of falling ash will be poor, which will greatly increase the consumption of firewood and cause the cost of firewood-fired Nixing pottery to be relatively high. high
Not only that, the firing temperature of traditional Nixing pottery clay is relatively low, generally 1100°C to 1200°C to make pottery. At this temperature, it is difficult for wood ash to completely melt, and it is impossible to accumulate ash on the surface of the Nixing pottery body to form a glaze. Increase the firing temperature to above 1260°C, and the body of Nixing pottery will be cracked

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 1) Prepare the blank: mix 5.5 parts of Dongni, 1.3 parts of Xini, 1 part of ashes from burning Paulownia branches and / or leaves, and 2 parts of high white mud, and make a blank through a series of processes such as grinding and dehydration;

[0020] 2) Body molding: the blank is made into various types of green bodies by plastic method or grouting method;

[0021] 3) Trim the green body: trim the green body to meet the design requirements;

[0022] 4) drying: adopt air-drying method to dry green body, make green body water get rid of;

[0023] 5) Firing the green body: put the dried green body into a firewood kiln, use Paulownia branches and / or leaves as fuel, heat up to 1180°C at a heating rate of 60°C, stop heating, and leave the kiln after natural cooling.

Embodiment 2

[0025] 1) Preparation of blanks: Mix 6.8 parts of eastern mud, 2.0 parts of western mud, 1.5 parts of ashes from burning citrus branches or leaves, and 2.5 parts of high white mud, and make blanks through a series of processes such as grinding and dehydration;

[0026] 2) Body molding: the blank is made into various types of green bodies by plastic method or grouting method;

[0027] 3) Trim the green body: trim the green body to meet the design requirements;

[0028] 4) drying: adopt air-drying method to dry green body, make green body water get rid of;

[0029] 5) Firing the green body: put the dried green body into a firewood kiln, use citrus branches or leaves as fuel, heat up to 1175°C at a heating rate of 80°C, stop heating, and leave the kiln after natural cooling.

Embodiment 3

[0031] 1) Prepare the blank: mix 5.6 parts of eastern mud, 1.3 parts of western mud, 1 part of ashes from burning pine branches and / or leaves, and 2.1 parts of high white mud, and make a blank through a series of processes such as grinding and dehydration;

[0032] 2) Body molding: the blank is made into various types of green bodies by plastic method or grouting method;

[0033] 3) Trim the green body: trim the green body to meet the design requirements;

[0034] 4) drying: adopt air-drying method to dry green body, make green body water get rid of;

[0035] 5) Firing the green body: put the dried green body into a firewood kiln, use pine branches and / or leaves as fuel, first raise the temperature to 450°C at a rate of 80°C per hour, and then increase the temperature at a rate of 80°C per hour. Raise the temperature to 900°C at a heating rate of 150°C, and then raise the temperature to 1160°C at a heating rate of 120°C per hour, stop heating, and leave the kiln after natural...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides pug of firewood-fired Nixing pottery and a process for manufacturing the Nixing pottery from the pug. The pug is prepared from, by weight, 5.5-6.8 parts of eastern mud, 1.3-2.0 parts of western mud, 1-1.5 parts of wood ash and 2-2.5 parts of kaolin. The process of for manufacturing the Nixing pottery from the pug comprises the steps of blank preparation, blank body forming, blank body drying and blank body firing; according to blank preparation, the eastern mud, the western mud, the wood ash and the kaolin with the formula amount are prepared into a blank through a conventional process; according to blank body burning, the blank body is fed into a wood-fired kiln, woody plants are adopted as fuel, the firing temperature ranges from 1,160 DEG C tot 1,180 DEG C, and after firing is completed, cooling and drawing are carried out. The kaolin and the wood ash are added into conventional Nixing pottery pug, so that the firing temperature range of the Nixing pottery is greatly widened; the melting temperature of ash of fuel wood can be reduced, the melting time of the ash can be shortened, and the fuel wood cost is greatly reduced.

Description

technical field [0001] The invention relates to a preparation method of Nixing pottery, in particular to a mud material for firewood-fired Nixing pottery and a process for making firewood-fired Nixing pottery by using the mud material. Background technique [0002] According to historical records, the mud-filling process of Nixing pottery in Qinzhou has been formed since the Qing Dynasty. The traditional mud-filling process of Nixing pottery mainly includes the following steps: 1) Preparation of blanks: The blanks are selected from the east of Qinjiang River, which crosses the urban area of ​​Qinzhou City. The soil in the area is commonly known as Dongni (soft clay with a yellowish-white color and contains a small amount of quartz sand, which plays a role in adjusting plasticity and bonding in the production process of Nixing pottery), and the soil in the west of the Qinjiang River is commonly known as Xini (contains a small amount of K 2 O, NaO, CaO, MgO, Fe 2 0 3 、TiO ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/135C04B33/32
CPCC04B33/1355C04B33/32Y02P40/60
Inventor 胡国章
Owner 钦州市壮冠坭兴陶材料开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products