Modified-chitosan-containing anti-ultraviolet finishing agent for cotton fabric and anti-ultraviolet cotton fabric obtained by aid of anti-ultraviolet finishing agent

A finishing agent and cotton fabric technology, which is applied in fiber treatment, plant fiber, textiles and papermaking, etc., can solve the problems of cumbersome preparation of nano-scale composite dispersion finishing liquid, complex composition of composite nano-composites, and high requirements for the stability of the dispersion system. Achieve the effects of maintaining human affinity, easy preparation, and simple composition

Active Publication Date: 2017-03-22
EASTERN LIAONING UNIV
View PDF10 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The composite nano-components of inorganic and organic matter are complex, and the implementation of the method requires modification of the original textile pretreatment equipment; in addition, in order to improve the affinity and durability of nano-zinc oxide and fabrics, the adhesive acrylate The addition of will affect the fabric style and feel worse
Another example is the disclosed functionalized nano-chitosan and nano-titanium dioxide modified tussah silk fabric of CN102677465A, which plays an anti-ultraviolet effect by nano-titanium dioxide, and improves the cross-linking fixation of chitosan and tussah silk fabric by organic polyacids, effectively improving and enhancing Tussah silk fabrics have comprehensive properties such as anti-wrinkle, softness, anti-bacterial, anti-shrinkage, self-cleaning, anti-ultraviolet, and dye adsorption efficiency, but the dispersion system of the finishing agent is also relatively complicated, and the preparation of nano-scale composite dispersion finishing liquid is cumbersome. High requirements on the stability of its dispersion system

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified-chitosan-containing anti-ultraviolet finishing agent for cotton fabric and anti-ultraviolet cotton fabric obtained by aid of anti-ultraviolet finishing agent
  • Modified-chitosan-containing anti-ultraviolet finishing agent for cotton fabric and anti-ultraviolet cotton fabric obtained by aid of anti-ultraviolet finishing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] This finishing agent is a homogeneous mixture of 3,4,5-trimethoxybenzoyl chitosan, crosslinking agent, penetrating agent and acetic acid or lactic acid solution, measured per 100 ml of final finishing agent solution, 3,4 , The amount of 5-trimethoxybenzoyl chitosan is 2.0g, dissolved in acetic acid or lactic acid solution containing 2 grams of acetic acid or lactic acid per 100 ml of finishing agent solution, adding 0.5 g of crosslinking agent citric acid, penetrating agent JFC 0.05g and citric acid reaction catalyst sodium hypophosphite 0.5g were prepared to obtain 100ml finishing agent solution;

[0018] Finished cotton fabrics are prepared by the following finishing process: immerse an appropriate amount of cotton fabrics in the above finishing agent solution at room temperature for 0.5 to 1 minute, after two dips and two rollings, the liquid retention rate is 90%, pre-baked at 70°C for 8 minutes, 150 Bake at ℃ for 2 minutes, wash in warm water at 40 ℃, wash in cold ...

Embodiment 2

[0020] This finishing agent is a homogeneous mixture of 3,4,5-trimethoxybenzoyl chitosan, crosslinking agent, penetrating agent and acetic acid or lactic acid solution, measured per 100 ml of final finishing agent solution, 3,4 , The amount of 5-trimethoxybenzoyl chitosan is 2.5g, dissolved in acetic acid or lactic acid solution containing 2 grams of acetic acid or lactic acid per 100 ml of finishing agent solution, and 0.5 g of cross-linking agent butane tetracarboxylic acid is added 1. Penetrant JFC 0.05g, butane tetracarboxylic acid reaction catalyst sodium hypophosphite 0.5g, prepare 100ml finishing agent solution;

[0021] Finished cotton fabrics are prepared by the following finishing process: soak an appropriate amount of cotton fabrics in the above finishing agent solution at room temperature for 0.5-1min, double dipping and rolling, the liquid retention rate is 90%, pre-baking at 85°C for 5 minutes, and baking at 130°C 3min, wash in warm water at 40°C, wash in cold wa...

Embodiment 3

[0023] This finishing agent is a homogeneous mixture of 3,4,5-trimethoxybenzoyl chitosan, crosslinking agent, penetrating agent and acetic acid or lactic acid solution, measured per 100 ml of final finishing agent solution, 3,4 , The amount of 5-trimethoxybenzoyl chitosan is 3.0g, dissolved in acetic acid or lactic acid solution containing 2 grams of acetic acid or lactic acid per 100 ml of finishing agent solution, adding 0.5 g of crosslinking agent citric acid, penetrating agent Pingpingjia O 0.05g, citric acid reaction catalyst sodium hypophosphite 0.5g, prepare 100ml finishing agent solution;

[0024] Finished cotton fabrics are prepared by the following finishing process: soak an appropriate amount of cotton fabrics in the above finishing agent solution at room temperature for 0.5-1min, double dipping and rolling, the liquid retention rate is 90%, pre-baking at 85°C for 5 minutes, and baking at 150°C 2min, wash in warm water at 40°C, wash in cold water, and dry to obtain ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a modified-chitosan-containing anti-ultraviolet finishing agent for cotton fabric and anti-ultraviolet cotton fabric obtained by aid of the anti-ultraviolet finishing agent. The modified-chitosan-containing anti-ultraviolet finishing agent for the cotton fabric is a uniformly mixed solution of 3,4,5-trimethoxybenzoyl chitosan, a crosslinking agent, a penetrant and an acetic acid or lactic acid solution, wherein the crosslinking agent is organic polycarboxylic acid or amino-modified silicone oil emulsion; the penetrant is either JFC or peregal O. The anti-ultraviolet cotton fabric with anti-ultraviolet, anti-bacterial and anti-crease finishing functions is obtained through double-dip double-nip, water washing and drying, the anti-ultraviolet, anti-bacterial and anti-crease finishing functions are high in durability, the cotton fabric still maintains the original style of the fabric after finishing, the hand feel, the strength, the whiteness and the color of the cotton fabric are not affected, and the original human body affinity is maintained; the finishing agent is simple in composition and easy to prepare, and a finishing process is simple and environment-friendly.

Description

technical field [0001] The application of the present invention relates to a fabric anti-ultraviolet finishing agent and its finished fabric, especially relates to a modified chitosan anti-ultraviolet finishing agent and its finished cotton fabric. Background technique [0002] Chitosan is a natural polysaccharide polymer material with rich sources, safety, non-toxicity and good biodegradability. At present, the application of chitosan and its derivatives in the functional finishing of textiles is mainly limited to antibacterial, anti-mildew and anti-wrinkle aspects. Such as the modified chitosan-modified nano-silver antibacterial composite material prepared by patent CN104128602A, the chitosan and nano-silver synergistically exert antibacterial effect. [0003] There are two main categories of textile anti-ultraviolet finishing agents, one is anti-ultraviolet shielding agent, which reduces the transmittance of ultraviolet light by means of reflection, refraction or scatter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/03D06M13/188D06M13/207D06M13/192D06M101/06
CPCD06M13/188D06M13/192D06M13/207D06M15/03D06M2101/06
Inventor 宋明姝路艳华程德红
Owner EASTERN LIAONING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com