Halogen-free flame retardant slowly-recoverable memory foam

A technology of memory foam and slow rebound, which is applied in the field of sponge preparation, which can solve problems such as difficult to extinguish, smoke toxicity, environmental pollution, etc., and achieve the effect of improving comfort, high flame retardancy, and improving slow rebound effect

Inactive Publication Date: 2017-02-15
HUAIAN TONGCHUANG FOAMED PLASTIC CO LTD
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Sponge products are easy to burn when exposed to open flames or hot flames, and the same is true for slow-rebound memory foam. Once burned, it is difficult to extinguish, and the smoke produced is also toxic to a certain extent. Fire-proof sponges are prepared by adding flame retardants It can achieve the effect of fire prevention and eliminate the hidden danger of flammability, but the flame retardant used in the existing fire prevention sponge contains halogen, which will pollute the environment after being manufactured and discarded

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Halogen-free flame retardant slow rebound memory foam, composed of the following raw materials in parts by weight ratio:

[0022] Polyether polyol 1030 20 parts

[0023] Polyether polyol 2000 4 parts

[0024] MDI 23 copies

[0025] Slow rebound polyether 8 parts

[0026] 8 parts white oil

[0027] Halogen-free flame retardant 9 parts

[0028] Cell opener 1.2 parts

[0029] Amine catalyst 0.02 parts

[0030] Silicone oil 0.3 parts

[0031] Among them, ether polyol 1030 is produced by Korea SKC Co., Ltd.; polyether polyol 2000 is produced by Shanghai Jinzijing Chemical Co., Ltd.; MDI is MM5042 produced by Nanjing Hanfeng Chemical Materials Co., Ltd.; slow rebound polyether is produced by Mitsui Chemicals Co., Ltd. LR-00; White oil is 2045 produced by Zhangjiagang Jiayan Chemical Co., Ltd.; Halogen-free flame retardant is HF560 produced by Zhejiang Wansheng Co., Ltd., and the opening agent is KY1218 produced by Shenzhen Weihongxin Technology Co., Ltd. The catalyst is A33 produced by BA...

Embodiment 2

[0036] The halogen-free flame-retardant slow-rebound memory foam raw materials in this implementation are as follows in parts by weight:

[0037] Polyether polyol 1030 30 parts

[0038] Polyether polyol 2000 6 parts

[0039] MDI 40 copies

[0040] Slow rebound polyether 15 parts

[0041] 15 parts white oil

[0042] Halogen-free flame retardant 15 parts

[0043] Opening agent 2 parts

[0044] Amine catalyst 0.2 parts

[0045] Silicone oil 0.5 parts

[0046] Other parameters are the same as in Example 1.

[0047] After testing, the sponge made with the formula in this embodiment: tensile strength 176mpa, rebound rate 37.6%, indentation coefficient 2.09, good slow rebound effect; average combustion coefficient 1.24mm / s (self-extinguishing after fire) , Good flame retardant effect, with a hardness value of 7.8 at 40°C and a hardness value of 12.1 at 0°C. Compared with the existing sponge, the temperature sensitivity is greatly reduced, and it is more comfortable to use.

Embodiment 3

[0049] The halogen-free flame-retardant slow-rebound memory foam raw materials in this implementation are as follows in parts by weight:

[0050] Polyether polyol 1030 50 parts

[0051] Polyether polyol 2000 10 parts

[0052] MDI 56 copies

[0053] Slow rebound polyether 20 parts

[0054] 20 parts white oil

[0055] Halogen-free flame retardant 24 parts

[0056] 3 parts of hole opener

[0057] Amine catalyst 0.5 parts

[0058] Silicone oil 0.9 parts

[0059] Other parameters are the same as in Example 1.

[0060] After testing, the sponge made with the formula in this example: tensile strength 187mpa, rebound rate 38.2%, indentation coefficient 2.07, good slow rebound effect; average combustion coefficient 1.14mm / s (self-extinguishing from fire) , The flame retardant effect is good, the hardness value of 40℃ is 7.5, and the hardness value of 0℃ is 12.1. Compared with the existing sponge, the temperature sensitivity is greatly reduced, and it is more comfortable to use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses halogen-free flame retardant slowly-recoverable memory foam which is prepared from the following raw materials in parts by weight: 20 to 50 parts of polyether glycol 1030, 4 to 10 parts of polyether glycol 2000, 23 to 56 parts of MDI, 8 to 20 parts of slowly-recoverable polyether, 8 to 20 parts of white oil, 9 to 24 parts of a halogen-free flame retardant, 1.2 to 3 parts of an opening agent, 0.02 to 0.5 part of an amine catalyst and 0.3 to 0.9 part of silicon oil. The product retains certain crosslinking degree, so that the product is insensitive to low temperature and cannot be hardened in winter; the added slowly-recoverable polyether LR-00 is insensitive to temperature, so that the influence on the product due to the environmental temperature is low; during use, the halogen-free flame retardant slowly-recoverable memory foam can keep cool in summer and warm in winter; the comfortableness is greatly improved, and the slow recovery effect can be also improved.

Description

Technical field [0001] The invention relates to the field of sponge preparation, in particular to a halogen-free flame-retardant slow-rebound memory sponge. Background technique [0002] Slow rebound memory foam is a kind of sponge that will not rebound immediately after being deformed by external force, but will be delayed for a few seconds and slowly restore. It has a soft hand feel, has a significant slow rebound ability, and can absorb impact, reduce vibration, and reduce The ability to release the rebound force is strong, and the cushions, pillows, mattresses and other items made of slow rebound sponge can make people feel more comfortable and natural. Sponge products are very easy to burn when encountering open flames or hot flames. The same is true for slow rebound memory sponges. Once burned, they are difficult to extinguish. The dense smoke produced is also toxic. Fire-resistant sponges are prepared with flame retardants. It can achieve the effect of fire prevention and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G18/76C08G18/48C08K3/00C08K5/00
CPCC08G18/7671C08G18/4804C08G2101/00C08K5/0066
Inventor 赵军
Owner HUAIAN TONGCHUANG FOAMED PLASTIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap