Waterproof fabric for fan
A waterproof fabric and fan technology, applied in textiles and papermaking, etc., can solve problems such as breakage and moisture absorption of fabrics, and achieve the effect of enhanced service life and good coloring effect.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] A waterproof fabric for fans, comprising a base cloth and a coating layer located on one side of the base cloth, the coating layer is sequentially composed of a bottom layer, a middle layer and a surface layer; between the bottom layer, the middle layer and the top layer The thickness ratio is 7:12:10.
[0017] The bottom layer is a slurry composed of 3 parts by mass of hexane diisocyanate, 5 parts by mass of butanone, 12 parts by mass of toluene, 40 parts by mass of polyurethane resin, 64 parts by mass of water, and 1 part by mass of N-methylethanolamine Obtained after coating and drying.
[0018] The middle layer is composed of 3 parts by mass of 1,6-diisocyanate hexane, 50 parts by mass of polyurethane resin, 2 parts by mass of N-methylethanolamine, 55 parts by mass of water, 11 parts by mass of butanone, and 20 parts by mass of toluene obtained after coating and drying.
[0019] The surface layer is obtained by coating and drying a slurry composed of 4 parts by ma...
Embodiment 2
[0021] A waterproof fabric for fans, comprising a base cloth and a coating layer located on one side of the base cloth, the coating layer is sequentially composed of a bottom layer, a middle layer and a surface layer; between the bottom layer, the middle layer and the top layer The thickness ratio is 7:12:10.
[0022] The bottom layer is a slurry composed of 8 parts by mass of 1,6-hexanediisocyanate, 10 parts by mass of butanone, 20 parts by mass of toluene, 70 parts by mass of polyurethane resin, 80 parts by mass of water, and 10 parts by mass of N-methylethanolamine Obtained after coating and drying.
[0023] The middle layer is a pulp composed of 15 parts by mass of 1,6-diisocyanate hexane, 100 parts by mass of polyurethane resin, 10 parts by mass of N-methylethanolamine, 80 parts by mass of water, 20 parts by mass of butanone, and 30 parts by mass of toluene obtained after coating and drying.
[0024] The surface layer is obtained by coating and drying a slurry consistin...
Embodiment 3
[0026] A waterproof fabric for fans, comprising a base cloth and a coating layer located on one side of the base cloth, the coating layer is sequentially composed of a bottom layer, a middle layer and a surface layer; between the bottom layer, the middle layer and the top layer The thickness ratio is 7:12:10.
[0027] The bottom layer is a slurry composed of 5 parts by mass of 1,6-diisocyanate hexane, 6 parts by mass of butanone, 12 parts by mass of toluene, 50 parts by mass of polyurethane resin, 64 parts by mass of water, and 2 parts by mass of N-methylethanolamine Obtained after coating and drying.
[0028] The middle layer is composed of 5 parts by mass of 1,6-diisocyanate hexane, 50 parts by mass of polyurethane resin, 5 parts by mass of N-methylethanolamine, 55 parts by mass of water, 11 parts by mass of butanone, and 20 parts by mass of toluene obtained after coating and drying.
[0029] The surface layer is obtained by coating and drying a slurry consisting of 6 part...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com