Graphene heating fabric and method for preparing same

A heating fabric and graphene technology, applied in the field of fabrics, can solve the problems of non-heating fabrics and cumbersome preparation methods

Inactive Publication Date: 2017-03-15
SUZHOU XINGFENGQIANG TEXTILE TECH CO LTD
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, the present invention provides a method for preparing a graphene heating fabric on the one hand, which solves the problems that the preparation method is cumbersome and the fabric has no heating function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene heating fabric and method for preparing same
  • Graphene heating fabric and method for preparing same
  • Graphene heating fabric and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The preparation method of the graphene heating fabric in this implementation comprises the following steps:

[0024] Configuration graphene printing paste, by mass parts, graphene printing paste comprises the following components:

[0025]

[0026] The graphene printing paste is printed on the fabric, and the graphene heating fabric is obtained by printing, drying, steaming, color fixing, washing, and expanding according to the pattern.

Embodiment 2

[0028] The preparation method of the graphene heating fabric in this implementation comprises the following steps:

[0029] Configuration graphene printing paste, by mass parts, graphene printing paste comprises the following components:

[0030]

[0031] Graphene printing paste is printed on the fabric, and the fabric is fixed between the upper and lower molds of the embossing machine, and the molds are closed. The fabric is transported to the bottom of the pressing plate through the transmission part, and the heating chamber is started to heat the fabric, embossing Press the heated fabric with rollers and bottom rollers, dry at 135°C for 30s, steam at 120°C for 8 minutes, wash at 65°C at a rate of 10m / min, and at 126°C at a rate of 36m / min. The expansion is carried out at a rate of min to obtain a graphene heating fabric.

Embodiment 3

[0033] The preparation method of the graphene heating fabric in this implementation comprises the following steps:

[0034] Configuration graphene printing paste, by mass parts, graphene printing paste comprises the following components:

[0035]

[0036] Graphene printing paste is printed on the fabric, and the fabric is fixed between the upper and lower molds of the embossing machine, and the molds are closed. The fabric is transported to the bottom of the pressing plate through the transmission part, and the heating chamber is started to heat the fabric, embossing Press the heated fabric with rollers and bottom rollers, dry at 142°C for 20s, steam at 122°C for 7 minutes, wash at 64°C at a rate of 9m / min, and at 126°C at a rate of 36m / min. The expansion is carried out at a rate of min to obtain a graphene heating fabric.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a graphene heating fabric and a method for preparing the same. The method includes steps of (1), preparing graphene printing paste comprising, by weight, 80-90 parts of dimethylformamide, 2-5 parts of ammonium chloride, 4-8 parts of triethanolamine, 0.2-1.2 parts of graphene and 10-20 parts of thickening agents; (2), printing the graphene printing paste on fabrics and carrying out printing, drying, steaming color fixing, washing and expanding on the fabrics according to patterns to obtain the graphene heating fabric. The graphene heating fabric and the method have the advantages that the graphene heating fabric has an excellent heating function, heat can be generated after the graphene heating fabric is in contact with human bodies, the temperatures can be increased by 2-3 DEG C, and accordingly the human bodies can feel warm.

Description

technical field [0001] The invention relates to the field of fabrics, in particular to a graphene heating fabric and a preparation method thereof. Background technique [0002] Fabric is the material used to make clothing. As one of the three elements of clothing, fabrics can not only interpret the style and characteristics of clothing, but also directly affect the color and shape of clothing. [0003] Patent Publication No. 104562715A discloses a method for processing cotton flannel printed fabrics, which includes the following steps: weaving → gray cloth off the machine and pre-treatment → bleaching and mercerizing the cloth surface → pre-setting by a setting machine → activity on the machine Printing drying→steaming and washing to fix color→leaving agent softener shaping→shrinking→finished product inspection. The printed fabric has no heating function. Contents of the invention [0004] In view of this, on the one hand, the present invention provides a method for pre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/673D06P1/44D06P1/645D06P1/649
CPCD06P1/673D06P1/445D06P1/645D06P1/6495D06P1/67341
Inventor 王方明
Owner SUZHOU XINGFENGQIANG TEXTILE TECH CO LTD
PatSnap Eureka logo

PatSnap Eureka turns technology decisions into work you can execute. Powered by our Innovation Knowledge Graph, it runs expert workflows across engineering, life sciences, materials and intellectual property. Get your review-ready output in minutes.

X (Twitter)LinkedInYouTubeSubstack

© 2026 PatSnap. All rights reserved. 

Terms of Service

 | 

Privacy policy

 | 

Modern Slavery Act Transparency Statement