A technology of amphoteric polycarboxylate and water reducer, applied in the field of polycarboxylate water reducer and its preparation, star-shaped amphoteric polycarboxylate water reducer and its preparation, to increase adsorption capacity, fluidity and good dispersibility , the effect of improving liquidity

Active Publication Date: 2017-03-15
SHANDONG JIAOTONG UNIV
View PDF5 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the search found that most of the polycarboxylate superplasticizers described in the current patents mainly achieve the anti-mud effect by adjusting the content of their own components or compounding with anti-mud agents. Few of them change the polymer structure through molecular structure design or adopt new ones. polymerization method to achieve its excellent application performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Star-like amphoteric polycarboxylate superplasticizer with efficient anti-mudding function and preparation method thereof
  • Star-like amphoteric polycarboxylate superplasticizer with efficient anti-mudding function and preparation method thereof
  • Star-like amphoteric polycarboxylate superplasticizer with efficient anti-mudding function and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] (1) Preparation of Star Chain Transfer Agent

[0033] Potassium O-ethylxanthate (16.03 g, 0.1 mol) was dissolved in 80 mL of anhydrous tetrahydrofuran (THF), added to a 150 mL three-neck flask, and then triethylamine (10.1, 0.1 mol) was added as a proton absorber. Stir in an ice-water bath for 0.5 h under a nitrogen atmosphere. 2-Bromopropionyl bromide (26.1 g, 0.1 mol) was dissolved in 20 mL of anhydrous THF, then added to a constant pressure dropping funnel, and added drop by drop into a three-necked flask. After the dropwise addition was completed, the reaction was carried out at room temperature for 24 h under nitrogen atmosphere. After the reaction is finished, the reaction solution is filtered, and the filtrate is rotary evaporated to remove the solvent to obtain a dithioester compound containing an acid bromide group.

[0034]β-cyclodextrin (11.35g, 0.01mo) was dissolved in 60mL of anhydrous N,N-dimethylformamide (DMF), added to a 100mL three-necked flask, and ...

Embodiment 2

[0042] This example prepares star-shaped amphoteric polycarboxylate superplasticizer (marked as SZP2) in the same manner as Example 1, the only difference being that the amount of methacryloyloxyethyltrimethylammonium chloride is 0.1mol, so that the chain The molar ratio of transfer agent, initiator, polyethylene glycol methacrylate, methacrylic acid and methacryloxyethyltrimethylammonium chloride is 1:7:35:105:10.

[0043] In this embodiment, the slurry fluidity and soil resistance performance are tested in the same manner as in Example 1, and the test results are shown in Table 1.

Embodiment 3

[0045] In this example, a star-shaped amphoteric polycarboxylate superplasticizer (marked as SZP3) was prepared in the same manner as in Example 1, except that the molecular weight of polyethylene glycol methacrylate in step (2) was 1000 g / mol.

[0046] In this embodiment, the slurry fluidity and soil resistance performance are tested in the same manner as in Example 1, and the test results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a star-like amphoteric polycarboxylate superplasticizer with efficient anti-mudding function and a preparation method thereof; the preparation method comprises: esterifying Beta-cyclodextrin and a dithioester compound with acyl halide groups to obtain star-structure reversible addition-fragmentation chain transfer agent (RAFT agent), initiating RAFT polymerization of (methyl)polyethylene glycol diacrylate, (methyl)acrylic acid and (methyl)acryloyloxyethyl trimethyl ammonium chloride under the action of the chain transfer agent and an initiator to obtain star-like amphoteric copolymer, and carrying out further processing to obtain the star-like amphoteric polycarboxylate superplasticizer having a solid content of 20% and efficient anti-mudding function. The polycarboxylate superplasticizer prepared herein has high water-reducing rate and efficient ant-mudding function and may meet high construction requirements.

Description

technical field [0001] The invention relates to a polycarboxylate water reducer and a preparation method thereof, in particular to a star-shaped amphoteric polycarboxylate water reducer with high-efficiency mud resistance and a preparation method thereof, belonging to the technical field of concrete admixtures in building materials. Background technique [0002] Polycarboxylate superplasticizer, as the third generation of high-performance concrete superplasticizer, has outstanding advantages such as low dosage, high water reducing rate, good slump retention performance, strong molecular structure adjustability, and high performance potential. It has been successfully used in a series of major projects such as high-speed railways, bridges, and tunnels. [0003] Polycarboxylate high-efficiency superplasticizers also encounter many technical difficulties in practical applications, such as adaptability to cement / admixtures, sensitivity to superplasticizer dosage and water consum...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/06C08F220/06C08F220/34C08F2/38C04B24/32C04B103/30
CPCC04B24/32C04B2103/302C08F2/38C08F283/065C08F2438/03C08F220/06
Inventor 唐新德胡秀颖徐大举徐静庞来学周德杰王可良
Owner SHANDONG JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap