A kind of composite resin filter press plate and preparation method thereof

A composite resin, filter press technology, applied in separation methods, chemical instruments and methods, filtration and separation, etc., can solve the problems of poor impact resistance and compressive strength performance of filter press plates, and achieve good cleanliness and relative deformation rate. Lowering, less damage effect

Active Publication Date: 2019-01-29
ZHENGZHOU HOLLOWLITE MATERIALS CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a composite resin filter press plate and a preparation method thereof, which solves the problems of poor impact resistance and compressive strength of the existing filter press plates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] This embodiment provides a composite resin filter press plate, which is made of the following raw materials in parts by weight: 100 parts by weight of polytetrafluoroethylene, 100 parts by weight of ultra-high molecular weight polyethylene, and 5 parts by weight of thermoplastic elastomer SBS , 35 parts by weight of glass fiber, 5 parts by weight of titanate coupling agent, 55 parts by weight of calcium carbonate, 15 parts by weight of modified zeolite, 35 parts by weight of hollow glass microspheres, 2 parts by weight of antioxidant .

[0022] The preparation method of the composite resin filter press plate of the present embodiment comprises the following steps:

[0023] (1) Dissolve the titanate coupling agent in absolute ethanol, add calcium carbonate at 40-45°C, stir evenly for 4 hours, filter, and dry in vacuum for 12 hours to obtain modified calcium carbonate;

[0024] (2) Take polyolefin polymer material, thermoplastic elastomer SBS, glass fiber, modified zeoli...

Embodiment 2

[0026] This embodiment provides a composite resin filter press plate, which is made of the following raw materials in parts by weight: 100 parts by weight of high-density polyethylene, 50 parts by weight of polypropylene, 8 parts by weight of thermoplastic elastomer SBS, 30 parts by weight of Glass fiber, 8 parts by weight of titanate coupling agent, 50 parts by weight of calcium carbonate, 20 parts by weight of modified zeolite, 30 parts by weight of hollow glass microspheres, and 3 parts by weight of antioxidant.

[0027] The preparation method of the composite resin filter press plate of the present embodiment comprises the following steps:

[0028] (1) Dissolve the titanate coupling agent in absolute ethanol, add calcium carbonate at 40-45°C, stir evenly for 2 hours, filter, and dry in vacuum for 16 hours to obtain modified calcium carbonate;

[0029] (2) Take polyolefin polymer material, thermoplastic elastomer SBS, glass fiber, modified zeolite, hollow glass microspheres...

Embodiment 3

[0031] This embodiment provides a composite resin filter press plate, which is made of the following raw materials in parts by weight: 250 parts by weight of high-density polyethylene and 100 parts by weight of polypropylene resin, 3 parts by weight of thermoplastic elastomer SBS, 340 parts by weight 3 parts by weight of glass fiber, 3 parts by weight of titanate coupling agent, 60 parts by weight of calcium carbonate, 10 parts by weight of modified zeolite, 40 parts by weight of hollow glass microspheres, and 1 part by weight of antioxidant.

[0032] The preparation method of the composite resin filter press plate of the present embodiment comprises the following steps:

[0033] (1) Dissolve the titanate coupling agent in absolute ethanol, add calcium carbonate at 40-45°C, stir evenly for 6 hours, filter, and dry in vacuum for 8 hours to obtain modified calcium carbonate;

[0034] (2) Take polyolefin polymer material, thermoplastic elastomer SBS, glass fiber, modified zeolite...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite resin filter-pressing plate. The composite resin filter-pressing plate is prepared from the following raw materials of, by weight, 150-250 parts of polyolefin high polymer materials, 3-8 parts of thermoplastic elastomer SBS, 30-40 parts of glass fibers, 3-8 parts of a titanate coupling agent, 50-60 parts of calcium carbonate, 10-20 parts of modified zeolite, 30-40 parts of hollow glass beads, and 1-3 parts of an antioxidant. The invention further provides a preparation method of the composite resin filter-pressing plate. Since the manufacturing materials and the manufacturing method are changed, the filtering efficiency of the manufactured filter-pressing plate is greatly improved, the compressive strength of the filter-pressing plate pressed at a high temperature and under high pressure reaches 360 kg / cm<2>, and the shock resistance and the compressive strength performance of the filter-pressing plate are good.

Description

technical field [0001] The invention relates to the technical field of filter plates of filter machines, in particular to a composite resin press filter plate and a preparation method thereof. Background technique [0002] Ceramic filter is a kind of equipment for solid-liquid separation, because the medium for solid-liquid separation is ceramic filter press plate, the core component of which is ceramic filter press plate, which is a porous ceramic containing tiny capillaries. The principle of solid-liquid separation is capillary theory. According to Kelvin's law, as long as the capillary diameter is controlled within a certain range, the required capillary force can be achieved. At this time, the filter plate is filled with liquid, but the air cannot pass through. Under the action of a small vacuum, the vacuum inside the filter plate keeps rising, making the filter cake sucked and hung outside the filter plate thicker and thicker, and the liquid flowing into the filter plat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/18C08L23/06C08L53/02C08L23/12C08K13/06C08K9/04C08K7/14C08K3/26C08K3/34C08K7/28B01D39/14
CPCB01D39/14C08K2201/003C08L23/06C08L27/18C08L2205/03C08L2207/04C08L2207/062C08L2207/068C08L53/02C08K13/06C08K9/04C08K7/14C08K2003/265C08K3/34C08K7/28C08L23/12
Inventor 蔡耀武张英才蔡新奇曾荣平蔡建武何南
Owner ZHENGZHOU HOLLOWLITE MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com