Organic and inorganic compound cemented water-permeable brick and preparation method thereof
An inorganic composite and composite cementing agent technology, applied in clay preparation devices, chemical instruments and methods, manufacturing tools, etc., can solve the problems of complex production process, failure of water permeability, unfriendly environment, etc., to achieve simple production process, guarantee glue Bonding strength and the effect of improving water permeability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0033] The present invention also provides a method for preparing the above-mentioned organic-inorganic composite cemented permeable brick, which includes preparation of organic composite cement, forming of permeable brick body, and maintenance of permeable brick body; specifically including the following steps:
[0034] (1) Mix the monomers hydroxypropyl acrylate, acrylamide, sodium dodecylbenzene sulfonate, propyltrimethoxysilane, water and cement according to the weight ratio of the permeable brick of the present invention, and use a rotary mixer to stir For the slurry, the stirring speed is 120 revolutions per minute, and the stirring time is 10-20 minutes. The grafting and copolymerization are completed to form an organic cement;
[0035] (2) On the basis of the organic cement obtained in step (1), add appropriate amount of cement and water, stir and mix with two different particle size aggregates according to the ratio, and vibrate in a steel mold of 100mm×100mm×35mm Press, s...
Example Embodiment
[0040] Example 1
[0041] This embodiment is used to illustrate the organic-inorganic composite cemented permeable brick and the preparation method thereof provided by the present invention.
[0042] Weigh 3g of monomeric hydroxypropyl acrylate, 1g of acrylamide, 0.5g of sodium dodecylbenzene sulfonate, 0.5g of propyltrimethoxysilane, 3g of water, and 4g of cement, and use a rotary mixer for mixing. The speed is 120 revolutions / minute, and the stirring time is 20 minutes to obtain an organic cement. Weigh 480g of gravel with a particle size of 5mm, 120g of river sand with a particle size of 0.5mm, and 68g of cement, mix with the above organic cement, add 20g of water, stir and mix for 10 minutes, pour the mixture into a steel with a size of 100mm×100mm×35mm In the mold making, vibrate for 1 minute, then use a hydraulic press to press and shape under 20MPa pressure, hold the pressure for 1 minute, release the pressure and release the mold to obtain a permeable brick body, which is ...
Example Embodiment
[0045] Example 2
[0046] This embodiment is used to illustrate the organic-inorganic composite cemented permeable brick and the preparation method thereof provided by the present invention.
[0047] Weigh 4g of monomeric hydroxypropyl acrylate, 1.5g of acrylamide, 0.8g of sodium dodecylbenzene sulfonate, 0.7g of propyltrimethoxysilane, 4g of water, and 4g of cement, and use a rotary mixer for mixing and mixing. The speed is 120 rpm and the stirring time is 20 minutes to obtain an organic cement. Weigh 500g of gravel with a particle size of 5mm, 100g of river sand with a particle size of 0.5mm, and 65g of cement, mix with the above organic cement, add 20g of water, stir and mix for 10 minutes, pour the mixture into a steel with a size of 100mm×100mm×35mm In the mold making, vibrate for 1 minute, then use a hydraulic press to press and shape under 20MPa pressure, hold the pressure for 1 minute, release the pressure and release the mold to obtain a permeable brick body, which is cur...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap